Characterization of Metal/Ceramic Interfaces in Dental Materials by Acoustic Emission

Effect of thermal and mechanical cycles on shear bond strength of zirconia core to porcelain veneer under different surface treatments

Background. Due to the fragile nature of all-ceramic restorations, it is necessary to provide an appropriate (core) infrastructure to support the veneering porcelain. The veneer detachment and chipping are disadvantages of these restorations. Several techniques have been proposed to minimize these problems. This study evaluated the effect of thermal and mechanical cycles on the shear bond strength of zirconia core to porcelain veneer under different surface treatments.

Methods. Sixty disk-like zirconium samples were randomly divided into three groups. The first group was polished and veneered with porcelain, without additional surface treatments. The two other groups were subjected to different surface treatments (modified aluminum oxide by silica and activator‒aluminum oxide and primer) and veneering with porcelain. Half of the samples in each group were subjected to 6000 thermal cycles and 20,000 masticatory cycles of 50 N to imitate the intraoral conditions; the other half were placed in distilled water at 37°C until the shear strength test. Each sample was then buried using PMMA in a mounting jig so that the gap between the core and the veneer could be placed upward. Then, they were exposed to shear stress using a universal testing machine at a rate of 1 mm/min until fracture. The maximum force leading to the fracture was recorded.

Results. Comparison of the groups showed that the highest shear bond strength was related to the samples treated with aluminum oxide and primer, without applying thermal and masticatory cycles, which indicated no significant difference from the group treated with aluminum oxide and primer, with thermal and masticatory cycles. The lowest shear bond strengths were related to the polished samples without surface treatment by applying thermal and masticatory cycles (P=0.001), which indicated no significant difference from the untreated group without thermal and masticatory cycles.

Conclusion. Based on the results, treatment with aluminum oxide and primer increased the shear bond strength of zirconia core to porcelain veneer. Thermocycling and masticatory cycles failed to reduce the shear bond strength in all the three groups significantly

Additive manufacturing of ceramics for dental applications: A review

OBJECTIVE

The main goal of this review is to provide a detailed and comprehensive description of the published work from the past decade regarding AM of ceramic materials with possible applications in dentistry. The main printable materials and most common technologies are also addressed, underlining their advantages and main drawbacks.

METHODS

Online databases (Web of knowledge, Science Direct, PubMed) were consulted on this topic. Published work from 2008 to 2018 was collected, analyzed and the relevant papers were selected for inclusion on this review.

RESULTS

Ceramic materials are broadly used in dentistry to restore/replace damaged or missing teeth, due to their biocompatibility, chemical stability and mechanical and aesthetic properties. However, there are several unmet challenges regarding their processing and performance. Due to their brittleness nature, a very tight control of the manufacturing process is needed to obtain dental pieces with adequate mechanical properties. Additive manufacturing (AM) is an emerging technology that constitutes an interesting and viable manufacturing alternative to the conventional subtractive methods. AM enables the production of customized complex 3D parts in a more sustainable and less expensive way. AM of ceramics can be achieved with an extensive variety of methods.

SIGNIFICANCE

There is no perfect technology for all materials/applications, capable alone of fulfilling all the specificities and necessities of every patient. Although very promising, AM of ceramic dental materials remains understudied and further work is required to make it a widespread technology in dentistry.