Spontaneous polymerization at the air-water interface: a Brewster angle microscopy study

Interfacial Synthesis of an Ultrathin Two-Dimensional Polymer Film via [2 + 2] Photocycloaddition

A carbon-carbon-linked, ultrathin, two-dimensional (2D) polymer film was prepared at the air/water interface through photochemically triggered [2 + 2] cycloaddition. The preorganization of the monomers on the water surface and the subsequent photo-polymerization led to the successful preparation of the ultrathin 2D polymer film. The obtained film is continuous, free standing, and has a large area (over 50 μm²). Transmission electron microscopy (TEM) and atomic force microscopy (AFM) give clear evidence of the ultrathin film morphology. Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) indicate successful photo-induced [2 + 2] polymerization.

2D Photopolymerization of Liquid Crystalline Langmuir Monolayers: In Situ Observation by Reflected Polarizing Microscopy

Photopolymerization of Langmuir monolayers composed of bifunctional acrylic liquid crystalline (LC) compounds was observed in situ by polarizing optical microscopy. In a dark state, monolayers of the LC compounds formed at an air-water or liquid-liquid interface exhibited liquid-like fluidity and in-plane optical anisotropy because of the coherent molecular tilt from the surface normal. Irradiated by UV light, the in-plane anisotropy and the liquid fluidity gradually disappeared with time, indicating the formation of the polymerized monolayers. Because the constituent molecules possess polymerizable acryloyl groups, under UV light, they are combined by acrylic polymer chains grown on the interface, which decreases the intermolecular distance and disturbs the coherent molecular tilt, resulting in the evanescence of the in-plane optical anisotropy and the fluidity. In contrast to the classical model of radical polymerization, the time taken for the monolayers to be photopolymerized was inversely proportional to the UV intensity, which is ascribed to the ideal two dimensionality of the reaction field. Because the polymerization degree is quantitatively estimated from the in-plane optical anisotropy of the LC monolayers, the process is traced, from moment to moment, by in situ microscopy observation.

Synthesis at the air-water interface of a two-dimensional semi-interpenetrating network based on poly(dimethylsiloxane) and cellulose acetate butyrate

The UV-induced cross-linking of methacryloxypropyl-terminated poly(dimethylsiloxane) oligomers was studied at the air-water interface either in pure PDMS Langmuir monolayers or in mixed films containing cellulose acetate butyrate. Surface pressure-area isotherms, area measurement at constant surface pressure, Brewster angle microscopy observations, and infrared-visible sum frequency generation (SFG) spectroscopy were combined to follow the evolution of the monolayers upon in situ UV photoirradiation. For both systems, the mean area per repeat unit decreases with irradiation time reflecting the monolayer contraction. In addition, SFG measurements evidence the conversion of the methacrylate groups into unconjugated poly(methacrylate) ones. These results demonstrate PDMS cross-linking, leading to the formation of either a single PDMS network or a PDMS network entrapped in a CAB matrix. The network formation is accompanied by morphology changes as shown by atomic force microscopy on the transferred monolayer. Indeed, filamentous structures appear on both pure and mixed preirradiated monolayers.