Ce4Ag3Ge4O(0.5)--chains of oxygen-centered [OCe2Ce(2/2)] tetrahedra embedded in a [CeAg3Ge4] intermetallic matrix

The quaternary arsenide oxides Ce9Au5–x As8O6 and Pr9Au5–x As8O6

The quaternary gold arsenide oxides Ce9Au5−x As8O6 and Pr9Au5−x As8O6 were synthesized from the rare earth elements (RE), rare earth oxides, arsenic and gold powder at maximum annealing temperatures of 1173 K. The structures were refined from single crystal X-ray diffractometer data: Pnnm, a=1321.64(6) pm, b=4073.0(3), c=423.96(2), wR2=0.0842, 3106 F 2 values, 160 variables for Ce9Au4.91(4)As8O6 and Pnnm, a=1315.01(4), b=4052.87(8), c=420.68(1) pm, wR2=0.0865, 5313 F 2 values, 160 variables for Pr9Au4.75(1)As8O6. They represent a new structure type and show a further extension of pnictide oxide crystal chemistry. A complex polyanionic gold arsenide network [Au5As8]15− (with some disorder in the gold substructure) is charge compensated with polycationic strands of condensed edge-sharing O@RE 4/4 and O@RE 4/3 tetrahedra ([RE 4O3]2 12+) as well as RE 3+ cations in cavities.

New quaternary arsenide oxides with square planar coordination of gold(I) - structure, (197)Au Mössbauer spectroscopic, XANES and XPS characterization of Nd10Au3As8O10 and Sm10Au3As8O10

The quaternary gold(I) arsenide oxides Nd10Au3As8O10 and Sm10Au3As8O10 were synthesized in sealed quartz ampoules from the rare earth (RE) elements, their appropriate sesquioxides, arsenic, arsenic(III) oxide and finely dispersed gold at maximum annealing temperatures of 1223 K. Both structures were refined from X-ray single crystal diffractometer data at room temperature and at 90 K. Nd10Au3As8O10 and Sm10Au3As8O10 crystallize with a new structure type that derives from the BaAl4 structure through distortions and formation of ordered vacancies. The structures consist of stacked polycationic [RE10O10](10+) layers with oxygen in tetrahedral rare earth coordination and polyanionic [Au(I)3(As2)4](10-) layers with gold in square planar or rectangular planar coordination of four arsenic dumbbells (255 pm As1-As2). In contrast to the well known ionic rare earth oxide layers, the gold arsenide layers rather show covalent bonding and account for the metallic nature of these two new arsenide oxides. This is confirmed by electronic structure calculations and resistivity measurements. The oxidation state of gold was investigated by (197)Au Mössbauer, X-ray absorption near edge structure (XANES) and photoelectron (XPS) spectroscopy. Due to missing comparative gold arsenide compounds, the monovalent gold phosphide oxides RE2AuP2O were measured for comparison. The XANES measurements additionally comprise monovalent gold arsenides REAuAs2. The XPS study contains BaAuAs as reference compound instead. Combination of all data clearly indicates Au(I), which was not observed in square planar coordination up to now. Temperature dependent magnetic susceptibility data show Curie-Weiss paramagnetism for Nd10Au3As8O10 and no magnetic ordering down to 2.5 K. Sm10Au3As8O10 shows the typical Van Vleck type paramagnetism for samarium compounds along with a transition to an antiferromagnetically ordered state at TN = 8.6 K.