Large-Scale Noncovalent Functionalization of 2D Materials through Thermally Controlled Rotary Langmuir-Schaefer Conversion

As two-dimensional (2D) materials are more broadly utilized as components of hybrid materials, controlling their surface chemistry over large areas through noncovalent functionalization becomes increasingly important. Here, we demonstrate a thermally controlled rotary transfer stage that allows areas of a 2D material to be continuously cycled into contact with a Langmuir film. This approach enables functionalization of large areas of the 2D material and simultaneously improves long-range ordering, achieving ordered domain areas up to nearly 10 000 μm². To highlight the layer-by-layer processing capability of the rotary transfer stage, large-area noncovalently adsorbed monolayer films from an initial rotary cycle were used as templates to assemble ultranarrow gold nanowires from solution. The process we demonstrate would be readily extensible to roll-to-roll processing, addressing a longstanding challenge in scaling Langmuir-Schaefer transfer for practical applications.

Reactive two-component monolayers template bottom-up assembly of nanoparticle arrays on HOPG

Two triphenyleneethynylene derivatives, 1OH and 2, self-assemble a patterned monolayer (ML) at the solution-graphite (HOPG) interface. The four molecule unit cell of the ML, (1OH1OH22), spans 19 nm and contains adjacent columns of 1OH molecules spaced by 4.7 nm. Following ML assembly, a disulfide is appended to the alcohol group on each 1OH molecule and used to capture 2.0 nm gold nanoparticles (AuNP). The patterned monolayer directs bottom-up assembly of a 5 nm/19 nm double pitch AuNP pattern.