Synthesis and characterization of new UV absorbing microspheres of narrow size distribution by dispersion polymerization of 2-(2′-hydroxy-5′-methacryloxyethylphenyl)-2H-benzotriazole

Design of UV-Absorbing Polypropylene Films with Polymeric Benzotriaziole Based Nano- and Microparticle Coatings

UV-absorbing nanoparticles (NPs) and microparticles (MPs) were prepared by emulsion and dispersion copolymerization of the vinylic monomer 2-(2'-hydroxy-5'-methacryloxyethylphenyl)-2H-benzotriazole (Norbloc (NB)) with the crosslinking monomer divinylbenzene. The effect of the initiator concentration on the size and size distribution of the polyNB (PNB) particles was elucidated. Thin coatings of the formed PNB NPs or MPs of 19 ± 2 and 200 ± 25 nm dry diameter, respectively, onto polypropylene (PP) films were then prepared and characterized. Increasing the concentration or thickness of the PNB NP or MP thin coatings on the PP films decreased their UV transmittance, up to complete UV blocking with just 2 μm of a 4% NP coating. Migration of the UV-absorbing agents from the coated PP films was not observed during three years of storage at room temperature, offering a unique solution to current problems of migration of UV-absorbing additives. The thin coatings obtained by the PNB NPs were superior to those of the PNB MPs, in that no UV transmittance or loss of optical properties of the PP films were observed for the NP coatings, while the coatings produced by the PNB MPs resulted in damaged optical properties, particularly increasing the haze, and achieved incomplete UV blocking.

Characterization and antibacterial properties of N-halamine-derivatized cross-linked polymethacrylamide nanoparticles

N-halamine-derivatized cross-linked polymethacrylamide nanoparticles with sizes ranging between 18 ± 2.0 and 460 ± 60 nm were prepared via surfactant-free dispersion co-polymerization of methacrylamide (MAA) and the cross-linking monomer N,N-methylenebisacrylamide (MBAA) in an aqueous continuous phase, followed by a chlorination process using sodium hypochlorite. The effect of various polymerization parameters (monomer concentration, initiator type and concentration, polymerization duration, polymerization temperature, and the weight ratio [MBAA]/[MAA]) on the size and size distribution of the produced cross-linked P(MAA-MBAA) nanoparticles was elucidated. The effect of various chlorination parameters (hypochlorite concentration, chlorination period and temperature) on the bound oxidative chlorine atom (Cl) content of the P(MAA-MBAA) nanoparticles was also investigated. The bactericidal activity of these chloramine-derivatized nanoparticles was tested against two common bacterial pathogens (Escherichia coli and Staphylococcus aureus), and they were found to be highly potent. Furthermore, these nanoparticles also exerted their antimicrobial activity against multi-drug resistant (MDR) bacteria, further demonstrating their efficacy.