Gas transport properties of truxene-based network polyimide membrane with flexible hexyl side chains

Intrinsically Microporous Polyimides Based on a Rigid-Soft Structure for Hydrogen Separation

Polyimide (PI)-based gas separation membranes are of great interest in the field of H2 purification owing to their good thermal stability, chemical stability, and mechanical properties. Among polyimide-based membranes, intrinsically microporous polyimides are easily soluble in common organic solvents, showing great potential for fabricating hollow fiber gas separation membranes. However, based on the solution-diffusion model, improving the free volume or the movability of polymer chains can improve gas permeability, but would result in poor thermal stability. Herein, we develop a carbazole-alkyl-based diamine monomer that endows PI chains with a "rigid-soft" structure to balance the trade-off between them. Soft units enhance the movability of polymer chains during the film-forming process, ensuring that rigid units achieve tight chain packing and strong intermolecular interactions. Meanwhile, bulky carbazole groups could further restrict the motion of soft units in the solid state. On the one hand, it restricts the movability of the polymer chains below Tg, enhancing the small gas selectivity for H2 and He. On the other hand, it ensures good thermal stability. Moreover, extending the length of the alkyl chains helps improve the free volume and intermolecular interactions simultaneously, thereby further optimizing the gas permeability/selectivity trade-off. As a result, the as-prepared PI shows H2 permeability of 89.61 Barrer, H2/CH4 selectivity of 87.85, and H2/N2 selectivity of 45.03 in contrast to the reference FPI TFMB-6FDA exhibiting H2 permeability of 92.95 Barrer, H2/CH4 selectivity of 72.62, and H2/N2 selectivity of 38.57. Meanwhile, a high Tg value of 334 °C is also achieved.

Tailoring the Micropore Structure of 6FDA-Based Network Polyimide Membranes for Advanced Gas Separation by Decarboxylation

The 6FDA-based network PI has attracted significant attention for gas separation. A facile strategy to tailor the micropore structure within the network PI membrane prepared by the in situ crosslinking method is extremely significant for achieving an advanced gas separation performance. In this work, the 4,4'-diamino-2,2'-biphenyldicarboxylic acid (DCB) or 3,5-diaminobenzoic acid (DABA) comonomer was incorporated into the 6FDA-TAPA network polyimide (PI) precursor via copolymerization. The molar content and the type of carboxylic-functionalized diamine were varied in order to easily tune the resulting network PI precursor structure. Then, these network PIs containing carboxyl groups underwent further decarboxylation crosslinking during the following heat treatment. Properties involving thermal stabilities, solubility, d-spacing, microporosity, and mechanical properties were investigated. Due to the decarboxylation crosslinking, the d-spacing and the BET surface areas of the thermally treated membranes were increased. Moreover, the content of DCB (or DABA) played a key role in determining the overall gas separation performance of the thermally treated membranes. For instance, after the heating treatment at 450 °C, 6FDA-DCB:TAPA (3:2) showed a large increment of about ~532% for CO₂ gas permeability (~266.6 Barrer) coupled with a decent CO₂/N₂ selectivity~23.6. This study demonstrates that incorporating the carboxyl-containing functional unit into the PI backbone to induce decarboxylation offers a practical approach with which to tailor the micropore structure and corresponding gas transport properties of 6FDA-based network PIs prepared by the in situ crosslinking method.