Fracture Toughness of Vocal Fold Tissue: A Preliminary Study

Effect of loading direction and anatomical location on the ultimate tensile stress, fracture toughness, and failure patterns of knee meniscus

BACKGROUND

Rupture of the knee menisci is a common injury that can have implications for other conditions, such as osteoarthritis. The fracture toughness of soft tissue (Jc) is a mechanical property that characterizes its resistance to tear extension. To date, Jc of the meniscus has not been quantified.

METHODS

Cyclic tensile tests were conducted on meniscus samples to determine Jc and explore its characteristics. Initially, the study investigated the impact of an initial notch on the ultimate tensile stress. This allowed for an understanding of how the presence of a notch affects its structural integrity. Subsequently, Jc was measured in both the radial and circumferential directions to assess its loading direction dependency. Furthermore, the study assessed the effect of anatomical location by comparing samples collected from the femoral and tibial layers.

RESULTS

Defect tolerance of the meniscus is influenced by the loading direction. In the circumferential direction, the presence of an initial notch did not affect the ultimate stress, and no crack expansion was observed. In radial samples with a notch length of 40% or more of the total width, crack propagation occurred, leading to a decrease in the ultimate stress (p< 0.01). Additionally, Jc was found to be higher in the femoral layer compared to the tibial layer (p= 0.017).

CONCLUSION

The study also examined the failure patterns of the meniscus to enhance our understanding of its pathology. These insights contribute to a better comprehension of meniscus injuries and can aid in the development of more effective treatment strategies.

Influence of crack length and anatomical location on the fracture toughness of annulus fibrosus

Fracture toughness (J_c) of a soft biological tissue is an important mechanical property that characterizes its resistance to crack or tear extension. To date, no information is available on fracture toughness of annulus fibrosus (AF); therefore, its defect tolerance is not known. The present study modified a previously introduced method to determine J_c of ovine AF. Then, the effect of the notch length on the failure pattern and J_c was investigated. Also, the test samples of anterior and lateral regions were collected to determine the effect of the location on J_c. Results showed that for a notch length of less than 45% of total width, no crack extension occurred, but for a notch length above 45% of the width, crack propagation and ultimately the failure of the AF were observed. However, statistical analysis indicated no significant difference on J_c (p = 0.5) for the initial notch length of 50% and 70% of total width. The fracture toughness was significantly higher for the samples extracted from the lateral site than those from the anterior site (p < 0.05). Dissimilar failure patterns were observed for different initial notch lengths. Among the parameters studied, the defect tolerance of AF was dependent on the initial tear size.