Polyoxomolybdate based ionic-liquids as active catalysts for oxidative desulfurization of simulated diesel

Effective Combination of the Metal Centers in MOF-Based Materials toward Sustainable Oxidation Catalysts

A successful encapsulation of Keggin-type polyoxomolybdate (H₃[PMo₁₂O₄₀], PMo₁₂) into metal-organic framework (MOF) materials with an identical framework but distinct metal centers (ZIF-8 with Zn²⁺ and ZIF-67 with Co²⁺) was accomplished by a straightforward room-temperature procedure. The presence of Zn²⁺ in the composite material PMo₁₂@ZIF-8 instead of Co²⁺ in PMo₁₂@ZIF-67 caused a remarkable increase in the catalytic activity that achieved a total oxidative desulfurization of a multicomponent model diesel under moderate and friendly conditions (oxidant: H₂O₂ and solvent: ionic liquid, IL). Interestingly, the parent ZIF-8-based composite with the Keggin-type polyoxotungstate (H₃[PW₁₂O₄₀], PW₁₂), PW₁₂@ZIF-8, did not show the relevant catalytic activity. The ZIF-type supports present an appropriate framework to accommodate active polyoxometalates (POMs) into their cavities without leaching, but the nature of the metallic center from the POM and the metal present in the ZIF framework were vital for the catalytic performance of the composite materials.

Lindqvist@Nanoporous MOF-Based Catalyst for Effective Desulfurization of Fuels

An effective and sustainable oxidative desulfurization process for treating a multicomponent model fuel was successfully developed using as a heterogeneous catalyst a composite material containing as an active center the europium Lindqvist [Eu(W5O18)2]9- (abbreviated as EuW10) encapsulated into the nanoporous ZIF-8 (zeolitic imidazolate framework) support. The EuW10@ZIF-8 composite was obtained through an impregnation procedure, and its successful preparation was confirmed by various characterization techniques (FT-IR, XRD, SEM/EDS, ICP-OES). The catalytic activity of the composite and the isolated EuW10 was evaluated in the desulfurization of a multicomponent model fuel containing dibenzothiophene derivatives (DBT, 4-MDBT and 4,6-DMDBT) with a total sulfur concentration of 1500 ppm. Oxidative desulfurization was performed using an ionic liquid as extraction solvent and aqueous hydrogen peroxide as oxidant. The catalytic results showed a remarkable desulfurization performance, with 99.5 and 94.7% sulfur removal in the first 180 min, for the homogeneous active center EuW10 and the heterogeneous EuW10@ZIF-8 catalysts, respectively. Furthermore, the stability of the nanocomposite catalyst was investigated by reusing and recycling processes. A superior retention of catalyst activity in consecutive desulfurization cycles was observed in the recycling studies when compared with the reusing experiments. Nevertheless, the nanostructure of ZIF-8 incorporating the active POM (polyoxometalate) was shown to be highly suitable for guaranteeing the absence of POM leaching, although structural modification was found for ZIF-8 after catalytic use that did not influenced catalytic performance.

Ionic Liquid-Based Polyoxometalate Incorporated at ZIF-8: A Sustainable Catalyst to Combine Desulfurization and Denitrogenation Processes

An effective and sustainable process capable of simultaneously execute desulfurization and denitrogenation of fuels is in fact an actual necessity in the refinery industry. The key to achieve this goal is the parallel oxidation of sulfur and nitrogen compounds present in fuels, which is only achieved by an active and recovered catalyst. A novel heterogeneous catalyst was successfully prepared by the encapsulation of an imidazolium-based polyoxometalate (POM) into a ZIF-8 framework ([BMIM]PMo₁₂@ZIF-8). This composite material revealed exceptional catalytic efficiency to concurrently proceed with the oxidative desulfurization and denitrogenation of a multicomponent model fuel containing various sulfur and nitrogen compounds. A complete removal of all these compounds was achieved after only one hour and the catalyst system was able to be reused for ten consecutive cycles without loss of efficiency. In fact, an ionic liquid POM was incorporated in the ZIF-8 for the first time, and this composite compound was originally applied as a catalyst for simultaneous oxidative desulfurization and denitrogenation processes.