Preparation, mechanical property and cytocompatibility of freeze-cast porous calcium phosphate ceramics reinforced by phosphate-based glass

Molecular Dynamics Simulation of Biomimetic Biphasic Calcium Phosphate Nanoparticles

Biphasic calcium phosphate (BCP) is used as a bone substitute and bone tissue repair material due to its better control over bioactivity and biodegradability. It is crucial to stabilize the implanted biomaterial while promoting bone ingrowth. However, a lack of standard experimental and theoretical protocols to characterize the physicochemical properties of BCP limits the optimization of its composition and properties. Computational simulations can help us better to learn BCP at a nanoscale level. Here, the Voronoi tessellation method was combined with simulated annealing molecular dynamics to construct BCP nanoparticle models of different sizes, which were used to understand the physicochemical properties of BCP (e.g., melting point, infrared spectrum, and mechanical properties). We observed a ∼20 to 30 Å layer of calcium-deficient hydroxyapatite at the HAP/β-TCP interface due to particle migration, which may contribute to BCP stability. The BCP model may stimulate further research into BCP ceramics and multiphasic ceramics. Moreover, our study may facilitate the optimization of compositions of BCP-based biomaterials.

Hydroxyethyl Chitosan-Reinforced Polyvinyl Alcohol/Biphasic Calcium Phosphate Hydrogels for Bone Regeneration

Fabrication of reinforced scaffolds for bone regeneration remains a significant challenge. The weak mechanical properties of the chitosan (CS)-based composite scaffold hindered its further application in clinic. Here, to obtain hydroxyethyl CS (HECS), some hydrogen bonds of CS were replaced by hydroxyethyl groups. Then, HECS-reinforced polyvinyl alcohol (PVA)/biphasic calcium phosphate (BCP) nanoparticle hydrogel was fabricated via cycled freeze-thawing followed by an in vitro biomineralization treatment using a cell culture medium. The synthesized hydrogel had an interconnected porous structure with a uniform pore distribution. Compared to the CS/PVA/BCP hydrogel, the HECS/PVA/BCP hydrogels showed a thicker pore wall and had a compressive strength of up to 5-7 MPa. The biomineralized hydrogel possessed a better compressive strength and cytocompatibility compared to the untreated hydrogel, confirmed by CCK-8 analysis and fluorescence images. The modification of CS with hydroxyethyl groups and in vitro biomineralization were sufficient to improve the mechanical properties of the scaffold, and the HECS-reinforced PVA/BCP hydrogel was promising for bone tissue engineering applications.

Tailoring the mechanical property and cell-biological response of β-tricalcium phosphate composite bioceramics by SrO-P2O5-Na2O based additive

β-tricalcium phosphate (β-TCP) bioceramic, which is a prevalent bone graft, is deficient in mechanical strength and mediating the biological functions. In the present study, β-tricalcium phosphate composite bioceramics (TCP/SPNs) were prepared by introducing SrO-P₂O₅-Na₂O based (SPN) sintering additive. With increasing mole ratio of SrO to P₂O₅, the SPN tended to crystallize. In the liquid-phase sintering process, β-TCP reacted with SPN, producing new compounds. The difference in characteristic of SPN additive affected the compressive strength and cell-biological response of the fabricated TCP/SPNs. By selecting SPN with appropriate formulation, the TCP/SPNs not only could more than double their compressive strength, but also improved the cell viability, promoted osteogenic differentiation and inhibited osteoclastic activities. Taken together, this work establishes a beneficial strategy to improve the overall performance of calcium phosphate bioceramic for application in bone regeneration.

Biological properties of calcium phosphate biomaterials for bone repair: a review

This article reviews the recent advances and various factors affecting the improvement of the biological properties of calcium phosphate for bone repair.

Fabrication of β-tricalcium phosphate composite ceramic sphere-based scaffolds with hierarchical pore structure for bone regeneration

Polymer sphere-based scaffolds, which are prepared by bonding the adjacent spheres via sintering the randomly packed spheres, feature uniform pore structure, full three-dimensional (3D) interconnection, and considerable mechanical strength. However, bioceramic sphere-based scaffolds fabricated by this method have never been reported. Due to high melting temperature of bioceramic, only limited diffusion rate can be achieved when sintering the bioceramic spheres, which is far from enough to form robust bonding between spheres. In the present study, for the first time we fabricated 3D interconnected β-tricalcium phosphate ceramic sphere-based (PG/TCP) scaffolds by introducing phosphate-based glass (PG) as sintering additive and placing uniaxial pressure during the sintering process. The sintering mechanism of PG/TCP scaffolds was unveiled. The PG/TCP scaffolds had hierarchical pore structure, which was composed by interconnected macropores (>200 μm) among spheres, pores (20–120 μm) in the interior of spheres, and micropores (1–3 μm) among the grains. During the sintering process, partial PG reacted with β-TCP, forming β-Ca2P2O7; metal ions from PG substituted to Ca2+ sites of β-TCP. The mechanical properties (compressive strength 2.8–10.6 MPa; compressive modulus 190–620 MPa) and porosity (30%–50%) of scaffolds could be tailored by manipulating the sintering temperatures. The introduction of PG accelerated in vitro degradation of scaffolds, and the PG/TCP scaffolds showed good cytocompatibility. This work may offer a new strategy to prepare bioceramic scaffolds with satisfactory physicochemical properties for application in bone regeneration.