Reactive B/Ti Nano-Multilayers with Superior Performance in Plasma Generation

In situ synthesis of [Cu(BODN)·5H2O]n@nano-Al composite energetic films with tunable properties in pyro-MEMS

Integrating energetic materials with microelectromechanical systems (MEMS) to achieve miniaturized integrated smart energetic microchips has broad application prospects in miniaturized aerospace systems and civil explosive systems. In this work, MEMS compatible [Cu(BODN)·5H2O]n arrays and [Cu(BODN)·5H2O]n@nano-Al composite energetic films were successfully fabricated on copper substrates by the in situ reaction method and drop-coating method. Single crystal X-ray diffraction, powder X-ray diffraction, scanning electron microscopy, infrared spectroscopy, differential thermal analyses, and pulsed laser ignition were employed to characterize the prepared samples. The results show that [Cu(BODN)·5H2O]n arrays formed by the coordination reaction between the Cu(OH)2 template and the BODN ligand exhibit a porous supramolecular structure with excellent thermal and energy properties. Their morphology and composition on a copper substrate can be effectively regulated by adjusting the reaction time and solution concentration. In addition, adjustable energetic properties of [Cu(BODN)·5H2O]n@nano-Al composite films can be achieved after the encapsulation of nano-Al. Their heat release, flame height and ignition duration can reach as much as 1987.5 J g-1, 13.2 mm, and 5900 μs, respectively, indicating that [Cu(BODN)·5H2O]n@nano-Al can be used as an excellent pyrotechnic agent in MEMS ignition chips. Overall, this work provides a reference for the integration and application of energetic materials in MEMS systems.

Exploring the Interfacial Reaction of Nano Al/CuO Energetic Films through Thermal Analysis and Ab Initio Molecular Dynamics Simulation

The effect of the interface layer on energy release in nanoenergetic composite films is important and challenging for the utilization of energy. Nano Al/CuO composite films with different modulation periods were prepared by magnetron sputtering and tested by differential scanning calorimetry. With the increase in the modulation period of the nano Al/CuO energetic composite films, the interface layer contained in the energetic composite film decreased meaningfully, increasing the total heat release meaningfully. Ab initio molecular dynamics (AIMD) simulation were carried out to study the preparation process changes and related properties of the nano Al/CuO energetic composite films under different configurations at 400 K. The results showed that the diffusion of oxygen atoms first occurred at the upper and lower interfaces of CuO and Al, forming AlO_x and Cu_xAl_yO_z. The two-modulation-period structure changed more obviously than the one-modulation-period structure, and the reaction was faster. The propagation rate and reaction duration of the front end of the diffusion reaction fronts at the upper and lower interfaces were different. The Helmholtz free energy loss of the nano Al/CuO composite films with a two-modulation-period configuration was large, and the number of interfacial layers had a great influence on the Helmholtz free energy, which was consistent with the results of the thermal analysis. Current molecular dynamics studies may provide new insights into the nature and characteristics of fast thermite reactions in atomic detail.

Nanomaterials by design: a review of nanoscale metallic multilayers

Nanoscale metallic multilayers have been shown to have a wide range of outstanding properties, which differ to a great extent from those observed in monolithic films. Their exceptional properties are mainly associated with the large number of interfaces and the nanoscale layer thicknesses. Many studies have investigated these materials focusing on magnetic, mechanical, optical, or radiation tolerance properties. Thus, this review provides a summary of the findings in each area, including a description of the general attributes, the adopted synthesis methods and most common characterization techniques used. This information is followed by a compendium of the material properties and a brief discussion of related experimental data, as well as existing and promising applications. Other phenomena of interest, including thermal stability studies, self-propagating reactions and the progression from nano multilayers to amorphous and/or crystalline alloys, are also covered. In general, this review highlights the use of nano multilayer architectures as viable routes to overcome the challenges of designing and implementing new engineering materials at the nanoscale.

Energetic Al/Ni Superlattice as a Micro-Plasma Generator with Superb Performances

In this study, energetic Al/Ni superlattice was deposited by magnetron sputtering. A micro-plasma generator was fabricated using the energetic Al/Ni superlattice. The cross-sectional micro-structure of the energetic Al/Ni superlattice was scanned by transmission electron microscopy. Results show that the superlattice is composed of Al layer and Ni layers, and its periodic structure is clearly visible. Moreover, the bilayer thickness is about 25 nm, which consists of about 15 nm Al layer and 10 nm Ni layer. The micro initiator was stimulated using a 0.22 μF capacitor charged at 2900-4100 V. The electrical behaviors were investigated by testing the current-voltage waveform, and the plasma generation was explored by ultra-high-speed camera and photodiode. The integrated micro generator exhibited remarkable electrical exploding phenomenon, leading to plasma generations at a small timescale. The plasma outputs reflected by flyer velocities were superior to that with a much thicker bilayer of 500 nm Al/Ni multilayer. The higher flyer velocity combined with Gurney energy model confirmed the chemical reaction of the Al/Ni superlattice structure contributed to plasma production in comparison with the Al/Ni multilayers. Overall, the energetic Al/Ni superlattice was expected to pave a promising avenue to improve the initiator efficiency at a lower energy investment.