Cs-137 immobilization in C-S-H gel nanopores

Cesium immobilization of high pH and low pH belite-rich cement under varying temperature

Low-pH cement is being studied in radioactive waste repositories. The belite-rich cement (BRC) recently gained attention due to its higher CO2 sequestration and low pH attainment under carbonation exposure. Therefore, this study evaluated the effects of pH and temperature on cesium immobilization of BRC. High pH (12.6) and low pH (9.9) BRC were produced via air curing and carbonation treatment, respectively. The high and low pH BRC samples were placed in a leaching environment at 25 °C and 45 °C for 90 days. An inverse correlation between pH and cesium mobilization of BRC was observed. The high pH BRC achieved the lowest effective diffusion coefficient (4.05E-09 cm2/s), whereas the highest value (2.64E-07 cm2/s) was achieved in case of low pH BRC. The physicochemical and morphological properties unveiled the decrease in Si/Ca ratio of gel, precipitation of Ca2+ ions in calcite formation, and increment in pore structure connectivity (pore size > 100 nm) in low pH BRC. However, the high pH BRC demonstrated the high Si/Ca ratio in C-S-H gel, hydroxide phases and higher disconnected pores. Thermodynamic modeling revealed the presence of significant carbonated phases beyond 15% CO2 uptake. The findings contributed to the BRC's feasibility in developing nuclear waste storage facility.

Atomic-Level and Surface Structure of Calcium Silicate Hydrate Nanofoils

Deciphering the calcium silicate hydrate (C-S-H) surface is crucial for unraveling the mechanisms of cement hydration and property development. Experimental observations of C-S-H in cement systems suggest a surface termination which is fundamentally different from the silicate-terminated surface assumed in many atomistic level studies. Here, a new multiparameter approach to describing the (001) basal C-S-H surface is developed, which considers how the surface termination affects the overall properties (Ca/Si ratio, mean chain length, relative concentration of silanol and hydroxide groups). Contrary to current beliefs, it is concluded that the (001) C-S-H surface is dominantly calcium terminated. Finally, an adsorption mechanism for calcium and hydroxide ions is proposed, which is in agreement with the surface charge densities observed in previous studies.

Immobilization of Radionuclide 133Cs by Magnesium Silicate Hydrate Cement

The radionuclide cesium (Cs) was solidified using magnesium silicate hydrate (M–S–H) cement. The influence of Cs⁺ on the reaction of the M–S–H gel system was evaluated by measuring the compressive strength and microscopic properties of the solidified body. By testing the impact resistance, leaching resistance and freeze–thaw resistance of the solidified body, the immobilizing ability of Cs⁺ by the M–S–H cement was analyzed. Results indicate that Cs⁺ only slightly affects the reaction process of the M–S–H gel system, and only slows down the transformation rate of Mg(OH)₂ into the M–S–H gel to a certain extent. The M–S–H cement exhibits superior performance in solidifying Cs⁺. Both the leaching rate and cumulative leach fraction at 42 d were considerably lower than the national requirements and better than the ordinary Portland cement-solidified body. The curing effect of the M–S–H cement on Cs⁺ is mainly physical encapsulation and chemisorption of hydration products.