Sorption, solubility and cytotoxicity of novel antibacterial nanofilled dental adhesive resins

Nanoparticle Augmentation of Adhesive Systems: Impact on Tensile Strength in Fiberglass Post Placement within Root Dentin

BACKGROUND Modification of the glass fiber post (GFP) with titanium dioxide or silver particles can improve the durability and reliability of dental treatments for ensuring long-term success. This research assessed the tensile bond strength (TBS) of an adhesive system used for cementing GFPs into root dentin following the incorporation of nanoparticles of titanium dioxide (NTiO2) and silver (NAg). MATERIAL AND METHODS Sixty human maxillary canines were prepared to create a 10-mm intra-radicular space for post placement from the cementoenamel junction. The specimens were randomly allocated into 2 groups (a non-thermocycling group and a thermocycling group). Each group was divided into 3 subgroups (10 samples each) according to the adhesive system used (adhesive system devoid of any addition, adhesive system including 1% NAg, and adhesive system infused with 1% NTiO2). TBS tests were conducted and recorded in MPa using a Universal Testing Machine, with an axial load applied at a rate of 0.5 mm/min until failure. The TBS for both groups (non-thermocycling and thermocycling) was measured in megapascals (MPa), and the failure type was recorded. The data were statistically analyzed using one-way analysis of variance (ANOVA) and Tukey's test with P.

Mechanical and antibacterial properties of an experimental flowable composite containing Nb2O5 and NF_TiO2 nanoparticles

This study developed an experimental flowable composite incorporated with niobium pentoxide (Nb2O5) combined or not with titanium dioxide co-doped with fluorine and nitrogen (NF_TiO2) and evaluated the mechanical and antibacterial properties. The experimental flowable composite (TEGDMA + BisGMA 1:1 + 60%wt - inorganic filler - borosilicate 0.7 μm) was formulated according to the type and concentration of Nb2O5 and NF_TiO2 (0.5, 1, 1.5 and 2 wt%) or NF_TiO2 + Nb2O5 (0.25, 0.5, 0.75 and 1 wt% - 1:1). The control groups were formed by the experimental composite without the incorporation of Nb2O5 and/or NF_TiO2 (GC-E) and by a commercial flowable composite (GC). The characterization of the surface of the composite and its particles was carried out using scanning electron microscopy (SEM) and energy dispersive x-rays (EDX). Specimens were manufactured and subjected to mechanical tests of flexural strength (FS) (n = 12), flexural modulus (FM) (n = 12), roughness (Ra) (n = 10), microhardness (n = 10), and contact angle (n = 10); and, to evaluate the antibacterial activity, they were submitted to tests of biofilm formation against S. mutans (CFU/mL) (n = 5), biofilm biomass by dry weight (n = 5) and confocal laser microscopy (%LIVE/DEAD) (n = 5). Data were submitted to one-way ANOVA and Tukey's post-hoc and, those that were not homoscedastic, but with normality, were submitted to Welch's ANOVA and Games-Howell's post-hoc. Dunnet's test was used to compare the controls with the other experimental groups (α = 5). The Nb2O5 particles had an average size of 32.4 μm and the nanoparticles (NPs) of NF_TiO2, 10 nm. EDX analysis identified isolated peaks of N, F, Ti, and Nb confirming the presence of these particles in the resin matrix. The 1.5% NF_TiO2 group had a higher FS and FM than the controls (p < 0.05). GC showed higher microhardness between groups (p < 0.05). There was no difference between the experimental groups regarding contact angle and roughness (p > 0.05), except for GC, which had the highest Ra values and the lowest contact angle between groups (p < 0.05). Composites containing 0.5%, 1%, 1.5%, and 2% Nb2O5, 1%, 1.5%, and 2% NF_TiO2 and 2% Nb2O5 + NF_TiO2 showed lower biofilm formation (p < 0.05), lower total biofilm biomass (p < 0.05), and a higher percentage of dead cells (44%, 52%, 52%, 79%, 42% 43%, 62%, 65%, respectively) than GC and GC-E (5% and 1%, respectively). It is concluded that the incorporation of 1.5% NF_TiO2 promoted a greater FS and FM among the experimental composites and that the addition of Nb2O5 particles (0.5%, 1%, 1.5%, and 2%), NF_TiO2 (1%, 1.5% and 2%) and the combination Nb2O5 + NF_TiO2 (2%) showed significant antibacterial effects.

Shear Bond Strength and Color Stability of Novel Antibacterial Nanofilled Dental Adhesive Resins

Experimental adhesives containing co-doped metaloxide nanoparticles were demonstrated to display strong and long-term antibacterial properties against Streptococcus mutans biofilms. The present study represents an effort to characterize the shear-bond strength (SBS) and color stability (CS) of these novel biomaterials. Experimental adhesives were obtained by dispersing nitrogen and fluorine co-doped titanium dioxide nanoparticles (NF_TiO2, 10%, 20% or 30%, v/v%) into OptiBond Solo Plus (OPTB). Dentin surfaces were wet-polished (600-Grit). Specimens (n = 5/group) of Tetric EvoCeram were fabricated and bonded using either OPTB or experimental (OPTB + NF_TiO2) adhesives. Specimens were stored in water (37 °C) for twenty-four hours (T1), three months (T2), and six months (T3). At T1, T2, or T3, specimens were removed from water storage and were tested for SBS. Disc-shaped specimens (n = 10/group; d = 6.0 mm, t = 0.5 mm) of adhesives investigated were fabricated and subjected to thermocycling (10,000 cycles, 5−55 °C, 15 s dwell time). Specimens’ colors were determined with a VITA Easyshade® V spectrophotometer (after every 1000 cycles). SBS data was analyzed using two-way ANOVA and post-hoc Tukey tests, while CS data was analyzed using one-way ANOVA and post-hoc Tukey tests (α = 0.05). Mean values of SBS ranged from 16.39 ± 4.20 MPa (OPTB + 30%NF_TiO2) to 19.11 ± 1.11 MPa (OPTB), from 12.99 ± 2.53 MPa (OPTB + 30% NF_TiO2) to 14.87 ± 2.02 (OPTB) and from 11.37 ± 1.89 (OPTB + 20% NF_TiO2) to 14.19 ± 2.24 (OPTB) after twenty-four hours, three months, and six months of water storage, respectively. Experimental materials had SBS values that were comparable (p > 0.05) to those from OPTB independently of nanoparticle concentration or time-point considered. Experimental materials with higher NF_TiO2 concentrations had less intense color variations and were more color stable than OPTB even after 10,000 thermocycles. In combination, the results reported have demonstrated that experimental adhesives can establish strong and durable bonds to human dentin while displaying colors that are more stable, thereby suggesting that the antibacterial nanotechnology investigated can withstand the harsh conditions within the oral cavity without compromising the esthetic component of dental restorations.

Characterization of Experimental Nanoparticulated Dental Adhesive Resins with Long-Term Antibacterial Properties

Experimental adhesives with functional nitrogen-doped titanium dioxide nanoparticles (N_TiO₂) have been shown to display improved properties. However, these materials have not been characterized regarding their degree of conversion (DC), biaxial flexure strength (BFS), surface roughness (SR), elastic modulus (EM), and long-term antibacterial functionalities. Experimental adhesives were synthesized by dispersing N_TiO₂ (10%, 20%, or 30%, v/v%) into OptiBond Solo Plus (OPTB, Kerr Corp., USA). Unpolymerized adhesives (volume = 50 μL/drop, n = 3/group) were individually placed onto a heated (37 °C) attenuated total reflectance (ATR) monolithic diamond crystal (Golden Gate, Specac). The spectra of composites were obtained with a Fourier-transform infrared (FTIR) spectrometer (Nicolet IS50; 500-4500 cm^-1; resolution = 4 cm^-1, 10 internal scans/spectrum) before and after polymerization. Disk-shaped specimens (diameter = 6.0 mm, thickness = 0.5 mm) for BFS (n = 12/group), SR and EM (n = 3/group), and for antibacterial testing (n = 18/group/time-point) were fabricated and photopolymerized (1 min each; 385-515 nm, 1000 mW/cm²; VALO). DC values (%) were calculated from pre- and post-polymerization spectra using the two-frequency method and tangent-baseline technique. BFS was assessed using a universal testing machine (Instron 68TM-5, crosshead speed = 1.27 mm/min, 25 °C). SR and EM were investigated using an atomic force microscope (Multimode 8) with aluminum-coated silicon probes (8 nm pyramidal tip, spring constant 40 N/m, Bruker). Antibacterial testing was performed by growing Streptococcus mutans biofilms (UA159-ldh, 37 °C, microaerophilic) on the surfaces of specimens for 24 h and then measuring the relative luminescence units (RLU) with a Biotek Synergy HT multi-well plate reader. Results demonstrate that experimental materials containing 10%, 20%, and 30% of N_TiO₂ displayed higher levels of DC, had better mechanical properties, and were able to exert strong and durable antibacterial properties without visible light irradiation and after extended periods of simulated shelf-life and aging in PBS. The reported experimental materials are expected to increase the service lives of polymer-based bonded restorations by decreasing the incidence of secondary caries.

Medical and Dental Applications of Titania Nanoparticles: An Overview

Currently, titanium oxide (TiO₂) nanoparticles are successfully employed in human food, drugs, cosmetics, advanced medicine, and dentistry because of their non-cytotoxic, non-allergic, and bio-compatible nature when used in direct close contact with the human body. These NPs are the most versatile oxides as a result of their acceptable chemical stability, lower cost, strong oxidation properties, high refractive index, and enhanced aesthetics. These NPs are fabricated by conventional (physical and chemical) methods and the latest biological methods (biological, green, and biological derivatives), with their advantages and disadvantages in this epoch. The significance of TiO₂ NPs as a medical material includes drug delivery release, cancer therapy, orthopedic implants, biosensors, instruments, and devices, whereas their significance as a dental biomaterial involves dentifrices, oral antibacterial disinfectants, whitening agents, and adhesives. In addition, TiO₂ NPs play an important role in orthodontics (wires and brackets), endodontics (sealers and obturating materials), maxillofacial surgeries (implants and bone plates), prosthodontics (veneers, crowns, bridges, and acrylic resin dentures), and restorative dentistry (GIC and composites).

Nitrogen doped titanium dioxide as an aesthetic antimicrobial filler in dental polymers

OBJECTIVE

To develop an aesthetic resin composite using a nitrogen-doped titanium dioxide (NTiO₂) filler that possesses antimicrobial properties against cariogenic bacteria.

METHODS

N-TiO₂ powder was manufactured by calcining commercial TiO₂ with urea. Free radical release from the N-TiO₂ powder under visible light irradiation was analysed using UV-Vis spectrophotometry. The N-TiO₂ powder was incorporated into a dental resin and the photocatalytic activity assessed using a dye under both visible light and dark conditions. Using XTT assay to measure the cellular metabolic activity, the antibacterial properties of the N-TiO₂ /resin composite discs were tested using Streptococcus mutans.

RESULTS

Doping nitrogen of TiO₂ resulted in a band gap shift towards the visible light spectrum, which enabled the powder to release reactive oxygen species when exposed to visible light. When incorporated into a dental resin, the N-TiO₂/resin composite still demonstrated sustained release of reactive oxygen species, maintaining its photocatalytic activity and showing an antibacterial effect towards Streptococcus mutans under visible light conditions.

SIGNIFICANCE

N-TiO₂ filled resin composite shows great promise as a potential aesthetic resin based adhesive for orthodontic bonding.

Influence of TiO2 and ZrO2 Nanoparticles on Adhesive Bond Strength and Viscosity of Dentin Polymer: A Physical and Chemical Evaluation

The present study aimed to formulate an experimental adhesive (EA) and reinforce it with 5 wt.% titanium dioxide (TiO₂) or zirconium oxide (ZrO₂) to yield 5% TiO₂ and 5% ZrO₂ adhesives, respectively, and then analyze the impact of this reinforcement on various mechanical properties of the adhesives. The EA contained a blend of monomers such as bisphenol A glycol dimethacrylate (BisGMA), triethylene glycol dimethacrylate (TEGDMA), 2-hydroxyethyl methacrylate (HEMA), and ethyl 4-dimethylamino benzoate and camphorquinone. The EA included ethyl 4-dimethylamino benzoate and camphorquinone photo-initiators, and diphenyliodonium hexafluorophosphate (DPIHP) was also included to act as an electron initiator. The TiO₂ and ZrO₂ nanoparticles were incorporated into the EA post-synthesis. To characterize the filler nanoparticles, scanning electron microscopy (SEM) and line-energy dispersive X-ray (EDX) spectroscopy were performed. The adhesives were characterized by analyzing their rheological properties, shear-bond strength (SBS), and interfacial failure types. Further, the resin-dentin interface was also analyzed via SEM. The TiO₂ nanoparticles were spherically shaped on the SEM micrographs, while the ZrO₂ nanoparticles were seen as non-uniformly shaped agglomerates. The EDX mapping demonstrated the presence of Ti and oxygen for TiO₂ and Zr and oxygen for the ZrO₂ nanoparticles. Both 5% TiO₂ and 5% ZrO₂ adhesives revealed decreased viscosity as compared with the EA. The 5% TiO₂ adhesive demonstrated higher SBS values for both non-thermocycled (NTC) and thermocycled samples (NTC: 25.35 ± 1.53, TC: 23.89 ± 1.95 MPa), followed by the 5% ZrO₂ adhesive group (NTC: 23.10 ± 2.22, TC: 20.72 ± 1.32 MPa). The bulk of the failures (>70%) were of adhesive type in all groups. The SEM analysis of the resin-dentin interface revealed the development of a hybrid layer and resin tags (of variable depth) for the EA and 5% TiO₂ groups. However, for the 5% ZrO₂ group, the hybrid layer and resin tag establishment appeared compromised. Reinforcement of the EA with TiO₂ or ZrO₂ caused an increase in the adhesive's SBS (with the 5% TiO₂ group demonstrating the highest values) in comparison with the EA (without nanoparticles). However, both nanoparticle-containing adhesives revealed decreased viscosity compared with the EA (without nanoparticles). Further studies investigating the impact of diverse filler concentrations on the properties of adhesives are suggested.

Advances of Anti-Caries Nanomaterials

Caries is the most common and extensive oral chronic disease. Due to the lack of anti-caries properties, traditional caries filling materials can easily cause secondary caries and lead to treatment failure. Nanomaterials can interfere with the bacteria metabolism, inhibit the formation of biofilm, reduce demineralization, and promote remineralization, which is expected to be an effective strategy for caries management. The nanotechnology in anti-caries materials, especially nano-adhesive and nano-composite resin, has developed fast in recent years. In this review, the antibacterial nanomaterials, remineralization nanomaterials, and nano-drug delivery systems are reviewed. We are aimed to provide a theoretical basis for the future development of anti-caries nanomaterials.