Semiempirical Peak Fitting Guided by ab Initio Calculations of X-ray Photoelectron Spectroscopy Narrow Scans of Chemisorbed, Fluorinated Silanes

A Novel Flame-Retardant, Smoke-Suppressing, and Superhydrophobic Transparent Bamboo

Silica glass, known for its brittleness, weight, and non-biodegradable nature, faces challenges in finding suitable alternatives. Transparent wood, made by infusing polymers into wood, shows promise but is hindered by limited availability of wood in China and fire risks associated with its use. This study explores the potential of utilizing bamboo, which has a shorter growth cycle, as a valuable resource for developing flame-retardant, smoke-suppressing, and superhydrophobic transparent bamboo. A 3-layered flame-retardant barrier, composed of a top silane layer, an intermediate layer of SiO2 formed through hydrolysis-condensation of Na2SiO3 on the surface, and an inner layer of Na2SiO3, has been confirmed to be effective in reducing heat release, slowing flame spread, and inhibiting the release of combustible volatiles, toxic smoke, and CO. Compared to natural bamboo and other congeneric transparent products, the transparent bamboo displays remarkable superiority, with the majority of parameters being notably lower by an entire order of magnitude. It achieves a long ignition time of 116 s, low total heat release (0.7 MJ/m2), low total smoke production (0.063 m2), and low peak CO concentration (0.008 kg/kg). Moreover, when used as a substrate for perovskite solar cells, the transparent bamboo displays the potential to act as a light management layer, leading to a marked efficiency enhancement of 15.29%. The excellent features of transparent bamboo make it an enticing choice for future advancements in flame-retardant glasses and optical devices.

In situ synchrotron X-ray scission of polytetrafluoroethylene chains and elucidation of dry etching

We investigated the mechanism of polytetrafluoroethylene (PTFE) chain scission through in situ hard X-ray photoelectron spectroscopy at room temperature, 200 °C, and 230 °C. The C-C bonds in the main chain and C-F bonds in the side chains were broken, and F desorption from the PTFE surface was observed at room temperature. The formation of CF₃ was also observed from the recombination of broken C-C bonds in the main chain and detached F, which were not induced by soft X-rays. In contrast, when the PTFE substrate was irradiated with hard X-rays at 200 °C, the CF₃ intensity initially produced by recombination reactions decreased with irradiation time, and the photoelectron spectrum retained the original PTFE spectrum. Under these conditions, the F1s/C1s intensity ratio did not change with the irradiation time; hence, the fragment containing only CF₂, the chemical composition of the original PTFE, was desorbed. When the substrate temperature was 230 °C, the CF₃ intensity increased in relation to that at 200 °C. This result indicated that the formation of CF₃ via recombination reactions of broken molecular chains is enhanced by thermal assistance. These phenomena were considered to be based on the balance between recombination and desorption by photochemical and pyrochemical reactions. These results will lead to a better understanding of the use of X-ray-irradiated fluorine resins and PTFE in potential space-based environments. This study will also promote the improvement of PTFE microfabrication methods and thin-film formation using synchrotron radiation.