Enhanced gas selectivity induced by surface active oxygen in SnO/SnO2 heterojunction structures at different temperatures

In Situ Local Oxidation of SnO Induced by Laser Irradiation: A Stability Study

In this work, semiconductor tin oxide (II) (SnO) nanoparticles and plates were synthesized at room conditions via a hydrolysis procedure. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the high crystallinity of the as-synthesized romarchite SnO nanoparticles with dimensions ranging from 5 to 16 nm. The stability of the initial SnO and the controlled oxidation to SnO2 was studied based on either thermal treatments or controlled laser irradiation using a UV and a red laser in a confocal microscope. Thermal treatments induced the oxidation from SnO to SnO2 without formation of intermediate SnOx, as confirmed by thermodiffraction measurements, while by using UV or red laser irradiation the transition from SnO to SnO2 was controlled, assisted by formation of intermediate Sn3O4, as confirmed by Raman spectroscopy. Photoluminescence and Raman spectroscopy as a function of the laser excitation source, the laser power density, and the irradiation duration were analyzed in order to gain insights in the formation of SnO2 from SnO. Finally, a tailored spatial SnO/SnO2 micropatterning was achieved by controlled laser irradiation with potential applicability in optoelectronics and sensing devices.

Au Nanoparticles Decorated Mesoporous SiO2 -WO3 Hybrid Materials with Improved Pore Connectivity for Ultratrace Ethanol Detection at Low Operating Temperature

Semiconducting metal oxides-based gas sensors with the capability to detect trace gases at low operating temperatures are highly desired in applications such as wearable devices, trace pollutant detection, and exhaled breath analysis, but it still remains a great challenge to realize this goal. Herein, a multi-component co-assembly method in combination with pore engineering strategy is proposed. By using bi-functional (3-mercaptopropyl) trimethoxysilane (MPTMS) that can co-hydrolyze with transition metal salt and meanwhile coordinate with gold precursor during their co-assembly with PEO-b-PS copolymers, ordered mesoporous SiO₂ -WO₃ composites with highly dispersed Au nanoparticles of 5 nm (mesoporous SiO₂ -WO₃ /Au) are straightforward synthesized. This multi-component co-assembly process avoids the aggregation of Au nanoparticles and pore blocking in conventional post-loading method. Furthermore, through controlled etching treatment, a small portion of silica can be removed from the pore wall, resulting in mesoporous SiO₂ -WO₃ /Au with increased specific surface area (129 m²  g^-1 ), significantly improved pore connectivity, and enlarged pore window (>4.3 nm). Thanks to the presence of well-confined Au nanoparticles and ε-WO₃ , the mesoporous SiO₂ -WO₃ /Au based gas sensors exhibit excellent sensing performance toward ethanol with high sensitivity (R_a /R_g = 2-14 to 50-250 ppb) at low operating temperature (150 °C).

Synergetic Improvement of Stability and Conductivity of Hybrid Composites formed by PEDOT:PSS and SnO Nanoparticles

In this work, layered hybrid composites formed by tin oxide (SnO) nanoparticles synthesized by hydrolysis and poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) have been analyzed. Prior to the composite study, both SnO and PEDOT:PSS counterparts were characterized by diverse techniques, such as X-ray diffraction (XRD), Raman spectroscopy, transmission electron microscopy (TEM), photoluminescence (PL), atomic force microscopy (AFM), optical absorption and Hall effect measurements. Special attention was given to the study of the stability of the polymer under laser illumination, as well as the analysis of the SnO to SnO2 oxidation assisted by laser irradiation, for which different laser sources and neutral filters were employed. Synergetic effects were observed in the hybrid composite, as the addition of SnO nanoparticles improves the stability and electrical conductivity of the polymer, while the polymeric matrix in which the nanoparticles are embedded hinders formation of SnO2. Finally, the Si passivation behavior of the hybrid composites was studied.