Janewithayapun R, Hedenqvist MS, Cousin F, Idström A, Evenäs L, Lopez-Sanchez P, Westman G, Larsson A, Ström A. Nanostructures of etherified arabinoxylans and the effect of arabinose content on material properties. Carbohydr Polym 2024; 331:121846. [PMID: 38388051 DOI: 10.1016/j.carbpol.2024.121846] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/16/2023] [Revised: 01/01/2024] [Accepted: 01/18/2024] [Indexed: 02/24/2024]
Abstract
To further our understanding of a thermoplastic arabinoxylan (AX) material obtained through an oxidation-reduction-etherification pathway, the role of the initial arabinose:xylose ratio on the material properties was investigated. Compression molded films with one molar substitution of butyl glycidyl ether (BGE) showed markedly different tensile behaviors. Films made from low arabinose AX were less ductile, while those made from high arabinose AX exhibited elastomer-like behaviors. X-ray scattering confirmed the presence of nanostructure formation resulting in nano-domains rich in either AX or BGE, from side chain grafting. The scattering data showed variations in the presence of ordered structures, nano-domain sizes and their temperature response between AX with different arabinose contents. In dynamic mechanical testing, three transitions were observed at approximately -90 °C, -50 °C and 80 °C, with a correlation between samples with more structured nano-domains and those with higher onset transition temperatures and lower storage modulus decrease. The mechanical properties of the final thermoplastic AX material can therefore be tuned by controlling the composition of the starting material.
Collapse
Affiliation(s)
- Ratchawit Janewithayapun
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
| | - Mikael S Hedenqvist
- FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; Department of Fibre and Polymer Technology, School of Engineering Science in Chemistry, Biotechnology and Health, KTH Royal Institute of Technology, SE-100 44 Stockholm, Sweden; Wallenberg Wood Science Center, KTH Royal Institute of Technology, SE-100 44, Stockholm, Sweden
| | - Fabrice Cousin
- Laboratoire Léon Brillouin, Université Paris-Saclay, UMR 12, CEA-CNRS, 91191 Gif Sur Yvette, France
| | - Alexander Idström
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
| | - Lars Evenäs
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; Wallenberg Wood Science Center, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
| | - Patricia Lopez-Sanchez
- Department of Analytical Chemistry, Nutrition, and Food Science. Facultad de Ciencias, Instituto de Materiales (IMATUS), Universidade de Santiago de Compostela, Campus Terra, 27002 Lugo, Spain
| | - Gunnar Westman
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; Wallenberg Wood Science Center, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
| | - Anette Larsson
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; Wallenberg Wood Science Center, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden
| | - Anna Ström
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden; FibRe Center for Lignocellulose-based Thermoplastics, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden.
| |
Collapse
|
2
|
Ali MA, Singh M, Zhang S, Kaneko D, Okajima MK, Kaneko T. Metal-Assisted Injection Spinning of Ultra Strong Fibers from Megamolecular LC Polysaccharides. Polymers (Basel) 2024; 16:1099. [PMID: 38675018 PMCID: PMC11054878 DOI: 10.3390/polym16081099] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/13/2024] [Revised: 04/09/2024] [Accepted: 04/10/2024] [Indexed: 04/28/2024] Open
Abstract
The molecular orientation of liquid crystalline (LC) hydrogels has the potential to induce a range of functionalities that can deliver great mechanical strength. Sacran is a supergiant LC polysaccharide isolated from the cyanobacterium Aphanothece sacrum with a high amount of anionic functional groups such as sulfates and carboxylates. In this article, ultra-strong sacran hydrogels and their dried fibers were produced by cross-linking under injection flow with trivalent metal ions such as Al3+, Cr3+, Fe3+, In3+, and rare-earth metal ions such Er3+ and Sr3+. Crossed-polarizing microscopy and X-ray diffraction imaging revealed a uniaxial molecular orientation in the LC gel fiber, resulting in outstanding mechanical characteristics.
Collapse
Affiliation(s)
- Mohammad Asif Ali
- Key Laboratory of Synthetic and Biological Colloids, Ministry of Education, School of Chemical and Material Engineering, Jiangnan University, 1800 Lihu Ave, Wuxi 214122, China; (M.A.A.); (D.K.)
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| | - Maninder Singh
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| | - Shuo Zhang
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| | - Daisaku Kaneko
- Key Laboratory of Synthetic and Biological Colloids, Ministry of Education, School of Chemical and Material Engineering, Jiangnan University, 1800 Lihu Ave, Wuxi 214122, China; (M.A.A.); (D.K.)
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| | - Maiko Kaneko Okajima
- Key Laboratory of Synthetic and Biological Colloids, Ministry of Education, School of Chemical and Material Engineering, Jiangnan University, 1800 Lihu Ave, Wuxi 214122, China; (M.A.A.); (D.K.)
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| | - Tatsuo Kaneko
- Key Laboratory of Synthetic and Biological Colloids, Ministry of Education, School of Chemical and Material Engineering, Jiangnan University, 1800 Lihu Ave, Wuxi 214122, China; (M.A.A.); (D.K.)
- Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technologies, 1-1 Asahidai, Nomi 923-1292, Ishikawa, Japan; (M.S.); (S.Z.)
| |
Collapse
|
3
|
Deralia PK, Sonker AK, Lund A, Larsson A, Ström A, Westman G. Side chains affect the melt processing and stretchability of arabinoxylan biomass-based thermoplastic films. CHEMOSPHERE 2022; 294:133618. [PMID: 35066072 DOI: 10.1016/j.chemosphere.2022.133618] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 08/25/2021] [Revised: 01/03/2022] [Accepted: 01/11/2022] [Indexed: 06/14/2023]
Abstract
Hydrophobization of hemicellulose causes melt processing and makes them stretchable thermoplastics. Understanding how native and/or appended side chains in various hemicelluloses after chemical modification affect melt processing and material properties can help in the development of products for film packaging and substrates for stretchable electronics applications. Herein, we describe a one-step and two-step strategy for the fabrication of flexible and stretchable thermoplastics prepared by compression molding of two structurally different arabinoxylans (AX). For one-step synthesis, the n-butyl glycidyl ether epoxide ring was opened to the hydroxyl group, resulting in the introduction of alkoxide side chains. The first step in the two-step synthesis was periodate oxidation. Because the melt processability for AXs having low arabinose to xylose ratio (araf/xylp<0.5) have been limited, two structurally distinct AXs extracted from wheat bran (AXWB, araf/xylp = 3/4) and barley husk (AXBH, araf/xylp = 1/4) were used to investigate the effect of araf/xylp and hydrophobization on the melt processability and properties of the final material. Melt compression processability was achieved in AXBH derived samples. DSC and DMA confirmed that the thermoplastics derived from AXWB and AXBH had dual and single glass transition (Tg) characteristics, respectively, but the thermoplastics derived from AXBH had lower stretchability (maximum 160%) compared to the AXWB samples (maximum 300%). Higher araf/xylp values, and thus longer alkoxide side chains in AXWB-derived thermoplastics, explain the stretchability differences.
Collapse
Affiliation(s)
- Parveen Kumar Deralia
- Chemistry and Biochemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden.
| | - Amit Kumar Sonker
- Chemistry and Biochemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden
| | - Anja Lund
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden
| | - Anette Larsson
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden
| | - Anna Ström
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden
| | - Gunnar Westman
- Chemistry and Biochemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296, Gothenburg, Sweden.
| |
Collapse
|
4
|
Deralia PK, du Poset AM, Lund A, Larsson A, Ström A, Westman G. Hydrophobization of arabinoxylan with n-butyl glycidyl ether yields stretchable thermoplastic materials. Int J Biol Macromol 2021; 188:491-500. [PMID: 34389389 DOI: 10.1016/j.ijbiomac.2021.08.041] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/30/2021] [Revised: 07/14/2021] [Accepted: 08/05/2021] [Indexed: 12/24/2022]
Abstract
Hemicelluloses are regarded as one of the first candidates for the development of value-added materials due to their renewability, abundance, and functionality. However, because most hemicelluloses are brittle, they can only be processed as a solution and cannot be processed using industrial melt-based polymer processing techniques. In this study, arabinoxylan (AX) was hydrophobized by incorporating butyl glycidyl ether (BuGE) into the hydroxyl groups through the opening of the BuGE epoxide ring, yielding alkoxy alcohols with terminal ethers. The formed BuGE derivatives were melt processable and can be manufactured into stretchable thermoplastic films through compression molding, which has never been done before with hemicellulose modified in a single step. The structural and thermomechanical properties of the one-step synthesis approach were compared to those of a two-step synthesis with a pre-activation step to demonstrate its robustness. The strain at break for the one-step synthesized AX thermoplastic with 3 mol of BuGE is ≈200%. These findings suggest that thermoplastic polymers can be composited with hemicelluloses or that thermoplastic polymers made entirely of hemicelluloses can be designed as packaging and stretchable electronics supports.
Collapse
Affiliation(s)
- Parveen Kumar Deralia
- Chemistry and Biochemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296 Gothenburg, Sweden.
| | - Aline Maire du Poset
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE- Gothenburg, Sweden
| | - Anja Lund
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE- Gothenburg, Sweden
| | - Anette Larsson
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE- Gothenburg, Sweden
| | - Anna Ström
- Applied Chemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE- Gothenburg, Sweden
| | - Gunnar Westman
- Chemistry and Biochemistry, Department of Chemistry and Chemical Engineering, Chalmers University of Technology, Kemivägen 10, SE-41296 Gothenburg, Sweden.
| |
Collapse
|