Synthesis and characterization of hollandite-type material intended for the specific containment of radioactive cesium

Preparation and characterization of multiphase ceramic designer waste forms

The long-term performance, or resistance to elemental release, is the defining characteristic of a nuclear waste form. In the case of multiphase ceramic waste forms, correlating the long-term performance of multiphase ceramic waste forms in the environment to accelerated chemical durability testing in the laboratory is non-trivial owing to their complex microstructures. The fabrication method, which in turn affects the microstructure, is further compounding when comparing multiphase ceramic waste forms. In this work, we propose a “designer waste form” prepared via spark plasma sintering to limit interaction between phases and grain growth during consolidation, leading to monolithic high-density waste forms, which can be used as reference materials for comparing the chemical durability of multiphase waste forms. Designer waste forms containing varying amounts of hollandite in the presence of zirconolite and pyrochlore in a fixed ratio were synthesized. The product consistency test (PCT) and vapor hydration test (VHT) were used to assess the leaching behavior. Samples were unaffected by the VHT after 1500 h. As measured by the PCT, the fractional Cs release decreased as the amount of hollandite increased. Elemental release from the zirconolite and pyrochlore phases did not appear to significantly contribute to the elemental release from the hollandite phase in the designer waste forms.

A-site compositional effects in Ga-doped hollandite materials of the form BaxCsyGa2x+yTi8-2x-yO16: implications for Cs immobilization in crystalline ceramic waste forms

The hollandite structure is a promising crystalline host for Cs immobilization. A series of Ga-doped hollandite BaxCsyGa2x+yTi8-2x-yO16 (x = 0, 0.667, 1.04, 1.33; y = 1.33, 0.667, 0.24, 0) was synthesized through a solid oxide reaction method resulting in a tetragonal hollandite structure (space group I4/m). The lattice parameter associated with the tunnel dimension was found to increases as Cs substitution in the tunnel increased. A direct investigation of cation mobility in tunnels using electrochemical impedance spectroscopy was conducted to evaluate the ability of the hollandite structure to immobilize cations over a wide compositional range. Hollandite with the largest tunnel size and highest aspect ratio grain morphology resulting in rod-like microstructural features exhibited the highest ionic conductivity. The results indicate that grain size and optimized Cs stoichiometry control cation motion and by extension, the propensity for Cs release from hollandite.