Electric current effects on bond strength, nanoleakage, degree of conversion and dentinal infiltration of adhesive systems

Are universal adhesives in etch-and-rinse mode better than old 2-step etch-and-rinse adhesives? One-year evaluation of bonding properties to dentin

OBJECTIVES

This study compared the bonding properties of dentin of three 2-step etch-and-rinse adhesives (2-ERAs) to those of three universal adhesives (UAs) applied with an etch-and-rinse strategy (ER), immediately and after 1 year of water storage.

METHODS

Sixty caries-free molars were divided into 6 groups according to the adhesive systems used (n = 10). The 2-ERA systems included were: 1) Adper Single Bond 2 (SB), 2) Tetric N-Bond (TB), and 3) Ambar (AM); and the UAs systems were: 4) Single Bond Universal (SBU) 5) Tetric N-Bond Universal (TBU), and 6) Ambar Universal (AMU). The occlusal third of each tooth was removed and the adhesives were applied. After the composite build-up, specimens were sectioned and tested for microtensile bond strength (µTBS) and nanoleakage (NL) immediately and after 1 year of water storage. In situ degree of conversion (DC) was only evaluated in the immediate time. For water sorption (WS), solubility (SO), and mass change (MC) tests, 48 disk-shaped specimens were prepared (n = 8) and assessed according to ISO 4049:2009.

RESULTS

UAs showed higher µTBS and lower NL values than 2-ERAs did after 1 year of water storage (p = 0.001). Regarding DC, 2-ERAs showed higher DC values than UAs (p = 0.001). Regarding WS, 2-ERAs showed higher WS values than those of UAs (p = 0.00001), except for AM and AMU. Lower WS was observed for AM than for other 2-ERAs (p = 0.00001).

CONCLUSION

The use of UAs applied with the ER strategy seems to be a more effective technique for maintaining adhesion to dentin substrate than 2-ERAS.

CLINICAL SIGNIFICANCE

This study may support clinicians in selecting the most adequate adhesive system to be used in ER strategy in dentin, demonstrating that UAs were more effective, considering the longevity of the resin restorations.

Evaluation of Chitosan-Oleuropein Nanoparticles on the Durability of Dentin Bonding

Purpose

To evaluate the effects of dentin pretreatment with chitosan-loaded oleuropein nanoparticles (CONPs) on the durability of resin-dentin bonding interfaces.

Methods

Eighty freshly extracted non-carious human third molars were randomly divided into four groups (n = 20 each): a de-ionized water (DW) group, a chitosan (CS) group, a chlorhexidine (CHX) group and a CONP group. The dentin in the DW, CS, CHX, and CONP groups were pretreated with de-ionized water, 1.0 mg/L CS solution, 2% chlorhexidine solution, and CONP suspension (prepared with 100 mg/L oleuropein), respectively, followed by the universal adhesive and resin composites. The bonded teeth of each group were randomly divided into two subgroups: an immediate subgroup and an aged subgroup. The bonded teeth of each group were then cut into the bonded beams. We measured their microtensile bond strength (μTBS), observed the characteristics of bonding interface by atomic force microscope, calculated the percentage of silver particles in a selected area for interfacial nanoleakage analysis, and evaluated the endogenous gelatinase activity within the bonding interface for in-situ zymogram analysis. Data were analyzed with two-way ANOVA and LSD multiple comparison test (P < 0.05).

Results

Regardless of after 24 h or after thermocycling, CONP exhibited better μTBS (P < 0.05) than the other three groups except that there was not a statistical significance (P > 0.05) in the CONP and CHX groups after 24 h. Besides, the CONP group presented significantly higher modulus of elasticity in the hybrid layers (P < 0.05), lower expression of nanoleakage (P < 0.05), and better inhibitory effect of matrix metalloproteinases than the other three groups before and after thermocycling.

Conclusion

Altogether, the CONPs had the potential to act as a dentin primer, which could effectively improve the dentin-resin binding durability.

Effect of Different Application Modalities on the Bonding Performance of Adhesive Systems to Dentin: A Systematic Review and Meta-Analysis

Diverse types of dental adhesives exhibit different cytotoxic outcomes on cells in vitro. Currently, no standard adhesive application technique has so far been decisive for clinicians for better durability of resin-dentin bonds of adhesive systems. The purpose of this study was to systematically review the literature to evaluate the bonding performance of adhesive systems to dentin by using different application modalities. The systematic research strategy was conducted by two reviewers among multiple databases: PubMed, Scopus, Web of Science, Embase, and Scielo. In vitro studies reporting the effects of additional steps for the application of adhesive systems on the bond strength to dentin were selected. Meta-analysis was performed using Review Manager Software version 5.3.5 using the random effects model. The methodological quality of each in vitro study was assessed according to the parameters of a previous systematic review. The electronic research through different databases generated a total of 8318 references. After the examination of titles and abstracts, a total of 106 potentially relevant studies accessed the full-text evaluation phase. After full-text examination, 78 publications were included for the qualitative analysis, and 68 studies were included in the meta-analysis. Regarding the etch-and-rinse adhesive systems, the application modalities that improved the overall bond strength were the application of a hydrophobic resin layer (p = 0.005), an extended application time (p < 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p = 0.05), the agitation technique (p = 0.02), and the active application of the adhesive (p < 0.001). For self-etch adhesive systems, the techniques that improved the overall bond strength were the application of a hydrophobic resin layer (p < 0.001), an extended application time (p = 0.001), an application assisted by an electric current (p < 0.001), a double-layer application (p < 0.001), the agitation technique (p = 0.01), and the active application of the adhesive (p < 0.001). The in vitro evidence suggests that the application of adhesive systems using alternative techniques or additional strategies may be beneficial for improving their bond strength to dentin. The application modalities that favored the overall bond strength to dentin were an extended application time, a double-layer application, an application assisted by an electric current, the active application of the adhesive, and the application of a hydrophobic resin layer. Worth mentioning is that some techniques are intended to increase the degree of the conversion of the materials, and therefore, improvements in the biocompatibility of the materials can be expected.

The effect of fluoride iontophoresis on seal ability of self-etch adhesive in human dentin in vitro

Background

Fluoride iontophoresis (FI) is a non-invasive method for the transfer of fluoride ions under electrical pressure into dental hard tissue. This study aimed to determine the effect of FI on the seal ability of self-etch adhesive in human dentin using dentin permeability test and scanning electron microscopy (SEM).

Methods

The experiments were divided into 2 series: series 1 was performed on 28 extracted intact third molars and series 2 was performed on 28 extracted carious third molars (ICDAS 4 and 5). In each series, 20 teeth were used for dentin permeability test and 8 teeth were used for SEM study. For dentin permeability test, the specimens were divided into dentin without FI (control) and dentin with FI (experimental) subgroups. Hydraulic conductance (HD) of dentin was measured before and after adhesive treatment, and calculated for the percentage decrease of HD in each subgroup. Two-way ANOVA and Tukey test were used for statistical analysis. SEM study was used to assess the seal ability of self-etch adhesive and penetration of fluoride ions into dentinal tubules.

Results

HD after self-etch adhesive treatment reduced by 57.75 ± 17.99% in intact dentin with FI, 46.60 ± 17.03% in intact dentin without FI, 45.00 ± 15.30% in caries affected dentin without FI, and 37.28 ± 14.72% in caries affected dentin with FI. There was no significant difference in percentage decrease of HD between dentin without FI and dentin with FI (P = 0.742); meanwhile, intact dentin with FI had significant greater percentage decrease than caries affected dentin with FI (P < 0.05). SEM findings showed FI produced more particle formation and deeper precipitation in intact dentin than those in caries affected dentin.

Conclusions

FI did not affect the seal ability of self-etch adhesive in human dentin when compared to without FI. However, FI could augment the seal ability of the self-etch adhesive in intact dentin better than that in caries affected dentin.

Supplementary Information

The online version contains supplementary material available at 10.1186/s12903-022-02146-w.

Novel nanostructured resin infiltrant containing calcium phosphate nanoparticles to prevent enamel white spot lesions

OBJECTIVES

The objective of this study was to develop a novel nanostructured resin infiltrant containing nanoparticles of amorphous calcium phosphate (NACP) to treat enamel white spot lesions (WSLs). Physical properties and the therapeutic effect of the new resin infiltrant were investigated for the first time.

METHODS

NACP was incorporated into ICON (Icon caries infiltrant, DMG, Germany) with different mass fractions. Cytotoxicity, degree of conversion, surface hardness, calcium (Ca) and phosphorus (P) ions release concentrations were tested. After application to the demineralized enamel samples, the color changes were determined. Surface and cross-sectional hardness were measured, scanning electron microscopy (SEM) images were taken on the cross-section of samples to observe microstructure changes after 14-day pH cycling.

RESULTS

Incorporating 10%-30% of NACP did not compromise the biocompatibility and physical properties of the resin infiltrant. ICON + 30% NACP group had long-lasting and high level of Ca and P ion release. After 14-day pH cycling, enamel surface hardness of ICON + 30% NACP group was 1.83 ± 0.21 GPa, significantly higher than the control group (1.32 ± 0.18 GPa) (p < 0.05). ICON + 30NACP group had the highest cross-sectional enamel hardness among all groups (p < 0.05), especially at 50 μm and 100 μm depth. SEM images showed that apparent enamel prism and inter-prism gaps in negative control were masked by mineral deposition in ICON + 30% NACP group.

SIGNIFICANCE

The novel ICON+30% NACP infiltrant is promising to inhibit enamel WSLs, protect the enamel and increase its hardness.