Mechanical properties and microstructural change of W-Y2O3 alloy under helium irradiation.
Sci Rep 2015;
5:12755. [PMID:
26227480 PMCID:
PMC4521205 DOI:
10.1038/srep12755]
[Citation(s) in RCA: 71] [Impact Index Per Article: 7.9] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/12/2015] [Accepted: 07/09/2015] [Indexed: 11/09/2022] Open
Abstract
A wet-chemical method combined with spark plasma sintering was used to prepare a W–Y2O3 alloy. High-temperature tensile tests and nano-indentation microhardness tests were used to characterize the mechanical properties of the alloy. After He-ion irradiation, fuzz and He bubbles were observed on the irradiated surface. The irradiation embrittlement was reflected by the crack indentations formed during the microhardness tests. A phase transformation from α-W to γ-W was investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Polycrystallization and amorphization were also observed in the irradiation damage layer. The W materials tended to exhibit lattice distortion, amorphization, polycrystallization and phase transformation under He-ion irradiation. The transformation mechanism predicted by the atomic lattice model was consistent with the available experimental observations. These findings clarify the mechanism of the structural transition of W under ion irradiation and provide a clue for identifying materials with greater irradiation resistance.
Collapse