Analysis of Antibacterial Efficacy and Cellular Alignment Regulation on Plasma Nanotextured Chitosan Surfaces

Enhancing silk fibroin structures and applications through angle-dependent Ar+ plasma treatment

This study tackles limitations of Silk Fibroin (SF), including availability of sites for modification. This is achieved by Direct Plasma Nanosynthesis (DPNS), an Ar+ bombardment method, to generate and modify nanostructures and nanoscale properties on the SF surface. SF samples were treated with DPNS at incidence angles of 45o and 60o, with specific ion dose and energy parameters (1 × 1018 ions/cm2 and 500 eV, respectively) maintained throughout the process. Fourier-transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) primarily underscored transformations in SF's nitrogenous components. Specifically, treatment produced a boost in C-NH2, particularly pronounced in the 45o-treated samples, suggesting changes were more superficial than alterations to the secondary structure. The DPNS treatment gave rise to periodic nanocone structures on the SF surface, with a scale increase correlated to a higher angle of incidence. This resulted in a decrease in surface stiffness and significant changes in the motility of J774 macrophages interacting with the transformed SF. Furthermore, the SF samples treated at a 60o incidence showcased a confinement effect, moderating the macrophages' motility, morphology, and inflammatory response. The DPNS-induced alterations not only mitigate SF's limitations but also affect cellular behavior, expanding potential for SF in biomaterials.

Ion-bombardment-driven surface modification of porous magnesium scaffolds: Enhancing biocompatibility and osteoimmunomodulation

Porous Mg scaffolds are promising for bone repair but are limited by high corrosion rates and challenges in preserving coating integrity. We used Directed Plasma Nanosynthesis (DPNS) at 400 eV and a fluence of 1 × 1018 cm-2 to augment the bioactivity and corrosion resistance of porous Mg scaffolds, maintaining their overall material integrity. DPNS creates nanostructures that increase surface area, promote apatite nucleation, and enhance osseointegration, improving the bioactivity and corrosion resistance of porous Mg scaffolds without compromising their structure. Our findings indicate a decrease in surface roughness, with pre-irradiated samples having Rq = 60.4 ± 5.3 nm andRa = 48.2 ± 3.1 nm, and post-DPNS samples showing Rq = 36.9 ± 0.3 nm andRa = 28.6 ± 0.8 nm. This suggests changes in topography and wettability, corroborated by the increased water contact angles (CA) of 129.2 ± 3.2 degrees. The complexity of the solution influences the CA: DMEM results in a CA of 120.4 ± 0.1 degrees, while DMEM + SBF decreases it to 103.6 ± 0.5 degrees, in contrast to the complete spreading observed in non-irradiated samples. DPNS-treated scaffolds exhibit significantly reduced corrosion rates at 5.7 × 10-3 ± 3.8 × 10-4 mg/cm²/day, compared to the control's 2.3 × 10-2 ± 3.2 × 10-4 mg/cm²/day over 14 days (P < 0.01). The treatment encourages the formation of a Ca-phosphate-rich phase, which facilitates cell spreading and the development of focal adhesion points in hBM-MSCs on the scaffolds. Additionally, J774A.1 murine macrophages show an enhanced immune response with diminished TNF-α cytokine expression. These results offer insights into nanoscale modifications of Mg-based biomaterials and their promise for bone substitutes or tissue engineering scaffolds.

Ion Bombardment-Induced Nanoarchitectonics on Polyetheretherketone Surfaces for Enhanced Nanoporous Bioactive Implants

In spite of the biocompatible, nontoxic, and radiolucent properties of polyetheretherketone (PEEK), its biologically inert surface compromises its use in dental, orthopedic, and spine fusion industries. Many efforts have been made to improve the biological performance of PEEK implants, from bioactive coatings to composites using titanium alloys or hydroxyapatite and changing the surface properties by chemical and physical methods. Directed plasma nanosynthesis (DPNS) is an atomic-scale nanomanufacturing technique that changes the surface topography and chemistry of solids via low-energy ion bombardment. In this study, PEEK samples were nanopatterned by using argon ion irradiation by DPNS to yield active nanoporous biomaterial surface. PEEK surfaces modified with two doses of low and high fluence, corresponding to 1.0 × 1017 and 1.0 × 1018 ions/cm2, presented pore sizes of 15-25 and 60-90 nm, respectively, leaving exposed PEEK fibers and an increment of roughness of nearly 8 nm. The pores per unit area were closely related for high fluence PEEK and low fluence PEEK surfaces, with 129.11 and 151.72 pore/μm2, respectively. The contact angle significantly decreases in hydrophobicity-hydrophilicity tests for the irradiated PEEK surface to ∼46° from a control PEEK value of ∼74°. These super hydrophilic substrates had 1.6 times lower contact angle compared to the control sample revealing a rough surface of 20.5 nm only at higher fluences when compared to control and low fluences of 12.16 and 14.03 nm, respectively. These super hydrophilic surfaces in both cases reached higher cell viability with ∼13 and 34% increase, respectively, compared to unmodified PEEK, with an increased expression of alkaline phosphatase at 7 days on higher fluences establishing a higher affinity for preosteblasts with increased cellular activity, thus revealing successful and improved integration with the implant material, which can potentially be used in bone tissue engineering.