Relationships between elastic anisotropy and thermal expansion in A2Mo3O12 materials

Phase Transition and Coefficients of Thermal Expansion in Al2-xInxW3O12 (0.2 ≤ x ≤ 1)

Materials from theA2M3O12 family are known for their extensive chemical versatility while preserving the polyhedral-corner-shared orthorhombic crystal system, as well as for their consequent unusual thermal expansion, varying from negative and near-zero to slightly positive. The rarest are near-zero thermal expansion materials, which are of paramount importance in thermal shock resistance applications. Ceramic materials with chemistry Al2-xInxW3O12 (x = 0.2-1.0) were synthesized using a modified reverse-strike co-precipitation method and prepared into solid specimens using traditional ceramic sintering. The resulting materials were characterized by X-ray powder diffraction (ambient and in situ high temperatures), differential scanning calorimetry and dilatometry to delineate thermal expansion, phase transitions and crystal structures. It was found that the x = 0.2 composition had the lowest thermal expansion, 1.88 × 10-6 K-1, which was still higher than the end member Al2W3O12 for the chemical series. Furthermore, the AlInW3O12 was monoclinic phase at room temperature and transformed to the orthorhombic form at ca. 200 °C, in contrast with previous reports. Interestingly, the x = 0.2, x = 0.4 and x = 0.7 materials did not exhibit the expected orthorhombic-to-monoclinic phase transition as observed for the other compositions, and hence did not follow the expected Vegard-like relationship associated with the electronegativity rule. Overall, compositions within the Al2-xInxW3O12 family should not be considered candidates for high thermal shock applications that would require near-zero thermal expansion properties.

Near-Zero Thermal Expansion in Freeze-Cast Composite Materials

Most materials expand when heated, which can lead to thermal stress and even failure. Whereas thermomiotic materials exhibit negative thermal expansion, the creation of materials with near-zero thermal expansion presents an ongoing challenge due to the need to optimize thermal and mechanical properties simultaneously. The present work describes the preparation and properties of polymer–ceramic composites with low thermal expansion. Ceramic scaffolds, prepared by freeze-casting of low-thermal-expansion Al2W3O12, were impregnated with poly(methylmethacrylate) (PMMA). The resulting composites can have a coefficient of thermal expansion as low as 2 × 10−6 K−1, and hardness values of 4.0 ± 0.3 HV/5 (39 ± 3 MPa) and 16 ± 3 HV/5 (160 ± 30 MPa) parallel and perpendicular to the ice growth, respectively. The higher hardness perpendicular to the ice growth direction indicates that the PMMA is acting to improve the mechanical properties of the composite.

Synthesis and thermoelastic properties of Zr(CN2)2and Hf(CN2)2

Metal carbodiimides with wine-rack topology exhibiting thermoelastic properties like those of flexible framework materials.

Thermal mismatch strain induced disorder of Y2Mo3O12 and its effect on thermal expansion of Y2Mo3O12/Al composites

Fully dense Y₂Mo₃O₁₂/Al composites were prepared by squeeze casting.