Precipitation of nanocrystalline CeO2 using triethanolamine

Synthesis and Characterization of Fluorite-Type La2Ce2O7 Plasma Sprayable Powder for TBCs Application

This work focuses on the fabrication of lanthanum cerate (La₂Ce₂O₇, LC) powders via two chemical routes: modified Pechini sol-gel method and solid-state synthesis. The synthesized LC powders were heat treated in the temperature range of 1000–1400 °C for 6 h and investigated as a material for thermal barrier coating (TBC) applications. For this purpose, the powder morphology, chemical composition, crystal structure and thermal stability were studied. Scanning electron microscopy (SEM) of the synthesized powders revealed an agglomerated structure consisting of fine and uniformly distributed grains. Energy-dispersive X-ray spectroscopy (EDXS) indicated that the chemical compositions of the LC powders were similar to the stoichiometric ratio of La₂Ce₂O₇. A cubic fluorite structure was observed by X-ray diffraction analysis (XRD) after calcining the LC powder prepared by solid-state synthesis at 1300 °C. In contrast, there was always a fluorite structure in the LC powder synthesized by the Pechini sol-gel method after heat treatment over the entire temperature range. The thermal behavior of the LC powders was analyzed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TG) in the temperature range of 25–1300 °C. Neither an obvious mass change nor a visible energy change was observed within the tested temperature range, indicating high phase stability of the LC powder and its suitability for TBC applications. Spheroidization on the prepared LC powders was also investigated, revealing that powder size and morphology had a significant impact on the spheroidization efficiency.

Tuning Properties of Cerium Dioxide Nanoparticles by Surface Modification with Catecholate-type of Ligands

Cerium dioxide (CeO₂) finds applications in areas such as corrosion protection, solar cells, or catalysis, finding increasing applications in biomedicine. This work reports on surface-modified CeO₂ particles in order to tune their applicability in the biomedical field. Stable aqueous CeO₂ sol, consisting of 3-4 nm in size crystallites, was synthesized using forced hydrolysis. The coordination of catecholate-type of ligands (catechol, caffeic acid, tiron, and dopamine) to the surface-Ce atoms is followed with the appearance of absorption in the visible spectral range as a consequence of interfacial charge-transfer complex formation. The spectroscopic observations are complemented with the density functional theory calculations using a cluster model. The synthesized samples were characterized by X-ray diffraction analysis, transmission electron microscopy, and nitrogen adsorption-desorption isotherms. The ζ-potential measurements indicated that the stability of CeO₂ sol is preserved upon surface modification. The pristine CeO₂ nanoparticles (NPs) are nontoxic against pre-osteoblast cells in the entire studied concentration range (up to 1.5 mM). Hybrid CeO₂ NPs, capped with dopamine or caffeic acid, display toxic behavior for concentrations ≥0.17 and 1.5 mM, respectively. On the other hand, surface-modified CeO₂ NPs with catechol and tiron promote the proliferation of pre-osteoblast cells.

Bi doped CeO2 oxide supported gold nanoparticle catalysts for the aerobic oxidation of alcohols

Gold nanoparticles supported on Bi–CeO₂ with four different bismuth loadings (2 to 8 mol%) were prepared to determine the role of oxide vacancies in doped ceria in the benzyl alcohol oxidation reaction.