Comparing the efficacy of hydroxyapatite nucleation regulated by amino acids, poly-amino acids and an amelogenin-derived peptide

Remineralizing capacity of zinc oxide eugenol sealer following the addition of nanohydroxyapatite-tyrosine amino acid: An in vivo animal study

OBJECTIVE

Although several sealers have been developed, the zinc oxide eugenol (ZOE) sealer is still used in many private dental clinics. This study aimed to compare the biocompatibility and remineralizing capacity οf ZOE sealer with the addition of nanohydroxyapatite-tyrosine amino acid.

METHODS

This study was conducted on Twenty rabbits. The rabbits were divided into four groups based on the test observation period (3, 7, 21, and 28 days) following surgical implantation. General anesthesia was administered to each rabbit, and a subcutaneous incision of approximately 1 ± 0.5 cm was made along the symphyseal area of the mandible of each rabbit. Four bone cavities were generated in the interdental space of the lower jaw between the central and molar teeth of each rabbit, with one longitudinal subcutaneous incision. The ZOE sealers were mixed according to the manufacturer's guidelines and directly inserted within the cavities generated at the end of each test period. The animals were sacrificed, and bone biopsy was carried out at the site of testing. The biopsy samples were obtained and subjected to histological analysis using a low-power light microscope (Olympus C ⅹ 21, Japan) and immunohistochemistry using Ki67 antibody.

RESULTS

The collected information was examined by parametric statistical tests using SPSS software version ''22." One-way ANOVA and post-hoc Duncan's tests were used to measure the significance among various groups, with statistical significance set, when "P ≤ 0.01".

CONCLUSION

The 20% mixed endodontic sealer displayed excellent outcomes compared to other experimental groups, as identified by higher new bone formation at every evaluation period.

Crystallization of smooth amorphous calcium phosphate microspheres to core-shell hydroxyapatite microspheres

Calcium phosphates (Ca-P) represent a significant class of biological minerals found in natural hard tissues. Crystallization through phase transformation of a metastable precursor is an effective strategy to guide the growth of crystalline Ca-P with exceptional functionality. Despite extensive research on Ca-P, the exact process during the crystallization of amorphous particles to hydroxyapatite (HA) remains elusive. Herein, pure HA microspheres with a core-shell structure are crystallized via dissolution and re-crystallization of smooth amorphous calcium phosphate (ACP) microspheres. The transformation is initiated with the increase of the hydrothermal treatment time in the presence of sodium trimetaphosphate and l-glutamic. The underlying mechanisms along with the kinetics of such transformation are explored. Nanocrystalline areas are formed on the smooth ACP microspheres and crystallization advances via nanometre-sized clusters formed by directional arrangement of nanocrystalline whiskers. Our findings shed light on a crucial but unclear stage in the genesis of HA crystals, specifically under the conditions of hydrothermal synthesis.

Rapid Deposition of the Biomimetic Hydroxyapatite-Polydopamine-Amino Acid Composite Layers onto the Natural Enamel

In this work, we developed a technology that enables rapid deposition of biomimetic composite films onto natural enamel slices (known as biotemplates). These films are composed of polydopamine (PDA) and nanocrystalline carbonate-substituted hydroxyapatite (nano-cHAp) that have been functionalized with amino acid l-Arginine. We utilized atomic force microscopy (AFM) and scattering scanning near-field optical microscopy (s-SNOM) combined with infrared (IR) synchrotron to achieve nanoscale spatial resolution for both IR absorption and topography analyses. This combined analytical modality allowed us to understand how morphology connects to local changes in the chemical environment on the biotemplate surface during the deposition of the bioinspired coating. Our findings revealed that when using the proposed technology and after the deposition of the first PDA layer, the film formed on the enamel surface nearly covers the entire surface of the specimen whose thickness is larger on the surface of the emerging enamel prisms. Calculation of the crystallinity index for the biomimetic layer showed a multiple increase compared with natural enamel. This indicates regular and dense aggregation of nano-cHAp into larger crystals, imitating the morphology of natural enamel rods. The microhardness of the formed PDA-based biomimetic layer mineralized with nano-cHAp functionalized with amino acid l-Arginine deposited on natural enamel was practically the same as that of natural enamel. The characterization of nano-cHAp-amino acid-PDA layers using IR and Raman microspectroscopy showed that l-arginine acts as a conjunction agent in the formation of mineralized biomimetic composite coatings. The uniformity of the mechanisms of PDA layer formation under different deposition conditions and substrate types allows for the formation of coatings regardless of the macro- and micromorphology of the template. Therefore, the results obtained in this work have a high potential for future clinical applications in dental practice.

Advanced materials for enamel remineralization

Dental caries, a chronic and irreversible disease caused by caries-causing bacteria, has been listed as one of the three major human diseases to be prevented and treated. Therefore, it is critical to effectively stop the development of enamel caries. Remineralization treatment can control the progression of caries by inhibiting and reversing enamel demineralization at an early stage. In this process, functional materials guide the deposition of minerals on the damaged enamel, and the structure and hardness of the enamel are then restored. These remineralization materials have great potential for clinical application. In this review, advanced materials for enamel remineralization were briefly summarized, furthermore, an outlook on the perspective of remineralization materials were addressed.

Promoting effect of a calcium-responsive self-assembly β-sheet peptide on collagen intrafibrillar mineralization

Recently, a de novo synthetic calcium-responsive self-assembly β-sheet peptide ID8 (Ile-Asp-Ile-Asp-Ile-Asp-Ile-Asp) has been developed to serve as the template inducing hydroxyapatite nucleation. The aim of this study was to evaluate the effect of ID8 on intrafibrillar mineralization of collagen making full use of its self-assembly ability. The mineralization experiments were carried out in vitro on both bare Type I collagen and fully demineralized dentin samples. The calcium-responsive self-assembly of ID8 was revealed by circular dichroism spectrum, 8-anilino-1-naphthalenesulfonic acid ammonium salt hydrate assay, attenuated total reflection Fourier transform infrared spectrum (ATR-FTIR) and transmission electron microscope (TEM). Polyacrylic acid (450 kDa) with a concentration of 100 μg ml⁻¹ was selected as the nucleation inhibitor based on the determination of turbidimetry and TEM with selected area electron diffraction (TEM-SAED). The results showed that collagen intrafibrillar mineralization was significantly promoted with the pretreatment of self-assembly ID8 detected by TEM-SAED, SEM, X-ray diffraction and ATR-FTIR. The pretreatment of collagen utilizing self-assembly ID8 not only enhanced intermolecular hydrogen bonding but also contributed to calcium retention inside collagen and significantly increased the hydrophilicity of collagen. These results indicated that peptides with self-assembly properties like ID8 are expected to be potential tools for biomimetic mineralization of collagen.

Biomimetic Mineralization of Tooth Enamel Using Nanocrystalline Hydroxyapatite under Various Dental Surface Pretreatment Conditions

In this report, we demonstrated the formation of a biomimetic mineralizing layer obtained on the surface of dental enamel (biotemplate) using bioinspired nanocrystalline carbonate-substituted calcium hydroxyapatite (ncHAp), whose physical and chemical properties are closest to the natural apatite dental matrix, together with a complex of polyfunctional organic and polar amino acids. Using a set of structural, spectroscopy, and advanced microscopy techniques, we confirmed the formation of a nanosized ncHAp-based mineralized layer, as well as studying its chemical, substructural, and morphological features by means of various methods for the pretreatment of dental enamel. The pretreatment of a biotemplate in an alkaline solution of Ca(OH)₂ and an amino acid booster, together with the executed subsequent mineralization with ncHAp, led to the formation of a mineralized layer with homogeneous micromorphology and the preferential orientation of the ncHAp nanocrystals. It was shown that the homogeneous crystallization of hydroxyapatite on the biotemplate surface and binding of individual nanocrystals and agglomerates into a single complex by an amino acid booster resulted in an increase (~15%) in the nanohardness value in the enamel rods area, compared to that of healthy natural enamel. Obtaining a similar hierarchy and cleavage characteristics as natural enamel in the mineralized layer, taking into account the micromorphological features of dental tissue, is an urgent problem for future research.

Advances in biomineralization-inspired materials for hard tissue repair

Biomineralization is the process by which organisms form mineralized tissues with hierarchical structures and excellent properties, including the bones and teeth in vertebrates. The underlying mechanisms and pathways of biomineralization provide inspiration for designing and constructing materials to repair hard tissues. In particular, the formation processes of minerals can be partly replicated by utilizing bioinspired artificial materials to mimic the functions of biomolecules or stabilize intermediate mineral phases involved in biomineralization. Here, we review recent advances in biomineralization-inspired materials developed for hard tissue repair. Biomineralization-inspired materials are categorized into different types based on their specific applications, which include bone repair, dentin remineralization, and enamel remineralization. Finally, the advantages and limitations of these materials are summarized, and several perspectives on future directions are discussed.

Morphological evolution of carbonated hydroxyapatite to faceted nanorods through intermediate states

On the conversion of a parent calcite nanocrystal, thin low-crystalline nanosheets of carbonated hydroxyapatite are initially grown via the dissolution–reprecipitation route and then evolve into faceted rods covered with stable surfaces.

The influence of Fe3+ doping on thermally induced crystallization and phase evolution of amorphous calcium phosphate

The present study investigates thermally induced crystallization and phase evolution of amorphous calcium phosphate (ACP) partially substituted with Fe³⁺ ions (M/P = 1.5 : 1).