Novel oxychloroborate glasses containing neodymium ions: Synthesis, structure and luminescent properties

Thermoluminescence emission on lead oxychloroborate glasses under UV exposure

Glassy materials were prepared using two different systems: 50B₂ O₃ - (50 - x)PbO - xPbCl_2, with x = 0, 2 and 5 in mol % (System BPCl-I) and 50BO_1.5 - (50 - x)PbO - xPbCl₂ with x = 0, 2, 5 and 7 in cationic % (System BPCl-II). Structural and optical characterization showed that PbCl when substituted for PbO changed the structure of the glass network by replacing nonbridging oxygens for chlorine ions. This substitution also caused a change in the number of defects responsible for thermoluminescence (TL) emission (electrons and hole trap centres). Thermoluminescence emissions were observed for the first time in lead oxychloroborate glasses after exposure to UV radiation. Sample BPCl-I-2 (x = 2 from System I) demonstrated better TL emission compared with other glass samples. One intense peak in the glow curve, centred at ~122°C followed by a shoulder at ~180°C, was highly sensitive to UV radiation. There were also good linear responses at dose range ~0.4 to ~2 J/cm² for the first peak (low temperature) and ~0.4 to ~4 J/cm² for the second peak (high temperature).

Structural reinvestigation of the photoluminescent complex [NdCl2(H2O)6]Cl

The structure of the photoluminescent compound hexaaquadichloridoneodymium(III) chloride has been redetermined from single-crystal X-ray diffraction data at 100 K, with the aim of providing an accurate structural model for the bulk crystalline material. The crystal structure may be described as a network of [NdCl2(H2O)6](+) cations with distorted square-antiprism geometry around the Nd(III) centre. The Nd(III) cation and the nonbonded Cl(-) anion are both located on twofold symmetry axes. The crystal packing consists of three different neodymium pairs linked by a three-dimensional network of O-H···Cl intermolecular interactions. The pair distribution function (PDF) calculated from the experimentally determined structure is used for the discussion of the local structure.

Visible luminescence of dysprosium ions in oxyhalide lead borate glasses

Visible luminescence of Dy(3+) ions in oxyhalide lead borate glasses was examined. Luminescence spectra show two intense bands at 480 nm and 573 nm due to (4)F(9/2)→(6)H(15/2) (blue) and (4)F(9/2)→(6)H(13/2) (yellow) transitions of Dy(3+). Luminescence decays from (4)F(9/2) state and yellow-to-blue luminescence intensity ratios (Y/B) were analysed with PbX(2) (X=F, Cl) content. An introduction of PbX(2) to the borate glass results in the increasing of (4)F(9/2) lifetime and the decreasing of yellow-to-blue luminescence intensity ratio, which is due to reduction of covalency between Dy(3+) and O(2-)/X(-) ions.