Temperature induced complex formation-deformation behavior of collagen model peptides and polyelectrolytes in aqueous solution

Complex Formation of Silica Nanoparticles with Collagen: Effects of the Conformation of Collagen

Negatively charged Ludox silica nanoparticles (SiNPs) form a complex with atelocollagen (AC) in acidic buffers (pH = 4 or 3). AC is a low-immunogenic derivative of collagen obtained by the removal of N- and C-terminal telopeptide components. Mixed solutions of negatively charged SiNPs and AC were turbid, while positively charged SiNPs (Ludox CL) did not form a complex with AC in pH 4 buffer, indicating that electrostatic attraction is the dominant force to form the complex. Small-angle X-ray scattering (SAXS) and circular dichroism (CD) measurements were made for AC and Ludox LS (or CL) solutions in acetate buffer (pH 4.0) and citrate buffer (pH 3.0). The CD data showed that the stability of the triple helical structure of AC in the buffers is not affected by the complexation. The resulting complex consisting of triple helical AC and SiNPs did not influence the SAXS profile except for the lowest q region investigated. On the contrary, different scattering profiles were observed for the single chain AC and SiNP mixture indicating densely packed SiNPs in the complex. This scattering behavior was fairly explained in terms of the sticky hard sphere model (SHSM). This AC conformation-dependent complexation may be because of the hydrogen bonding interaction between the single chain AC and SiNPs. The temperature-induced change of the complex formation can be applied for thermoresponsive hybrid materials.

Self-Assembly of Amphiphilic Amylose Derivatives in Aqueous Media

Six amylose derivative (C₁₂CMA) samples with hydrophobic dodecyl ether groups and hydrophilic sodium carboxymethyl groups were synthesized from an enzymatically synthesized amylose for which the weight-average molar mass is 50 kg mol^-1 to realize amylose-based amphiphilic polymer micelles. The degree of substitution of hydrophobic (DS_C12) and hydrophilic (DS_CM) groups ranges between 0.076 and 0.39 and between 0.35 and 1.83, respectively. Static and dynamic light scattering, small-angle X-ray scattering (SAXS), and fluorescence measurements with pyrene as a probe were carried out for the samples in 150 mM aqueous NaCl to characterize the higher-order structure in solution. The fluorescence from pyrene showed that all six samples have hydrophobic environment, while the hydrophobicity tends to increase with rising DS_C12. All six samples have high scattering intensity owing to the relatively large concentrated droplets ranging in the hydrodynamic radius from 50 to 110 nm, whereas the weight fraction of such large particles is substantially small except for the highest DS_C12 sample. Most polymer chains for relatively low DS_C12 of 0.076 were molecularly dispersed with a very small amount of large droplets. The dispersed chain has a slightly smaller helix pitch per residue and a more rigid main chain than those for amylose in dimethyl sulfoxide, suggesting that the amylosic main chain of C₁₂CMA has a helical structure with dodecyl groups at least locally. On the other hand, an anisotropic shaped micelle-like structure is only found for relatively high DS_C12 (0.23 and 0.39) samples, which was detected by the SAXS profile at a high scattering vector range. The micelle structure for high DS_C12 samples is consistent with the high chain stiffness.