Zn-doped Tin monoxide nanobelt induced engineering a graphene and CNT supported Zn-doped Tin dioxide composite for Lithium-ion storage

Chitosan modulated engineer tin dioxide nanoparticles well dispersed by reduced graphene oxide for high and stable lithium-ion storage

Tin based materials are widely investigated as a potential anode material for lithium-ion batteries. Effectively dispersing SnO₂ nanocrystals in carbonaceous supporting skeleton using simplified methods is both promising and challenging. In this work, water soluble chitosan (CS) chains are employed to modulate the redox coprecipitation reaction between stannous chloride (SnCl₂) and few-layered graphene oxide (GO), where the excessive restacking of the corresponding reduced graphene oxide sheets (RGO) has been effectively inhibited and the grain size of the in-situ formed SnO₂ nanoparticles have been significantly controlled. In particular, the CS molecules are gradually detached from the RGO sheets with the GO deoxygenation process, leaving only a small quantity of CS remnants in the intermediate SnO₂@CS@RGO sample. The final SnO₂/CSC/RGO sample with significantly improved microstructure is synthesized after a simple thermal treatment, which delivers a high specific capacity of 842.9 mAh g^-1 at 1000 mA·g^-1 for 1000 cycles in half cells and a specific capacity of 410.5 mAh g^-1 at 200 mA·g^-1 for 100 cycles in full cells. The reasons for the good lithium-ion storage performances for the SnO₂/CSC/RGO composite have been studied.

Rationally engineering a hierarchical porous carbon and reduced graphene oxide supported magnetite composite with boosted lithium-ion storage performances

Ferric gallate (Fe-GA), an ancient metal-organic framework (MOF) material, has been recently employed as an eco-friendly and cost-effective precursor sample to synthesize a porous carbon confined nano-iron composite (Fe/RPC), and the Fe element in the Fe/RPC sample could be further oxidized to Fe₃O₄ nanocrystals in a 180 °C hydrothermal condition. On this foundation, this work reports an optimized approach to engineering a hierarchical one-dimensional porous carbon and two-dimensional reduced graphene oxide (RGO) supporting framework with Fe₃O₄ nanoparticles well dispersed. Under mild hydrothermal condition, the redox reaction between metal iron atoms from Fe/RPC and surface functional radicals from few-layered graphene oxide sheets (GO) is triggered. As a result, reinforced microstructure and improved atomic efficiency have been achieved for the Fe₃O₄@RPC/RGO sample. The homogeneously dispersed Fe₃O₄ nanoparticles with controlled size are anchored on the surface of the larger sized RGO coating layers while the smaller sized RPC domains are embedded between the RGO sheets as spacer. Challenges including spontaneous aggregation of RPC, over exposure of Fe₃O₄ nanoparticles and excessive restacking of RGO have been significantly inhibited. Furthermore, micro-sized carbon fiber (CF) is chosen as a structural reinforcement additive during electrode fabrication, and the Fe₃O₄@RPC/RGO sample delivers a good specific capacity of 1170.5 mAh·g^-1 under a current rate of 1000 mA·g^-1 for 500 cycles in the half cell form. The reasons for superior electrochemical behaviors have been revealed and the lithium-ion storage performances of the Fe₃O₄@RPC/RGO sample in the full cell form have been preliminarily investigated.