Formation of heterogeneous polymer films via simultaneous or sequential depositions of soluble and insoluble monomers onto ionic liquids

Vapor Deposition of Silicon-Containing Microstructured Polymer Films onto Silicone Oil Substrates

In this study, a silicon-containing cross-linked polymer, poly(1,3,5,7-tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane-co-ethylene glycol diacrylate) (p(V4D4-co-EGDA)), was deposited onto high-viscosity silicone oil using initiated chemical vapor deposition (iCVD). The ratio of the feed flow rate of V4D4 to EGDA was systematically studied, and the chemical composition and morphology of the top and bottom surfaces of the films were analyzed. The films were microstructured, and the porosity and thickness of the films increased with increasing V4D4 content. The top of the film was composed of densely packed and loosely packed microstructured regions. X-ray photoelectron spectroscopy on the top and bottom surfaces of the films showed a heterogeneous chemical composition along the thickness of the film, with higher silicon content on the top surface compared to that on the bottom surface. To the best of our knowledge, this is the first study of iCVD deposition of a silicon-containing polymer film onto silicone oil. The results of this study can be used for the synthesis of polymer precursor films for the fabrication, via pyrolysis, of silicon-based inorganic membranes for use in hydrogen production using silicone oil to prevent infiltration of monomer into the underneath membrane support structure during vapor deposition.

Fabricating Polymer Canopies onto Structured Surfaces Using Liquid Scaffolds

In this work, we study the use of initiated chemical vapor deposition in conjunction with liquid scaffolds to deposit polymer canopies onto structured surfaces. Liquid is applied to micropillar and microstructure surfaces to act as a scaffolding template such that the deposited polymer films take the shape of the liquid surface. Two methods for directing the location of the scaffolding liquid were examined. In the first method, high surface tension liquids rest in a Cassie-Baxter state over the structured surfaces, allowing for control over the canopy location and size by varying the position and volume of the liquid. In the second method, the structured surfaces are inverted onto a thin layer of low surface tension liquid, allowing the coverage and height of the canopy to be controlled by varying the area and thickness of the liquid layer. Although the canopies demonstrated in this study were fabricated using initiated chemical vapor deposition, the generality of our scaffolding method can easily be translated to other vapor deposition processes.

Microstructured Films Formed on Liquid Substrates via Initiated Chemical Vapor Deposition of Cross-Linked Polymers

We studied the formation of microstructured films at liquid surfaces via vapor phase polymerization of cross-linked polymers. The films were composed of micron-sized coral-like structures that originate at the liquid-vapor interface and extend vertically. The growth mechanism of the microstructures was determined to be simultaneous aggregation of the polymer on the liquid surface and wetting of the liquid on the growing aggregates. We demonstrated that we can increase the height of the microstructures and increase the surface roughness of the films by either decreasing the liquid viscosity or decreasing the polymer deposition rate. Our vapor phase method can be extended to synthesize functional, free-standing copolymer microstructured thin films for potential applications in tissue engineering, electrolyte membranes, and separations.