Mechanical and Microstructural Characterization of Al-5083/St-12 lap joints made by friction stir welding

Effect of Microstructure and Tensile Shear Load Characteristics Evaluated by Process Parameters in Friction Stir Lap Welding of Aluminum-Steel with Pipe Shapes

In recent years, friction stir welding (FSW) of dissimilar materials has become an important issue in lightweight and eco-friendly bonding technology. Although weight reduction of low-rigidity parts has been achieved, the weight reduction has been minimal because high-rigidity parts such as chassis require the use of iron. Considering the difficulty of welding a pipe shape, it is necessary to understand the effect of process parameters on mechanical performance. As a result of the study by various process parameters affecting the joint between aluminum and steel in the shape of a pipe, it can be seen that the tool penetration depth (TPD) has the most important effect on the tensile shear load (TSL). However, the effect of TPD on intermetallic compound (IMC), which has the most important influence on fracture, has not been well established. In this study, the effect of process parameters on IMC thickness and TSL in FSW of A357 cast aluminum and FB590 high tensile steel was investigated to reduce the weight of the torsion beam shaft of an automobile chassis. After the FSWed experiment, measurements were performed using an optical microscope and scanning electron microscopy (SEM) to investigate the microstructure of the weld. The formation of an IMC layer was observed at the interlayer between aluminum and steel. TPD is a major factor in IMC thickness variation, and there is a direct relationship between IMC thickness reduction and TSL increase, except for certain sections where the welding speed (WS) effect is large. Therefore, in order to improve mechanical properties in friction stir lap welding of aluminum and steel for high-rigidity parts, it is necessary to deepen the TPD at a level where flow is dominant rather than heat input.

Effect of Tilt Angle and Pin Depth on Dissimilar Friction Stir Lap Welded Joints of Aluminum and Steel Alloys

Automobile, aerospace, and shipbuilding industries are looking for lightweight materials for cost effective manufacturing which demands the welding of dissimilar alloy materials. In this study, the effect of tool rotational speed, welding speed, tilt angle, and pin depth on the weld joint were investigated. Aluminum 5052 and 304 stainless-steel alloys were joined by friction stir welding in a lap configuration. The design of the experiments was based on Taguchi's orthogonal array for conducting the experiments with four factors and three levels for each factor. The microstructural analysis showed tunnel defects, micro voids, and cracks which formed with 0° and 1.5° tilt angles. The defects were eliminated when the tilt angle increased to 2.5° and a mixed stir zone was formed with intermetallic compounds. The presence of the intermetallic compounds increased with the increase in tilt angle and pin depth which further resulted in obtaining a defect-free weld. Hooks were formed on either side of the weld zone creating a mechanical link for the joint. A Vickers hardness value of HV 635.46 was achieved in the mixed stir zone with 1000 rpm, 20 mm/min, and 4.2 mm pin depth with a tilt angle of 2.5°, which increased by three times compared to the hardness of SS 304 steel. The maximum shear strength achieved with 800 rpm, 40 mm/min, and a 4.3 mm pin depth with a tilt angle of 2.5° was 3.18 kN.