Heterostructural Sn/SnO2 microcube powders coated by a nitrogen-doped carbon layer as good-performance anode materials for lithium ion batteries

The nitrogen-doped carbon (NC) coating encapsulating heterostructural Sn/SnO₂ microcube powders (Sn/SnO₂@NC) are successfully fabricated through hydrothermal, polymerization of hydrogel, and carbonization processes, in which the SnO precursor powders exhibit regular microcube structure and uniform size distribution in the presence of optimized N₂H₄·H₂O (3.0 mL of 1.0 mol/L). Interestingly, the precursor powders are easily subjected to a disproportionated reaction to yield the desirable heterostructural Sn/SnO₂@NC microcube powders after being calcined at 600 °C in N₂ atmosphere in the presence of home-made hydrogel. The coin cells assembled with the Sn/SnO₂@NC electrode present a high initial discharge specific capacity (1058 mAh g^-1 at 100 mA g^-1), improved rate capability (an excellent D_Li+ value of 2.82 × 10^-15 cm² s^-1) and enhanced cycling stability (a reversible discharge specific capacity of 486.5 mAh g^-1 after 100 cycles at 100 mA g^-1). The enhanced electrochemical performance can be partly ascribed to the heterostructural microcube that can accelerate the transfer rate of lithium ions by shortening the transmission paths, and be partly to the NC coating that can accommodate the volume effect and contribute to partial lithium storage capacity. Therefore, the strategy may be able to extend the fabrication of Sn/SnO₂ heterostructural microcube powders and further application as promising anode materials in lithium ion batteries.

Structural characterization of SnO nanoparticles synthesized by the hydrothermal and microwave routes

SnO particles were synthesized by an alkali-assisted hydrothermal and microwave methods. The aqueous-based reactions were carried out at pH ~ 8, under inert atmosphere (Ar). The reactions were taken under different times, and a full XRD structural analysis was made to evaluate the conversion from the Sn₆O₄(OH)₄ intermediate to SnO particles. Williamson-Hall analysis showed that the size and strain of the SnO particles were time and route treatment dependent. Microwave heating yielded a single tetragonal SnO phase after 1 h of thermal treatment, and TEM images revealed spherical-shaped SnO nanoparticles with an average size of 9(1) nm. While by the hydrothermal treatment single SnO phase was obtained only after 4 hours, yielding non-uniform and elongated particles with sub-micrometric size. A dissolution-recrystallization process was taken into account as the mechanism for SnO particles formation, in which hydroxylated complexes, Sn₂(OH)₆⁻², then condense to form the oxide. The time-shorting reaction provided by the microwave-assisted synthesis may be attributed to better heat distribution.

Reproducible shape control of single-crystal SnO micro particles

A straightforward method for synthesizing well-defined four-petal starfish-like single-crystalline SnO micro particles in an organic medium with various oleylamine concentrations was examined.

Morphologically robust NiFe2O4 nanofibers as high capacity Li-ion battery anode material

In this work, the electrochemical performance of NiFe2O4 nanofibers synthesized by an electrospinning approach have been discussed in detail. Lithium storage properties of nanofibers are evaluated and compared with NiFe2O4 nanoparticles by galvanostatic cycling and cyclic voltammetry studies, both in half-cell configurations. Nanofibers exhibit a higher charge-storage capacity of 1000 mAh g(-1) even after 100 cycles with high Coulmbic efficiency of 100% between 10 and 100 cycles. Ex situ microscopy studies confirmed that cycled nanofiber electrodes maintained the morphology and remained intact even after 100 charge-discharge cycles. The NiFe2O4 nanofiber electrode does not experience any structural stress and eventual pulverisation during lithium cycling and hence provides an efficient electron conducting pathway. The excellent electrochemical performance of NiFe2O4 nanofibers is due to the unique porous morphology of continuous nanofibers.

Template-free synthesis of amorphous double-shelled zinc-cobalt citrate hollow microspheres and their transformation to crystalline ZnCo2O4 microspheres

A novel and facile approach was developed for the fabrication of amorphous double-shelled zinc-cobalt citrate hollow microspheres and crystalline double-shelled ZnCo2O4 hollow microspheres. In this approach, amorphous double-shelled zinc-cobalt citrate hollow microspheres were prepared through a simple route and with an aging process at 70 °C. The combining inward and outward Ostwald ripening processes are adopted to account for the formation of these double-shelled architectures. The double-shelled ZnCo2O4 hollow microspheres can be prepared via the perfect morphology inheritance of the double-shelled zinc-cobalt citrate hollow microspheres, by calcination at 500 °C for 2 h. The resultant double-shelled ZnCo2O4 hollow microspheres manifest a large reversible capacity, superior cycling stability, and good rate capability.

Li-cycling properties of molten salt method prepared nano/submicrometer and micrometer-sized CuO for lithium batteries

We report the synthesis of CuO material by molten salt method at a temperature range, 280 to 950 °C for 3 h in air. This report includes studies on the effect of morphology, crystal structure and electrochemical properties of CuO prepared at different temperatures. Obtained CuO was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) surface area methods. Samples prepared at ≥410 °C showed a single-phase material with a lattice parameter value of a = 4.69 Å, b = 3.43 Å, c = 5.13 Å and surface area values are in the range 1.0-17.0 m(2) g(-1). Electrochemical properties were evaluated via cyclic voltammetry (CV) and galvanostatic cycling studies. CV studies showed a minor difference in the peak potentials depending on preparation temperature and all compounds exhibit a main anodic peak at ~2.45 V and cathodic peaks at ~0.85 V and ~1.25 V vs Li. CuO prepared at 750 °C showed high and stable capacity of ~620 mA h g(-1) at the end of 40th cycle.