A novel non-destructive technique for qualitative and quantitative measurement of dental erosion in its entirety by porosity and bulk tissue-loss

Tooth Wear and Tribological Investigations in Dentistry

Dental or tooth wear is a physiological process in the life cycle of teeth. Loss of the occlusal surface may cause excessive tooth wear. Several factors may contribute to tooth wear with different intensities and duration in the oral cavity. The oral cavity is generally compared to a tribological system to determine the various types of wear between teeth and restorative materials and assess the amount of dental wear. However, it is challenging to investigate in vitro and in vivo wear owing to the complexity of tooth wear; thus, a clear correlation between in vitro and in vivo data could not be established. This review is aimed at providing an insight into the etiology of tooth wear and tribological investigations in dentistry.

Bioactive remineralization of dentin surface with calcium phosphate-based agents: An in vitro analysis

Background:

With the increasing prevalence of erosive tooth wear affecting both adults and children; designing optimum protocols of management in a noninvasive manner is gaining precedence.

Aim:

Comparative evaluation of topically applied calcium phosphate-based agents casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and beta tricalcium phosphate (β-TCP) on the surface of eroded dentin.

Materials and Methods:

Dentin blocks from human third molars in four groups were subjected to the surface treatment: (G1) sound dentin (G2) demineralized dentin (G3) CPP-ACP (G4) β-TCP. All the samples except control (G1) were immersed in an acidic solution incubated at 37°C for 96 h. The samples in G3 and G4 were topically treated with CPP-ACP and β-TCP for 4 min twice daily for 14 days; followed by pH-cycling for 21 days. Surface hardness testing and surface morphology were observed using the scanning electron microscopy. Data were analyzed using the Statistical Package for the Social Sciences (SPSS) software with Kruskal-Wallis test and post hoc test.

Results:

Dentin treated with both CPP-ACP (37.25) and β-TCP (32.05) recorded significantly higher VHN than demineralized (G2-23.51) but lower compared to sound control (G1-57.06).

Conclusion:

The topical application of CPP-ACP and β-TCP agents shows definite potential in promoting the hardening of demineralized dentin surface.