Performance enhancement of asymmetric supercapacitors with bud-like Cu-doped Mn3O4 hollow and porous structures on nickel foam as positive electrodes

Elucidating the Role of Copper-Induced Mixed Phases on the Electrochemical Performance of Mn-Based Thin-Film Electrodes

Manganese oxide is a fascinating material for use as a thin-film electrode in supercapacitors. Herein, the consequences of copper incorporation on spray pyrolyzed manganese oxide thin films and their electrochemical performance were investigated. The Cu-incorporated manganese oxide thin films were deposited by spray pyrolysis, and their structural and electrochemical properties were thoroughly evaluated. The formation of the spinel Mn3O4 phase with effective Cu incorporation was confirmed by X-ray diffraction investigation. Through Raman studies, it was noticed that mixed phases of manganese oxide tend to form after Cu incorporation, and this result was also reflected in X-ray photoelectron spectroscopic studies. The surface morphology and roughness were also altered by the addition of copper. However, electrochemical measurements implied a reduction in the specific capacitance upon copper inclusion. The cyclic voltammetry test indicated a specific capacitance of 132 F/g for Mn3O4 electrodes, but a substantial drop for copper-incorporated samples due to the mixed manganese phase. The decremental tendency was further supported by galvanostatic charge-discharge studies and electrochemical impedance spectroscopic measurements. These results provide valuable insights into the effects of copper addition in manganese oxide thin-film-based electrodes for energy storage applications.

Bioinspired palladium-doped manganese oxide nanocorns: a remarkable antimicrobial agent targeting phyto/animal pathogens

Microbial pathogens are known for causing great environmental stress, owing to which emerging challenges like lack of eco-friendly remediation measures, development of drug-resistant and mutational microbial strains, etc., warrants novel and green routes as a stepping stone to serve such concerns sustainably. In the present study, palladium (Pd) doped manganese (II, III) oxide (Mn3O4) nanoparticles (NPs) were synthesized using an aqueous Syzygium aromaticum bud (ASAB) extract. Preliminary phytochemical analysis of ASAB extract indicates the presence of polyphenolics such as phenols, alkaloids, and flavonoids that can act as potential capping agents in NPs synthesis, which was later confirmed in FTIR analysis of pure and Pd-doped Mn3O4 NPs. XRD, Raman, and XPS analyses confirmed the Pd doping in Mn3O4 NPs. FESEM and HRTEM study reveals the mixed morphologies dominated by nanocorns appearance. Zeta potential investigation reveals high stability of the synthesized NPs in colloidal solutions. The developed Pd-doped Mn3O4 NPs were tested against two fungal phytopathogens, i.e., Sclerotinia sclerotiorum and Colletotrichum gloeosporioides, known for causing great economic losses in yield and quality of different plant species. The antifungal activity of synthesized Pd-doped Mn3O4 NPs displayed a dose-dependent response with a maximum of ~92%, and ~72% inhibition was recorded against S. sclerotiorum and C. gloeosporioides, respectively, at 1000 ppm concentration. However, C. gloeosporioides demonstrated higher sensitivity to Pd-doped Mn3O4 NPs upto 500 ppm) treatment than S. sclerotiorum. The prepared NPs also showed significant antibacterial activity against Enterococcus faecalis. The Pd-doped Mn3O4 NPs were effective even at low treatment doses, i.e., 50-100 ppm, with the highest Zone of inhibition obtained at 1000 ppm concentration. Our findings provide a novel, eco-benign, and cost-effective approach for formulating a nanomaterial composition offering multifaceted utilities as an effective antimicrobial agent.

Reliable, High-Performance Electrochromic Supercapacitors Based on Metal-Doped Nickel Oxide

Herein, high-performance, reliable electrochromic supercapacitors (ECSs) are proposed based on tungsten trioxide (WO₃) and nickel oxide (NiO) films. To maximize device performance and stability, the stoichiometric balance between anode and cathode materials is controlled by carefully adjusting the thickness of the anodic NiO film while fixing the thickness of WO₃ to ∼660 nm. Then, a small amount (≤10 mol %) of metal (e.g., copper) is doped into the NiO film, improving the electrical conductivity and electrochemical activity. At a Cu doping level of 7 mol %, the resulting ECS exhibited the highest performance, including a high areal capacitance (∼14.9 mF/cm²), excellent coulombic efficiency (∼99%), wide operating temperature range (0-80 °C), reliable operation with high charging/discharging cyclic stability (>10,000 cycles), and good self-discharging durability. Simultaneously, the change in transmittance of the device is well synchronized with the galvanostatic charging/discharging curve by which the real-time energy storage status is visually indicated. Furthermore, the practical feasibility of the device is successfully demonstrated. These results imply that the ECS fabricated in this work is a promising potential energy storage platform and an attractive component for future electronics.

Synthesis of Cu-Doped Mn3O4@Mn-Doped CuO Nanostructured Electrode Materials by a Solution Process for High-Performance Electrochemical Pseudocapacitors

Cu-doped Mn3O4 and Mn-doped CuO (CMO@MCO) mixed oxides with isolated phases together with pristine Mn3O4 (MO) and CuO (CO) have been synthesized by a simple solution process for applications in electrochemical supercapacitors. The crystallographic, spectroscopic, and morphological analyses revealed the formation of all of the materials with good crystallinity and purity with the creation of rhombohedral-shaped MO and CMO and a mixture of spherical and rod-shaped CO and MCO nanostructures. The ratio of CMO and MCO in the optimized CMO@MCO was 2:1 with the Cu and Mn dopants percentages of 12 and 15%, respectively. The MO-, CO-, and CMO@MCO-modified carbon cloth (CC) electrodes delivered the specific capacitance (C s) values of 541.1, 706.7, and 997.2 F/g at 5 mV/s and 413.4, 480.5, and 561.1 F/g at 1.3 A/g, respectively. This enhanced C s value of CMO@MCO with an energy density and a power density of 78.0 Wh/kg and 650.0 W/kg, respectively, could be attributed to the improvement of electrical conductivity induced by the dopants and the high percentage of oxygen vacancies. This corroborated to a decrease in the optical band gap and charge-transfer resistance (R ct) of CMO@MCO at the electrode/electrolyte interface compared to those of MO and CO. The net enhancement of the Faradaic contribution induced by the redox reaction of the dopant and improved surface area was also responsible for the better electrochemical performance of CMO@MCO. The CMO@MCO/CC electrode showed high electrochemical stability with a C s loss of only ca. 4.7%. This research could open up new possibilities for the development of doped mixed oxides for high-performance supercapacitors.