Reorientation Times for Solid-State Electrolyte Solvents and Electrolytes from NMR Spin-Lattice Relaxation Studies

Shear rheology senses the electrical room-temperature conductivity optimum in highly Li doped dinitrile electrolytes

Glutaronitrile (GN) doped with lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) at concentrations below and above the room-temperature conductivity optimum near 1M of Li salt is investigated using dielectric spectroscopy and shear rheology. The experiments are carried out from ambient down to the glass transition temperature Tg, which increases considerably as LiTFSI is admixed to GN. As the temperature is lowered, the conductivity optimum shifts to lower salt concentrations, while the power-law exponents connecting resistivity and molecular reorientation time remain smallest for the 1M composition. By contrast, the rheologically detected time constants, as well as those obtained using dielectric spectroscopy, increase monotonically with increasing Li salt concentration for all temperatures. It is demonstrated that the shear mechanical measurements are, nevertheless, sensitive to the 1M conductivity optimum, thus elucidating the interplay of the dinitrile matrix with the mobile species. The data for the Li doped GN and other nitrile solvents all follow about the same Walden line, in harmony with their highly conductive character. The composition dependent relation between the ionic and the reorientational dynamics is also elucidated.

Paddle-wheel mechanism in doped succinonitrile-glutaronitrile plastic electrolyte: a joint magnetic resonance, dielectric, and viscosimetry study of Li ion translational and molecular reorientational dynamics

Mixtures of 60% SN (succinonitrile) and 40% GN (glutaronitrile) doped with LiTFSI or LiPF₆ at different concentrations are investigated using dielectric spectroscopy. Room temperature conductivities up to 10^-3 S cm^-1 are measured along with an overall conductivity enhancement of almost five decades compared to pure SN. Additionally, the dynamics of the methylene (CD₂) groups of SN and that of the Li⁺ ions within the mixture are studied in a wide temperature range using ²H and ⁷Li NMR relaxometry, respectively. Static-field-gradient proton NMR combined with viscosity measurements probe the molecular diffusion. GN addition and Li doping both enhance the electrical conductivity significantly, while leaving the reorientational motion within the matrix essentially unchanged. The times scales and thus the effective energy barriers characterizing the Li ion motion as well as the molecular reorientations are very similar in the liquid and in the plastic phases, findings that argue in favor of the presence of a paddle-wheel mechanism.