On scale dependence in friction: Transition from intimate to monolayer-lubricated contact

Nanotribology of hydrogels with similar stiffness but different polymer and crosslinker concentrations

HYPOTHESIS

The stiffness has been found to regulate hydrogel performances and applications. However, the key interfacial properties of hydrogels, like friction and adhesion are not controlled by the stiffness, but are altered by the structure and composition of hydrogels, like polymer volume fraction and crosslinking degree.

EXPERIMENTS

Colloidal probe atomic force microscopy has been use to investigate the relationship between tribological properties (friction and adhesion) and composition of hydrogels with similar stiffness, but different polymer volume fractions and crosslinking degrees.

FINDINGS

The interfacial normal and lateral (friction) forces of hydrogels are not directly correlated to the stiffness, but altered by the hydrogel structure and composition. For normal force measurements, the adhesion increases with polymer volume fraction but decreases with crosslinking degree. For lateral force measurements, friction increases with polymer volume fraction, but decreases with crosslinking degree. In the low normal force regime, friction is mainly adhesion-controlled and increases significantly with the adhesion and polymer volume fraction. In the high normal force regime, friction is predominantly load-controlled and shows slow increase with normal force.

A double-Hertz model for adhesive contact between cylinders under inclined forces

A generalized double-Hertz (D-H) model has been proposed to consider the adhesive contact between an elastic cylinder and an elastic half space under inclined forces. The normal traction is exactly the same as that in the conventional D-H model. The shear traction of finite value is distributed into a slipping zone and a non-slipping zone. In the slipping zone, the shear traction is proportional to the compressive pressure. With the model, adhesive contact behaviour between cylinders has been numerically illustrated. The shear-induced peeling has been demonstrated. The value of the ratio for shear traction to normal traction larger than friction coefficient has been found in part of the non-slipping zone. Those altogether are consistent with experiments.

Static friction between silicon nanowires and elastomeric substrates

This paper reports the first direct measurements of static friction force and interfacial shear strength between silicon (Si) nanowires (NWs) and poly(dimethylsiloxane) (PDMS). A micromanipulator is used to manipulate and deform the NWs under a high-magnification optical microscope in real time. The static friction force is measured based on "the most-bent state" of the NWs. The static friction and interface shear strength are found to depend on the ultraviolet/ozone (UVO) treatment of PDMS. The shear strength starts at 0.30 MPa without UVO treatment, increases rapidly up to 10.57 MPa at 60 min of treatment and decreases for longer treatment. Water contact angle measurements suggest that the UVO-induced hydrophobic-to-hydrophilic conversion of PDMS surface is responsible for the increase in the static friction, while the hydrophobic recovery effect contributes to the decrease. The static friction between NWs and PDMS is of critical relevance to many device applications of NWs including NW-based flexible/stretchable electronics, NW assembly and nanocomposites (e.g., supercapacitors). Our results will enable quantitative interface design and control for such applications.

Friction and shear strength at the nanowire-substrate interfaces

The friction and shear strength of nanowire (NW)-substrate interfaces critically influences the electrical/mechanical performance and life time of NW-based nanodevices. Yet, very few reports on this subject are available in the literature because of the experimental challenges involved and, more specifically no studies have been reported to investigate the configuration of individual NW tip in contact with a substrate. In this letter, using a new experimental method, we report the friction measurement between a NW tip and a substrate for the first time. The measurement was based on NW buckling in situ inside a scanning electron microscope. The coefficients of friction between silver NW and gold substrate and between ZnO NW and gold substrate were found to be 0.09-0.12 and 0.10-0.15, respectively. The adhesion between a NW and the substrate modified the true contact area, which affected the interfacial shear strength. Continuum mechanics calculation found that interfacial shear strengths between silver NW and gold substrate and between ZnO NW and gold substrate were 134-139 MPa and 78.9-95.3 MPa, respectively. This method can be applied to measure friction parameters of other NW-substrate systems. Our results on interfacial friction and shear strength could have implication on the AFM three-point bending tests used for nanomechanical characterisation.

Mechanical probing of icelike water monolayers

Direct measurements of the normal force interactions between a mica-tungsten contact pair at various humidity levels reveal the presence of repulsive forces at about 0.5 nm before intimate contact. Such repulsive interactions begin to appear above 20% RH and are fully developed in the range of 38-45% RH. Using the DMT model of contact, a reduced elastic modulus of approximately 6.7 GPa is extracted from these repulsive interactions and attributed to the presence of icelike water on mica at room temperature. The collapse of such structures was also inferred from the measurements.