Effect of incorporation of nano bioactive silica into commercial Glass Ionomer Cement (GIC)

The Impact of Nano- and Micro-Silica on the Setting Time and Microhardness of Conventional Glass-Ionomer Cements

The objective of this study was to investigate the effect of the incorporation of 2, 4 or 6 wt% of amorphous nano- or micro-silica (Aerosil® OX 50 or Aeroperl® 300 Pharma (Evonik Operations GmbH, Essen, Germany), respectively) on the net setting time and microhardness of Ketac™ Molar (3M ESPE, St. Paul, MN, USA) and Fuji IX GP® (GC Corporation, Tokyo, Japan) glass-ionomer cements (GICs) (viz. KM and FIX, respectively). Both silica particles were found to cause a non-linear, dose-dependent reduction in setting time that was within the clinically acceptable limits specified in the relevant international standard (ISO 9917-1:2007). The microhardness of KM was statistically unaffected by blending with 2 or 4 wt% nano-silica at all times, whereas 6 wt% addition decreased and increased the surface hardness at 1 and 21 days, respectively. The incorporation of 4 or 6 wt% nano-silica significantly improved the microhardness of FIX at 1, 14 and 21 days, with no change in this property noted for 2 wt% addition. Micro-silica also tended to enhance the microhardness of FIX, at all concentrations and times, to an extent that became statistically significant for all dosages at 21 days. Conversely, 4 and 6 wt% additions of micro-silica markedly decreased the initial 1-day microhardness of KM, and the 21-day sample blended at 4 wt% was the only specimen that demonstrated a significant increase in this property. Scanning electron microscopy indicated that the nano- and micro-silica particles were well distributed throughout the composite structures of both GICs with no evidence of aggregation or zoning. The specific mechanisms of the interaction of inorganic nanoparticles with the constituents of GICs require further understanding, and a lack of international standardization of the determination of microhardness is problematic in this respect.

Incorporation of Nanomaterials in Glass Ionomer Cements-Recent Developments and Future Perspectives: A Narrative Review

Glass ionomer cements (GICs), restorative materials with commercial availability spanning over five decades, are widely applied due to their advantages (including bio-compatibility, fluoride release, or excellent bonding properties). However, GICs have shortcomings. Among the disadvantages limiting the application of GICs, the poor mechanical properties are the most significant. In order to enhance the mechanical or antimicrobial properties of these materials, the addition of nanomaterials represents a viable approach. The present paper aims to review the literature on the application of different types of nanomaterials for the enhancement of GICs' mechanical and antimicrobial properties, which could lead to several clinical benefits, including better physical properties and the prevention of tooth decay. After applying the described methodology, representative articles published in the time period 2011-present were selected and included in the final review, covering the modification of GICs with metallic nanoparticles (Cu, Ag), metallic and metalloid oxide nanoparticles (TiO₂, ZnO, MgO, Al₂O₃, ZrO₂, SiO₂), apatitic nanomaterials, and other nanomaterials or multi-component nanocomposites.

Study of Microleakage between Teeth and Glass Ionomer Cement Modified with 5% Silica from Sea Sand

Glass ionomer cement (GIC) is the most commonly used restoration material because of biocompatible material. GIC is restoration material that can be attached to enamel either to dentin physicochemically. The adhesion properties of teeth to restoration have an effect on marginal adaptation. This causes different attachment values. An alternative difference in attachment can be achieved by adding bioactive glass silica material to glass ionomer cement. The formation of hydroxyapatite can be occurred by bioactive glass silica between the tooth surfaces and the restoration materials and it is been expected to reduce microleakage rates. The purpose of this study was to seen the effect of adding 5% silica nanoparticles from sea sand to the GIC on microleakage rates. In this study, silica was synthesized from sea sand by using coprecipitation method. Specimens were 20 maxillary premolars were classified into two groups which were applied GIC (n=10) and silica 5% modified GIC as restorations (n=10). The specimens were immersed in 5% methylene blue solution for 24 hours, then were observed under stereomicroscope and SEM. There were a difference score microleakage and mean value of distance between silica 5% modified GIC with enamel and dentin had smaller distance, as compared to GIC.

Current aspects and prospects of glass ionomer cements for clinical dentistry

Glass ionomer cement (GIC) is a tailor-made material that is used as a filling material in dentistry. GIC is cured by an acid-base reaction consisting of a glass filler and ionic polymers. When the glass filler and ionic polymers are mixed, ionic bonds of the material itself are formed. In addition, the extra polymer anion reacts with calcium in enamel or dentin to increase adhesion to the tooth tissue. GICs are widely used as adhesives for artificial crowns or orthodontic brackets, and are also used as tooth repair material, cavity liner, and filling materials. In this review, the current status of GIC research and development and its prospects for the future have been discussed in detail.