Robust microfluidic construction of polyvinyl pyrrolidone microfibers incorporated with W/O emulsions stabilized by amphiphilic konjac glucomannan

Robust construction of konjac glucomannan/polylactic acid nanofibrous films incorporated with carvacrol via microfluidic blow spinning for food packaging

In recent years, the application of biopolymer-based nanofibers prepared via microfluidic blow spinning (MBS) for food packaging has continuously increased due to their advantages of biocompatibility, biodegradability, and safety. However, the poor spinnability, undesirable water barrier capacity, and loss of antibacterial and antioxidant properties of biopolymer-based nanofibers strictly restrict their real-world applications. In this work, carvacrol (CV) incorporated konjac glucomannan (KGM)/polylactic acid (PLA) nanofibrous films (KP-CV) were produced by MBS. The FTIR spectra and XRD analysis revealed the hydrogen bonding interactions among CV, PLA, and KGM, thus significantly improving the TS of KP-CV nanofibrous films from 0.23 to 1.27 MPa with increased content of CV from 0 % to 5 %. Besides, KP-CV nanofibrous films showed improved thermal stability, excellent hydrophobicity (WCA: 128.19°, WVP: 1.02 g mm/m2 h kPa), and sustained release of CV combined with good antioxidant activities (DPPH radical scavenging activity: 77.51 ± 1.57 %), and antibacterial properties against S. aureus (inhibition zone: 26.33 mm) and E. coli (inhibition zone: 22.67 mm). Therefore, as prepared KP-CV nanofibrous films can be potentially applied as packaging materials for the extended shelf life of cherry tomatoes.

Pullulan nanofibrous films incorporated with W/O emulsions via microfluidic solution blow spinning technology

In this work, pullulan (PUL) nanofibrous films incorporated with water-in-oil emulsions (PE) were prepared by microfluidic blowing spinning (MBS). The microstructures of nanofibers were characterized by scanning electron microscopy (SEM), fourier transform infrared (FT-IR), and X-ray diffraction (XRD). With the addition of W/O emulsions, the thermal stability, mechanical, and water barrier properties of PUL nanofibers were improved. Increases in emulsion content significantly affected the antioxidant and antimicrobial properties of nanofibrous films. ABTS and DPPH free radical scavenging rates increased from 10.26 % and 8.57 % to 60.66 % and 57.54 %, respectively. The inhibition zone of PE nanofibers against E. coli and S. aureus increased from 11.00 to 20.00 and from 15.67 to 21.17 mm, respectively. In addition, we investigated the freshness effectiveness of PE nanofibrous films on fresh-cut apples. PE nanofibrous films significantly maintained the firmness, and reduced the weight loss and browning index of the fresh-cut apple, throughout the 4 days of storage. Thus, the PE nanofibrous films exhibited good potential to prolong the shelf life of fresh-cut fruit and promote the development of active food packaging.

Electrospun Konjac Glucomannan/Polyvinyl Alcohol Long Polymeric Filaments Incorporated with Tea Polyphenols for Food Preservations

In this study, nanofiber films were prepared by electrospinning technology with polyvinyl alcohol (PVA) and konjac glucomannan (KGM) as raw materials. Tea polyphenols (TPs) were incorporated in the above matrix, which increased physicochemical (thermal and mechanical characteristics) and antibacterial properties of the nanofiber films. The release behavior of phenolic compounds from PVA/KGM-TPs nanofiber films was determined in different food simulants; antioxidant and antibacterial activity of the films were also evaluated. The results showed that the addition of KGM increased the physical and chemical properties of the films. The tensile strength (TS) and elongation at break (EB) increased from 5.40 ± 0.33 to 10.62 ± 0.34 and from 7.24 ± 0.32 to 18.10 ± 0.91, respectively. PVA/KGM-TPs nanofiber films performed controlled release of TPs, with final release of 49.17% in 3% acetic acid, 43.6% in 10% ethanol, and 59.42% in 95% ethanol. The nanofiber films showed good antioxidation properties, with the free radical scavenging rate increasing from 1.33% to 25.61%, and good antibacterial properties with inhibition zones against E. coli and S. aureus of 24.33 ± 0.47 mm and 34.33 ± 0.94 mm, respectively. In addition, the as-prepared films showed significant preservation performance for raw bananas at 25 °C.

Konjac glucomannan/carboxymethyl chitosan film embedding gliadin/casein nanoparticles for grape preservation

Constructing biopolymer-based packaging films with fantastic water resistance and mechanical properties for food preservation is highly desirable and challenging. In this work, Gliadin/Casein nanoparticles (GCNPs) were prepared by pH-driven method and embedded into konjac glucomannan/carboxymethyl chitosan (KC) film matrix to improve the water resistance and mechanical properties of KC film. Gliadin and Casein showed good compatibility and co-assembled to form compact GCNPs clusters through hydrogen bonding and hydrophobic interaction verified by FT-IR spectroscopy, and fluorescence spectroscopy. The particle size and zeta potential of GCNPs was 269.7 nm and -7.6 mV, respectively. The effect of GCNPs on the mechanics, water barrier, thermal stability, and UV-shielding of KC-GCNPs film was investigated. SEM images revealed that GCNPs uniformly distributed into KC film matrix and significantly improved the mechanics (tensile strength: 75.6 MPa, elongation at breaking: 36.7 %), water barrier ability (water contact angle: 91.3°, water vapor permeability: 0.994 g mm/m2 day kPa, water solubility: 52.0 %), thermal stability and UV blocking property of KC-GCNPs film. Furthermore, KC-GCNPs film could also be applied to extend the shelf life of grapes. This paper demonstrated the great potential of GCNPs as functional nanofillers in enhancing the physicochemical properties of KC film.