Synergistic Covalent-and-Supramolecular Polymers with an Interwoven Topology

Highly robust supramolecular polymer networks crosslinked by a tiny amount of metallacycles

Supramolecular polymeric materials have exhibited attractive features such as self-healing, reversibility, and stimuli-responsiveness. However, on account of the weak bonding nature of most noncovalent interactions, it remains a great challenge to construct supramolecular polymeric materials with high robustness. Moreover, high usage of supramolecular units is usually necessary to promote the formation of robust supramolecular polymeric materials, which restrains their applications. Herein, we describe the construction of highly robust supramolecular polymer networks by using only a tiny amount of metallacycles as the supramolecular crosslinkers. A norbornene ring-opening metathesis copolymer with a 120° dipyridine ligand is prepared and self-assembled with a 60° or 120° Pt(II) acceptor to fabricate the metallacycle-crosslinked polymer networks. With only 0.28 mol% or less pendant dipyridine units to form the metallacycle crosslinkers, the mechanical properties of the polymers are significantly enhanced. The tensile strengths, Young's moduli, and toughness of the reinforced polymers reach up to more than 20 MPa, 600 MPa, and 150 MJ/m3, respectively. Controllable destruction and reconstruction of the metallacycle-crosslinked polymer networks are further demonstrated by the sequential addition of tetrabutylammonium bromide and silver triflate, indicative of good stimuli-responsiveness of the networks. These remarkable performances are attributed to the thermodynamically stable, but dynamic metallacycle-based supramolecular coordination complexes that offer strong linkages with good adaptive characteristics.

Hyperbranched Dynamic Crosslinking Networks Enable Degradable, Reconfigurable, and Multifunctional Epoxy Vitrimer

Degradation and reprocessing of thermoset polymers have long been intractable challenges to meet a sustainable future. Star strategies via dynamic cross-linking hydrogen bonds and/or covalent bonds can afford reprocessable thermosets, but often at the cost of properties or even their functions. Herein, a simple strategy coined as hyperbranched dynamic crosslinking networks (HDCNs) toward in-practice engineering a petroleum-based epoxy thermoset into degradable, reconfigurable, and multifunctional vitrimer is provided. The special characteristics of HDCNs involve spatially topological crosslinks for solvent adaption and multi-dynamic linkages for reversible behaviors. The resulting vitrimer displays mild room-temperature degradation to dimethylacetamide and can realize the cycling of carbon fiber and epoxy powder from composite. Besides, they have supra toughness and high flexural modulus, high transparency as well as fire-retardancy surpassing their original thermoset. Notably, it is noted in a chance-following that ethanol molecule can induce the reconstruction of vitrimer network by ester-exchange, converting a stiff vitrimer into elastomeric feature, and such material records an ultrahigh modulus (5.45 GPa) at -150 °C for their ultralow-temperature condition uses. This is shaping up to be a potentially sustainable advanced material to address the post-consumer thermoset waste, and also provide a newly crosslinked mode for the designs of high-performance polymer.

Mechanically Robust, Recyclable, and Self-Healing Polyimine Networks

To achieve energy saving and emission reduction goals, recyclable and healable thermoset materials are highly attractive. Polymer copolymerization has been proven to be a critical strategy for preparing high-performance polymeric materials. However, it remains a huge challenge to develop high-performance recyclable and healable thermoset materials. Here, polyimine dynamic networks based on two monomers with bulky pendant groups, which not only displayed mechanical properties higher than the strong and tough polymers, e.g., polycarbonate, but also excellent self-repairing capability and recyclability as thermosets are developed. Owing to the stability of conjugation effect by aromatic benzene rings, the final polyimine networks are far more stable than the reported counterparts, exhibiting excellent hydrolysis resistance under both alkaline condition and most organic solvents. These polyimine materials with conjugation structure can be completely depolymerized into monomers recovery in an acidic aqueous solution at ambient temperature. Resulting from the bulky pendant units, this method allows the exchange reactions of conjugation polyimine vitrimer easily within minutes for self-healing function. Moreover, the introduction of trifluoromethyl diphenoxybenzene backbones significantly increases tensile properties of polyimine materials. This work provides an effective strategy for fabricating high-performance polymer materials with multiple functions.

Durable Lithium Metal Anodes Enabled by Interfacial Layers Based on Mechanically Interlocked Networks Capable of Energy Dissipation

Solid electrolyte interphase (SEI) has received considerable attention due to its vital role in stabilizing Li anode. However, native and many artificial SEIs often suffer from cracking and fragmentation under dendrite impact or long-term repeated volume variation, causing capacity decay. Herein, a mechanically interlocked network (MIN) was innovatively designed as interfacial layer to protect Li anode by incorporating the unique energy dissipation capability, which helps Li anode survive repeated volume variation during long-term cycling. As a result, symmetric cell with MIN-coated Li anode (MIN@Li) exhibited prolonged cycling life of 1500 hours at 1 mA cm^-2 . The full cell using LFP cathode (13.5 mg cm^-2 ) cycled stably for 500 cycles with capacity retention over 88 % (1 C). Our results highlight a creative application of MIN in Li anode, and its unique energy dissipation capability promises future success in other battery fields suffering from repeated volume variations.

Supramolecular Crystal Networks Constructed from Cucurbit[8]uril with Two Naphthyl Groups

Naphthyl groups are widely used as building blocks for the self-assembly of supramolecular crystal networks. Host-guest complexation of cucurbit[8]uril (Q[8]) with two guests NapA and Nap1 in both aqueous solution and solid state has been fully investigated. Experimental data indicated that double guests resided within the cavity of Q[8], generating highly stable homoternary complexes NapA₂@Q[8] and Nap1₂@Q[8]. Meanwhile, the strong hydrogen-bonding and π···π interaction play critical roles in the formation of 1D supramolecular chain, as well as 2D and 3D networks in solid state.