Structural characterization of magnesium silicate hydrate: towards the design of eco-sustainable cements

Study on the Performance and Mechanism of Glass Fiber-Reinforced MgO-SiO2-H2O Cement

The magnesium silicate hydrate system (MgO-SiO2-H2O) possesses issues such as susceptibility to cracking, brittleness, and poor volumetric stability, which hinder its development and practical use in engineering applications. This study aimed to enhance the properties of the MgO-SiO2-H2O system by incorporating glass fiber as a reinforcing material. The mechanical properties, shrinkage properties, and properties during accelerated aging were tested at different content levels of glass fiber. Additionally, the reaction mechanism and microscopic morphology were characterized using microscopic testing methods. The results revealed that the addition of glass fiber improved the mechanical properties of the MgO-SiO2-H2O system; meanwhile, with an increase in fiber content, the mechanical properties showed an initial increase followed by a decreasing trend. With a glass fiber content of 0.6%, the system exhibited a flexural strength of 7.9 MPa at 28 d, a compressive strength of 42.5 MPa at 28 d, and a 27.2% increase in splitting tensile strength compared to the control group. At a fiber content of 0.9%, the flexural toughness steadily increased, reaching a maximum value of 2.238 N·m, which is 5.41 times greater than that of the control group. Moreover, the incorporation of glass fiber effectively inhibited the shrinkage of the MgO-SiO2-H2O system. Accelerated aging experiments confirmed that the glass fiber in the MgO-SiO2-H2O system did not undergo significant deterioration or corrosion, thereby maintaining long-term stability. These findings have important theoretical and practical significance for the application and development of the MgO-SiO2-H2O system.

Visible Light Active Magnesium Silicate–Graphitic Carbon Nitride Nanocomposites for Methylene Blue Degradation and Pb2+ Adsorption

Magnesium silicate nanosheets (MgSiNS) and graphitic carbon nitride (g-C3N4) nanocomposites were produced by varying different weight percentages of g-C3N4. The obtained nanocomposites were characterized by various techniques such as X-Ray diffraction (XRD), Fourier transformed infrared spectroscopy (FT-IR), diffuse reflectance UV–vis spectroscopy (DR UV–vis), N2-physisorption, transmission electron microscopy (TEM), and X-ray photon spectroscopy (XPS). The photocatalytic activities of the nanocomposites were measured using visible light irradiation to degrade methylene blue (MB) and Pb2+ adsorption in aqueous solution. The ideal physicochemical properties such as porosity, band gap energy, and functional groups in the MgSiNS-GN20 composite (80% MgSiNS and 20 wt % of g-C3N4) offered high Pb2+ adsorption (0.005 mol/g) and excellent MB degradation efficiency (approximately 93%) at pH 7 within 200 min compared to other composites. In addition, the influences of different reaction parameters such as the effect of pH, the load catalyst, and the concentration of MB and Pb+2 ions were examined. The obtained results indicate that inexpensive and eco-friendly MgSiNS and g-C3N4 composites could be recycled several times, hence representing a promising material to purify water from both organic and inorganic contaminants.

Influence of Synthetic Limestone Sand on the Frost Resistance of Magnesium Potassium Phosphate Cement Mortar

Synthetic limestone sand has advantages, such as stable quality and adjustable particle size distribution, and has gradually substituted high-quality natural sand as a fine aggregate in concrete production. The project team has prepared Magnesium Potassium Phosphate Cement (MKPC) mortar by replacing part of the river sand with machine-made limestone sand in equal amounts, which proves that its physical and mechanical properties are obviously better than mortar prepared by whole river sand. However, the research on the impact of machine-made limestone sand on the durability of MKPC mortar has not been carried out. As the repairing material of concrete structures, the frost resistance of MKPC mortar must be evaluated. In this study, the effect of synthetic limestone sand on the frost resistance of Magnesium Potassium Phosphate Cement (MKPC) mortar was investigated by characterizing the strength, mass loss rate, and water absorption of specimens subjected to freeze-thaw cycling. MKPC mortars prepared using solely river sand (M0) or limestone sand (M1) were completely degraded after 225 freezing-thawing cycles in water, whereas the flexural and compressive strengths of MKPC mortar (M2) prepared using both river and synthetic limestone sands was 29.3 and 22.0% of the initial strengths, respectively. The water freeze-thaw resistance of M2 specimens were significantly higher than that of M0 and M1 specimens, and the sulfate freeze-thaw resistance of M1 and M2 were significantly higher than that of M0. The mass loss of MKPC mortar is not more than 0.4% when it is frozen and thawed 225 times in water and 5% Na₂SO₄ solution, which is far lower than the damage standard of 5%. Based on the favorable composition of the two aggregates, the initial open porosity of M2 was relatively low, owing to the lower water-cement ratio of the mortar at the same flow rate.

Poly(lactic acid)-poly(ethylene glycol)/Magnesium Silicate Membrane for Methylene Blue Removal: Adsorption Behavior, Mechanism, Ionic Strength and Reusability Studies

In this work, the effect of magnesium silicate (MgSiO₃) as a filler on poly(lactic acid)-poly(ethylene glycol) (PLA-PEG) membrane was investigated towards the enhancement of adsorption capacity for removal of cationic dye. The preparation and fabrication of membranes were performed through copolymerization and phase inversion techniques. Analysis of functional groups, tensile strength, morphology and surface wettability were employed in the characterization of the membranes. After the addition of MgSiO₃, it was found that the PLA-PEG/MgSiO₃ membrane presented a higher hydrophilic property with improved mechanical strength. Next, the adsorption of methylene blue (MB) was optimized using response surface methodology (RSM) with the parameters mass of membrane and initial concentration of MB solution. The effects of pH and ionic strength were also examined to determine the mechanism involved during adsorption processes, which later were found to be electrostatic interaction and ion-exchange mechanism. From the isotherms and kinetics studies, the PLA-PEG/MgSiO₃ membrane was well fitted by the Freundlich model and pseudo second order model, respectively. This membrane also demonstrated reusable character of up to six cycles.

Chemical and Microstructural Properties of Designed Cohesive M-S-H Pastes

Concretes can be exposed to a magnesium attack in several environments leading to the formation of magnesium silicate hydrates (M-S-H) and brucite (MH). The formation of M-S-H is likely to alter the properties of the cement matrix because it is linked to the decalcification of C-S-H. However, relatively few data on M-S-H exist in the literature. In order to characterize, physically and mechanically, the M-S-H phase, pure M-S-H cohesive pastes are needed. This work studies the formation of cohesive M-S-H pastes made with MgO-to-SiO₂ atomic ratios of 0.78, 1 and 1.3, from two types of silica (silica fume or colloidal silica) and under 20 °C and 50 °C thermal curing. X-ray diffraction and thermogravimetric analyses confirmed that the consumption of brucite and the formation of M-S-H were quicker with a 50 °C curing. Energy-dispersive X-ray spectroscopy and microtomography showed that colloidal silica enabled a better distribution of the particles than silica fume. Microstructural characterizations were conducted under the protocol with colloidal silica and 50 °C thermal curing. Porosity investigations allowed to describe the M-S-H pastes as highly porous materials with a low content of micropores in comparison with mesopores. The type of mixing influenced the mesopore size distribution.

3D printable magnesium-based cements towards the preparation of bioceramics

HYPOTHESIS

Among all the materials used so far to replace and repair damaged bone tissues, magnesium silicate bioceramics are one of the most promising, thanks to their biocompatibility, osteoinductive properties and good mechanical stability.

EXPERIMENTS

Magnesium silicate cement pastes were prepared by hydration of MgO mixed with different SiO₂ batches at different Mg/Si molar ratios. Pastes were either moulded or 3D printed to obtain set cements that were then calcined at 1000 °C to produce biologically relevant ceramic materials. Both cements and ceramics were characterized by means of X-ray diffraction, while two selected formulations were thoroughly characterized by means of injectability tests, Raman confocal microscopy, scanning electron microscopy, atomic force microscopy, gas porosimetry, X-ray microtomography and compressive tests.

FINDINGS

The results show that bioceramic scaffolds, namely forsterite and clinoenstatite, can be effectively obtained by 3D printing MgO/SiO₂ cement pastes, paving the way towards important advances in the field of bone tissue engineering.

Functionalised nanoclays as microstructure modifiers for calcium and magnesium silicate hydrates

Calcium silicate hydrate (C-S-H) is the main binding product of ordinary Portland concrete (OPC). Unfortunately, OPC production generates ∼5% of all anthropomorphic CO2. Among the most promising green alternatives, magnesium silicate hydrate (M-S-H) is a colloidal gel equivalent to C-S-H which exhibits weaker mechanical properties. Here we investigated the effect of the inclusion of aluminosilicate nanoclays (HNTs) on the microstructure of the silicate hydrate gels as a strategy to ultimately improve their mechanical properties. The microstructure of C-S-H and M-S-H gels synthesized with and without carboxylic or polycarboxylic functionalised HNTs (HNT-COOH, HNT-PAA) was investigated by a multi-technique approach including small- and wide-angle X-ray scattering (SWAXS) and scanning electron microscopy (SEM). The results indicate that, during C-S-H formation in solution, HNTs decrease the size of the disk-like globules with little influence on the spacing of calcium silicate layers. In the case of M-S-H, the presence of functionalised HNTs has a reduced effect on the hydrate structure as a result of the weaker interaction of the carboxylic moieties with Mg2+ ions. SEM investigation on the synthesized composites shows that HNT-PAA are better included in the hydration products. Moreover, in the proximity of the PAA functionalised surfaces, less extended aggregates are formed. The morphology at the micron scale for M-S-H and C-S-H with HNT-COOH is conserved.

Influence of Dry Milling on Phase Transformation of Sepiolite upon Alkali Activation: Implications for Textural, Catalytic and Sorptive Properties

Activation of natural sepiolite by means of grinding in a planetary mill followed by wet NaOH activation was studied for the purpose of endowing the product with enhanced basicity for potential catalytic/sorptive applications. Synthesized solids were characterized with X-ray powder diffraction (XRD), N₂ adsorption/desorption, scanning electron microscopy (SEM), energy dispersive (EDX), atomic absorption (AAS), Fourier-transform infrared (FTIR) and ²⁹Si magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopies. Surface basicity was determined by titration with benzoic acid. Grinding changed the pathway of sepiolite phase transformation upon NaOH treatment. The as-received sepiolite evolved to Na-sepiolite (loughlinite) with a micropore system blocked by nanocrystalline Mg(OH)₂, while ground samples yielded magnesium silicate hydrate phase (MSH), with well-developed microporous texture. In unmilled sepiolite desilication involved preferential leaching of Si from the center of the structural ribbons, while in ground samples additional loss of Si from ribbon-ribbon corner linkages was observed. In all cases treatment with NaOH led to enhancement of surface basicity. Synthesized materials were tested as catalysts in a base-catalyzed aldol self-condensation of acetone and oxidation of cyclohexanone to ε-caprolactone, as well as CO₂ sorbents. Catalytic trends depended not only on samples’ basicity, but also on texture and phase composition of the catalysts. Grinding combined with alkali activation proved a simple and effective method for boosting CO₂-sorption capacity of sepiolite to the level comparable to amine-functionalized, acid-activated sepiolite sorbents.

Exploiting in-situ solid-state NMR spectroscopy to probe the early stages of hydration of calcium aluminate cement

We report a high-field in-situ solid-state NMR study of the hydration of CaAl₂O₄ (the most important hydraulic phase in calcium aluminate cement), based on time-resolved measurements of solid-state ²⁷Al NMR spectra during the early stages of the reaction. A variant of the CLASSIC NMR methodology, involving alternate recording of direct-excitation and MQMAS ²⁷Al NMR spectra, was used to monitor the ²⁷Al species present in both the solid and liquid phases as a function of time. Our results provide quantitative information on the changes in the relative amounts of ²⁷Al sites with tetrahedral coordination (the anhydrous reactant phase) and octahedral coordination (the hydrated product phases) as a function of time, and reveal significantly different kinetic and mechanistic behaviour of the hydration reaction at the different temperatures (20 °C and 60 °C) studied.

How the acido-basic properties of Mg silicates and clays govern the catalytic mechanism of transesterification reactions

Choosing acido-basic properties of magnesium silicates to tune the transesterification mechanism in the liquid phase.

Characterization of Magnesium Silicate Hydrate (MSH) Gel Formed by Reacting MgO and Silica Fume

Magnesium silicate hydrate (MSH) gel was formed by reacting magnesium oxide (MgO) with silica fume (SF) in distilled water. The MSH was prepared using a MgO/SF molar ratio of 1.0 (40:60 weight ratio). Samples were analyzed during hydration process up to 300 days at room temperature. The MSH characterization has been carried out using a range of analytical techniques. Quantitative analysis was achieved using thermogravimetric analysis (TG/DTG) with a de-convolution technology. The structure of MSH gel was characterized using solid state nuclear magnetic resonance (²⁹Si NMR) and Fourier transform infrared (FT-IR) spectroscopy. Transmission electron microscopy (TEM) was used to investigate MSH microstructure. Compared with natural magnesium silicate hydrate minerals, the structure of MSH gel is highly disordered and generates on the surface of particles, producing a shell structure with cavity. The molecular structure of MSH phase is layered. The results also show that the extent of polymerization of MSH gel is related to the solution pH during hydration.

Unlocking the role of MgO in the carbonation of alkali-activated slag cement

MgO incorporation into alkali-activated slag cement reduces the rate of carbonation.

Influence of acid–base properties of Mg-based catalysts on transesterification: role of magnesium silicate hydrate formation

Catalysts with the strongest basic properties are not always the most efficient ones for transesterification, a series of magnesium-based materials, exhibiting a large range of acido–basic properties, was investigated.