Ultrafine fully vulcanized natural rubber modified by graft-copolymerization with styrene and acrylonitrile monomers

This research aims to modify ultrafine fully vulcanized powdered natural rubber (UFPNR) prepared by emulsion graft-copolymerization with styrene (St) and acrylonitrile (AN) monomers onto deproteinized natural rubber (DPNR). The effects of monomers content and St/AN weight ratio on grafting efficiency and thermal stability of the developed DPNR-g-(PS-co-PAN) were investigated. The results showed that grafting efficiency was enhanced up to 86% with monomers content 15 phr and weight ratio St:AN 80:20. The obtained DPNR-g-(PS-co-PAN) was radiated by an electron beam at various doses, followed by a spray drying process to produce UFPNR. The obtained modified UFPNR particles irradiated at dose up to 300 kGy were relatively spherical with a particle size of approximately 4.4 µm. Furthermore, the degradation temperature of 5wt% loss (Td5) of UFPNR was found in the range of 349-356 °C. The results revealed that the modified UFPNR is suitable as a toughening filler for a broader spectrum of polymers.

A review of smart electrospun fibers toward textiles

Electrospinning as a versatile technology has attracted a large amount of attention in the past few decades due to the facile way to produce micro- and nano-scale fibers featuring flexibility, large specific surface area and high porosity. Stimuli-responsive polymers are a class of smart materials that are capable of sensing surround environment and interacting with them. Therefore, the combination of electrospinning and smart materials could have a great deal of benefits over the development of smart fibers. In this review, it offers a comprehensive understanding of smart electrospun fibers toward textile applications. Firstly, the definition of smart fibers and the differences between interactive fibers and passive interactive fibers are briefly introduced. Then some interactive fibers made from temperature-, pH-, light-, electric field/electricity-, magnetic field-, multi-responsive polymers, as well as some polymers featuring piezoelectric and triboelectric effect which are suitable flexible electrics, are emphasized with their applications in the form of electrospun fibers. Afterwards, some passive and hybrid smart electrospun fibers are introduced. Finally, associated challenges and perspectives are summarized and discussed.

•

Understanding of passive smart electrospun fibers and interactive smart electrospun fibers.

•

The recent progress in flexible electronics from electrospun fibers.

•

The recent progress in stimuli-responsive polymers applied in interactive smart electrospun fibers.

Electrospun Nano-Fibers for Biomedical and Tissue Engineering Applications: A Comprehensive Review

Pharmaceutical nano-fibers have attracted widespread attention from researchers for reasons such as adaptability of the electro-spinning process and ease of production. As a flexible method for fabricating nano-fibers, electro-spinning is extensively used. An electro-spinning unit is composed of a pump or syringe, a high voltage current supplier, a metal plate collector and a spinneret. Optimization of the attained nano-fibers is undertaken through manipulation of the variables of the process and formulation, including concentration, viscosity, molecular mass, and physical phenomenon, as well as the environmental parameters including temperature and humidity. The nano-fibers achieved by electro-spinning can be utilized for drug loading. The mixing of two or more medicines can be performed via electro-spinning. Facilitation or inhibition of the burst release of a drug can be achieved by the use of the electro-spinning approach. This potential is anticipated to facilitate progression in applications of drug release modification and tissue engineering (TE). The present review aims to focus on electro-spinning, optimization parameters, pharmacological applications, biological characteristics, and in vivo analyses of the electro-spun nano-fibers. Furthermore, current developments and upcoming investigation directions are outlined for the advancement of electro-spun nano-fibers for TE. Moreover, the possible applications, complications and future developments of these nano-fibers are summarized in detail.