Intrinsically microporous polyimides derived from norbornane-2-spiro-α-cyclopentanone-α′-spiro-2″-norbornane-5,5″,6,6″-tetracarboxylic dianhydride

Incorporation of Carbocyclic Moieties into Polymer Structure: A Powerful Way to Polymers with Increased Microporosity

Microporous soluble polymers attract great attention as materials for membrane gas separation, gas storage and transportation, as sorbents, supports for catalysts, and matrices for mixed matrix membranes. The key problems in the development of this area of polymer chemistry include the search for methods of controlling the porous structure parameters and ensuring the stability of their properties over time. In this connection, a fruitful approach is to introduce bulky and rigid, often framework carbocyclic moieties into the polymer backbones and side chains. This review discusses the effect of carbocyclic moieties on gas transport properties, BET surface area, and FFV of glassy polymers, such as polyacetylenes, polynorbornenes, polyimides, and ladder and partially ladder polymers. In the majority of cases, the incorporation of carbocyclic moieties makes it possible to controllably increase these three parameters. Carbocyclic moieties can also improve CO2/gas separation selectivity, which is displayed for ladder polymers and polynorbornenes.

Intrinsically Microporous Polyimides Derived from 2,2'-Dibromo-4,4',5,5'-bipohenyltetracarboxylic Dianhydride for Gas Separation Membranes

This work aims to expand the structure-property relationships of bromo-containing polyimides and the influence of bromine atoms on the gas separation properties of such materials. A series of intrinsically microporous polyimides were synthesized from 2,2'-dibromo-4,4',5,5'-bipohenyltetracarboxylic dianhydride (Br-BPDA) and five bulky diamines, (7,7'-(mesitylmethylene)bis(8-methyldibenzo[b,e][1,4]dioxin-2-amine) (MMBMA), 7,7'-(Mesitylmethylene)bis(1,8-dimethyldibenzo[b,e][1,4] dioxin-2-amine) (MMBDA), 4,10-dimethyl-6H,12H-5,11-methanodibenzo[b,f][1,5]diazocine-2,8-diamine (TBDA1), 4,10-dimethyl-6H,12H-5,11-methanodibenzo[b,f][1,5]diazocine-3,9-diamine (TBDA2), and (9R,10R)-9,10-dihydro-9,10-[1,2]benzenoanthracene-2,6-diamine (DAT). The Br-BPDA-derived polyimides exhibited excellent solubility, high thermal stability, and good mechanical properties, with their tensile strength and modulus being 59.2-109.3 MPa and 1.8-2.2 GPa, respectively. The fractional free volumes (FFVs) and surface areas (SBET) of the Br-BPDA-derived polyimides were in the range of 0.169-0.216 and 211-342 m2 g-1, following the order of MMBDA > MMBMA > TBDA2 > DAT > TBDA1, wherein the Br-BPDA-MMBDA exhibited the highest SBET and FFV and thus highest CO2 permeability of 724.5 Barrer. Moreover, Br-BPDA-DAT displayed the best gas separation performance, with CO2, H2, O2, N2, and CH4 permeabilities of 349.8, 384.4, 69.8, 16.3, and 19.7 Barrer, and H2/N2 selectivity of 21.4. This can be ascribed to the ultra-micropores (<0.7 nm) caused by the high rigidity of Br-BPDA-DAT. In addition, all the bromo-containing polymers of intrinsic microporosity membranes exhibited excellent resistance to physical ageing.