Effect of zirconium nitride physical vapor deposition coating on preosteoblast cell adhesion and proliferation onto titanium screws

Analyzing the Surface Topography of Hafnium Nitride Coating on Titanium Screws: An In Vitro Analysis

Background The use of surface coatings to enhance the properties lacking in titanium has attracted significant focus in recent times. Hafnium nitride (HfN) coatings could be explored as promising in the osteoinductive properties of titanium implants. HfN exhibits excellent mechanical attributes, such as hardness and wear resistance, and is often used as a coating on high-end equipment for protection. The findings from this research may carve a new path for the production and optimization of HfN coatings to enhance the longevity and augment properties of implant materials. Thus, the present study was orchestrated to elucidate the surface morphology of HfN coating, ultimately contributing to the advancement of dental implant biomaterials. Materials and methods A total of twenty samples of medical grade commercially pure titanium screws (2 mm diameter and 7 mm length) were procured from G. R. Bioure Surgical System Pvt. Ltd., Ravali, Uttar Pradesh, India, and ten samples were reacted with HfN (0.1 M) (Nano Research Elements, Kurukshetra, Haryana, India) in 100% ethanol and stirred continuously for about 48 hours. Then these screw samples were immersed in the prepared colloidal suspension and sintered for two hours at 400 degrees centigrade. The implant screws were affixed onto metal supports. The magnifications for photomicrographs at ×30, ×200, ×1,500, ×3,000, and ×5,000 were standardized. Elementary semi-quantitative analysis of both dental implants was conducted using energy-dispersive X-ray spectrometry (EDX) coupled with the field emission scanning electron microscope (FE-SEM) equipment (JEOL Ltd., Akishima, Tokyo, Japan). The software used for the analysis of the obtained images is SEM Center. Results The surface analysis using the scanning electron microscope (SEM) showed the coating of HfN over titanium screws. The difference in surface morphology of both the group of implant screws can be visualized under 40.0 and 10.0 mm working distance (WD) for both groups. The surface analysis using the EDX of uncoated titanium screws shows five elements in the spectrum: titanium (Ti), oxygen (O), aluminum (Al), carbon (C), and vanadium (V). The EDX of the HfN-coated screws has two additional metals dispersed in the spectrum, hafnium (Hf). The element characteristics are tabulated with their apparent concentration, k ratio, line type, weight percentage, standard label, and factory label for uncoated titanium screws and HfN-coated titanium screws. Conclusion The study evaluated HfN coating over medical grade commercially pure titanium. The surface topography of coated versus uncoated was visualized. The scanning electron microscope (SEM) images showed a homogenous coating over the titanium surfaces, and the EDX showed elemental dispersion of the coated implant. The study aims to provide a comprehensive understanding of the coating's surface morphology, which will aid in the development of more durable and biocompatible implants. This thereby provides a promising scope for further research of this novel metal coating for use in the biomedical sectors, specifically for dental implants.

Epithelial Biological Response to Machined Titanium vs. PVD Zirconium-Coated Titanium: An In Vitro Study

The aim of this study was to compare the epithelial biological response to machined titanium Ti-6Al-4V grade 5 and titanium Ti-6Al-4V grade 5 coated with zirconia (ZrN) by physical vapor deposition (PVD). Human keratinocytes were cultured in six-well plates. Machined titanium TiAl4V4 grade 5 (T1) and ZrN-coated titanium TiAl4V4 grade 5 (T2) discs were placed in two different wells. The remaining two wells served as control (C). Scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were performed to compare the T1 and T2 surfaces. Subsequent analyses were performed to explore the effect of T1 and T2 contact with human keratinocyte HUKE cell lines. Cell viability was evaluated using a trypan blue exclusion test and MTT assay. Cell lysates from C, T1, and T2 were Western blotted to evaluate E-cadherin and Integrin-α6β4 expression. SEM revealed that T2 was smoother and more homogeneous than T1. EDS showed homogeneous and uniform distribution of ZrN coating on T2. Cell viability analyses did not show significant differences between T1 and T2. Furthermore, E-cadherin and Integrin-α6β4 expressions of the epithelial cells cultured in T1 and T2 were similar. Therefore, titanium Ti-6Al-4V grade 5 surfaces coated with ZrN by PVD seem to be similar substrates to the uncoated surfaces for keratinocyte adhesion and proliferation.

Zirconium Oxide Thin Films Obtained by Atomic Layer Deposition Technology Abolish the Anti-Osteogenic Effect Resulting from miR-21 Inhibition in the Pre-Osteoblastic MC3T3 Cell Line

Introduction

The development of the field of biomaterials engineering is rapid. Various bioactive coatings are created to improve the biocompatibility of substrates used for bone regeneration, which includes formulation of thin zirconia coatings with pro-osteogenic properties. The aim of this study was to assess the biological properties of ZrO₂ thin films grown by Atomic Layer Deposition (ALD) technology (ZrO₂^ALD).

Methodology

The cytocompatibility of the obtained layers was analysed using the mice pre-osteoblastic cell line (MC3T3) characterized by decreased expression of microRNA 21-5p (miR-21-5p) in order to evaluate the potential pro-osteogenic properties of the coatings. The in vitro experiments were designed to determine the effect of ZrO₂^ALD coatings on cell morphology (confocal microscope), proliferative activity (cell cycle analysis) and metabolism, reflected by mitochondrial membrane potential (cytometric-based measurement). Additionally, the influence of layers on the expression of genes associated with cell survival and osteogenesis was studied using RT-qPCR. The following genes were investigated: B-cell lymphoma 2 (Bcl-2), Bcl-2-associated X protein (Bax), p53 and p21, as well as osteogenic markers, i.e. collagen type 1 (Coll-1), osteopontin (Opn), osteocalcin (Ocl) and runt-related transcription factor 2 (Runx-2). The levels of microRNA (miRNA/miR) involved in the regulation of osteogenic genes were determined, including miR-7, miR-21, miR-124 and miR-223.

Results

The analysis revealed that the obtained coatings are cytocompatible and may increase the metabolism of pre-osteoblast, which was correlated with increased mitochondrial membrane potential and extensive development of the mitochondrial network. The obtained coatings affected the viability and proliferative status of cells, reducing the population of actively dividing cells. However, in cultures propagated on ZrO₂^ALD coatings, the up-regulation of genes essential for bone metabolism was noted.

Discussion

The data obtained indicate that ZrO₂ coatings created using the ALD method may have pro-osteogenic properties and may improve the metabolism of bone precursor cells. Given the above, further development of ZrO₂^ALD layers is essential in terms of their potential clinical application in bone regenerative medicine.