Synergistic corrosion inhibition effects of benzimidazole-samarium (III) molecules on the steel corrosion prevention in simulated seawater

Study of the anticorrosive behavior of samarium as a corrosion inhibitor in multilayer systems for aluminum alloy

This study shows a multilayer system based on samarium compounds as a corrosion inhibitor and a continuous SiO₂ layer by atmospheric pressure plasma jet (APPJ) as a protective barrier for aluminim alloy AA3003. One of the main advantages of this new coating is that it does not require vacuum chambers, which makes it easy to incorporate into production lines for automotive and aeronautical components, etc. The deposit of samarium corrosion inhibitor was carried out by two methods for comparison, the immersion method and a novel method to deposit corrosion inhibitor by APPJ. The multilayer system generated was homogeneous, continuous, adherent, and dense. The electrochemical behavior shows that the samarium compound was completely oxidized on coatings by the immersion method and favors corrosion. The APPJ deposition method shows a protective behavior against corrosion by both samarium compounds and silica depositions. XPS analyses show that the amount of Sm(OH)³ increases by the APPJ method compared with the immersion method since the spectrum of O1s is mainly controlled by OH. It was determined that the best processing times for the electrochemical study of the multilayer system were 40 min for the immersion method and 30 s for the APPJ method for the layer of corrosion inhibitor. In the case of the SiO₂ barrier layer by APPJ, the best time was 60 s of exposure to the plasma jet and this coating could reduce the corrosion of AA3003 by 31.42%.

Synthesis of graphene oxide nanosheets decorated by nanoporous zeolite-imidazole (ZIF-67) based metal-organic framework with controlled-release corrosion inhibitor performance: Experimental and detailed DFT-D theoretical explorations

For the first time, the zeolite-imidazole (ZIF-67) framework, a new subfamily of metal-organic frameworks (MOFs), is synthesized on the graphene oxide (GO) platform. Co²⁺ (as a central atom) and 2-methylimidazole (as organic ligands) were assembled to fabricate ZIF-67/GO NPs for providing epoxy-based anti-corrosion coatings with both active (self-healing) and passive (barrier) performance. Also, the ZIF-67/GO NPs were modified by 3-Aminopropyl triethoxysilane (APS) to improve the particles compatibility with the epoxy matrix and control their solubility in saline media. The FE-SEM, FT-IR, UV-Vis, Raman, TGA, and low-angle XRD techniques were used to prove the successful ZIF-67 particles growth onto the GO platforms. Tafel (potentiodynamic) polarization test demonstrated that the ZIF-67/GO@APS NPs could protect the surface of steel through mixed anodic/cathodic type (O₂ reduction/Fe oxidation) mechanisms and the corrosion current density of the iron sample decreased to 1.41 µA·cm^-2. Interestingly, the epoxy coatings containing ZIF-67/GO and ZIF-67/GO@APS particles revealed long-term corrosion protection durability and outstanding self-healing anti-corrosion performance, which were well studied via EIS, salt spray, cathodic delamination, and pull-off techniques. The impedance value at the lowest frequency for the coating containing ZIF-67/GO@APS after 50 days decreased from 10.7 Ω·cm² to 10.2 Ω·cm² that showed the lowest reduction among the studied samples.