Buffering or non-buffering; an action of pit-and-fissure sealants

Anti-demineralizing protective effects on enamel identified in experimental and commercial restorative materials with functional fillers

The aim of this study was to investigate whether experimental and commercial dental restorative materials with functional fillers can exert a protective anti-demineralizing effect on enamel that is not immediately adjacent to the restoration. Four experimental resin composites with bioactive glass and three commercial restorative materials were investigated. Enamel blocks were incubated in a lactic acid solution (pH = 4.0) at a standardized distance (5 mm) from cured specimens of restorative materials. The lactic acid solution was replenished every 4 days up to a total of 32 days. Surfaces of enamel blocks were periodically evaluated by Knoop microhardness measurements and scanning electron microscopy. The protective effect of restorative materials against acid was identified as enamel microhardness remaining unchanged for a certain number of 4-day acid addition cycles. Additionally, the pH of the immersion medium was measured. While enamel microhardness in the control group was maintained for 1 acid addition cycle (4 days), restorative materials postponed enamel softening for 2–5 cycles (8–20 days). The materials capable of exerting a stronger alkalizing effect provided longer-lasting enamel protection. The protective and alkalizing effects of experimental composites improved with higher amounts of bioactive glass and were better for conventional bioactive glass 45S5 compared to a fluoride-containing bioactive glass. Scanning electron micrographs evidenced the protective effect of restorative materials by showing a delayed appearance of an etching pattern on the enamel surface. A remotely-acting anti-demineralizing protective effect on enamel was identified in experimental composites functionalized with two types of bioactive glass, as well as in three commercial ion-releasing restorative materials.

A New Customized Bioactive Glass Filler to Functionalize Resin Composites: Acid-Neutralizing Capability, Degree of Conversion, and Apatite Precipitation

This study introduced an experimental bioactive glass (BG) with a lower Na₂O content than conventional BG 45S5 (10.5 wt% vs. 24.5 wt%), additionally containing CaF₂ (12 wt%) and a network connectivity similar to that of BG 45S5. A series of experimental composites functionalized with 5-40 wt% of the novel BG was prepared and compared to a corresponding series of experimental composites functionalized with 5-40 wt% of BG 45S5. Commercial acidneutralizing materials (alkasite, giomer, and glass ionomer) were used as references. The capabilities of the materials to neutralize hydrochloric acid (pH = 2.6) and lactic acid (pH = 4.5) were evaluated by real-time pH measurements over 1 h. The degree of conversion and precipitation of calcium phosphate were also investigated. Data were analyzed using one-way and Welch ANOVA at an overall level of significance of 0.05. The acid-neutralizing potential of the experimental BG incorporated into resin composites was generally comparable to that of BG 45S5, and better than that of a giomer and glass ionomer. Fluorine was identified in the precipitate that developed on the composites functionalized with the experimental BG, suggesting a capability of forming fluorapatite. Unlike the 45S5 composition, the experimental BG did not impair the degree of conversion of resin composites. The novel BG filler is therefore an interesting candidate for future investigations of caries-preventive resin composites, and their potential clinical applicability for restorative, preventive, and orthodontic purposes.