Effects of Zn-In-Sn elements on the electric properties of magnesium alloy anode materials

High-Performance Mg–Al–Bi Alloy Anode for Seawater Batteries and Related Mechanisms

Bi, a group 15 element, was added to magnesium alloys and applied to seawater batteries in marine operating machinery to improve the electrochemical performance and corrosion resistance of the battery. The electrochemical properties of as-cast pure Mg, Mg–8Al, and Mg–8Al–xBi alloy anodes in 3.5% NaCl solution were researched. Electrochemical impedance spectroscopy and an immersion test in 3.5% NaCl solution show that the Mg–8%Al–0.4%Bi alloy provides better corrosion resistance than Mg and the Mg–8Al alloy. The galvanostatic discharge results show that the Mg–8%Al–0.4%Bi alloy revealed better electrochemical properties and utilization efficiency in 3.5% NaCl solution. The Mg17Al12 and BiOCl phases formed during the discharge process of the Mg–8%Al–0.4%Bi alloy play an important role in improving the electrochemical performance and utilization efficiency of the alloy.

Effect of stress corrosion cracking at various strain rates on the electrochemical corrosion behavior of Mg-Zn-In-Sn alloy

This study is aimed to determine the effect of stress corrosion with low strain rates on the electrochemical properties of alloy electrode. Stress corrosion cracking tests of Mg-Zn-In-Sn alloy in 3.5 wt.% sodium chloride solutions at 25°C were performed. The effects of the electrochemical properties under the stress corrosion with low strain rates were investigated. The microstructures of cross section were observed by optical microscope. The results showed that the ultimate tensile strengths of Mg-Zn-In-Sn alloy increased and the strain decreased as the strain rates increased. Open circuit potentials (OCP) of Mg-Zn-In-Sn alloy electrode possess stability and the loop currents (LC) were improved with the increasing of stress in the elastic zone. The variation of OCP and LC did not change with the increasing of strain-rate. The microstructure of cross section observing revealed the mechanism of OCP and LC changing.