Immobilization of nanofibrous metal oxides on microfibers: A macrostructured catalyst system functionalized with nanoscale fibrous metal oxides

Facile synthesis of nanostructured perovskites by precursor accumulation on nanocarbons

Perovskite-type oxides have impacted various research fields, including materials and energy science. Despite their vast potential in various applications, general and simple synthesis methods for nano-perovskites remain limited. Herein, various nano-perovskites were synthesized by a facile approach involving the use of nanocarbons. The calcination of the nanocarbon deposited with metal salts yielded nano-perovskites, emulating the morphology of nanocarbons. The accumulation of precursors (i.e., metal salts) on the surface of the nanocarbon during the evaporation of the solvent is the key step in which the precursors are homogeneously mixed prior to calcination. The homogeneity of the precursors facilitated low-temperature calcination that resulted in the formation of nano-perovskites. Various nano-perovskites, including LaMnO₃, LaCoO₃, LaFeO₃, LaNiO₃, LaAlO₃, LaGaO₃, CaMnO₃, BaMnO₃, SrMnO₃, La_0.7Sr_0.3FeO₃, La₂CuO₄, and Ca₂Fe₂O₅, were successfully synthesized, demonstrating the simplicity and novelty of the method for the general synthesis of nano-perovskites.

Precursor accumulation on nanocarbons for the synthesis of LaCoO3 nanoparticles as electrocatalysts for oxygen evolution reaction

Oxygen evolution reaction (OER) is a key step in energy storage devices. Lanthanum cobaltite (LaCoO₃) perovskite is an active catalyst for OER in alkaline solutions, and it is expected to be a low-cost alternative to the state-of-the-art catalysts (IrO₂ and RuO₂) because transition metals are abundant and inexpensive. For efficient catalysis with LaCoO₃, nanosized LaCoO₃ with a high surface area is desirable for increasing the number of catalytically active sites. In this study, we developed a novel synthetic route for LaCoO₃ nanoparticles by accumulating the precursor molecules over nanocarbons. This precursor accumulation (PA) method for LaCoO₃ nanoparticle synthesis is simple and involves the following steps: (1) a commercially available carbon powder is soaked in a solution of the nitrate salts of lanthanum and cobalt and (2) the sample is dried and calcined in air. The LaCoO₃ nanoparticles prepared by the PA method have a high specific surface area (12 m² g⁻¹), comparable to that of conventional LaCoO₃ nanoparticles. The morphology of the LaCoO₃ nanoparticles is affected by the nanocarbon type, and LaCoO₃ nanoparticles with diameters of less than 100 nm were obtained when carbon black (Ketjen black) was used as the support. Further, the sulfur impurities in nanocarbons significantly influence the formation of the perovskite structure. The prepared LaCoO₃ nanoparticles show excellent OER activity owing to their high surface area and perovskite structure. The Tafel slope of these LaCoO₃ nanoparticles is as low as that of the previously reported active LaCoO₃ catalyst. The results strongly suggest that the PA method provides nanosized LaCoO₃ without requiring the precise control of chemical reactions, harsh conditions, and/or special apparatus, indicating that it is promising for producing active OER catalysts at a large scale.

A simple synthetic process for LaCoO₃ nanoparticles based on the accumulation of precursors on nanocarbon supports was presented. The LaCoO₃ nanoparticles showed excellent OER activity owing to their high surface area and perovskite structure.

Coating of Silica Nanolayers on Carbon Nanofibers via the Precursor Accumulation Method

Surface modification of nanocarbons, for example, by coating with oxide nanolayers, is a research topic of significant interest because of the drastic changes in the physicochemical properties of the modified nanocarbons. One simple method of creating these oxide nanolayer coatings on nanocarbons is the precursor accumulation (PA) technique, which entails the following: (1) a precursor solution is added dropwise onto nanocarbon powder; (2) the solvent is dried, leaving the accumulated precursor on the nanocarbon surface; and (3) hydrolysis or decomposition of the precursor in air leads to the formation of oxide nanolayers on the nanocarbons. In this study, tetraethoxysilane (TEOS) was used as a precursor for coating silica nanolayers onto carbon nanofibers (CNFs). TEOS is so stable that it hardly undergoes hydrolysis on the surface of pristine CNFs. By treating CNFs with H₂SO₄/HNO₃, acidic functional groups were introduced onto the CNF surfaces. Silica nanolayers were successfully synthesized on these acid-treated CNFs via PA coating because the acidic functional groups catalyzed the hydrolysis of TEOS accumulated on the CNF surfaces. Scanning transmission electron microscopy indicated that the thickness of silica layer is approximately several nanometers. Pore size distribution analysis for the silica nanolayer suggested the presence of nanopores with 3-5 nm. The TEOS molecules could have accessed the functional groups through the nanopore; therefore, the number of silica nanolayers formed increased with the number of PA coatings. Finally, we compared the PA coating with conventional sol-gel and atomic layer deposition techniques.