Reversible Thermo-Optical Response Nanocomposites Based on RAFT Symmetric Triblock Copolymers (ABA) of Acrylamide and N-Isopropylacrylamide and Gold Nanoparticles

The development of composite materials with thermo-optical properties based on smart polymeric systems and nanostructures have been extensively studied. Due to the fact of its ability to self-assemble into a structure that generates a significant change in the refractive index, one of most attractive thermo-responsive polymers is poly(N-isopropylacrylamide) (PNIPAM), as well as its derivatives such as multiblock copolymers. In this work, symmetric triblock copolymers of polyacrylamide (PAM) and PNIPAM (PAM_x-b-PNIPAM_y-b-PAM_x) with different block lengths were prepared by reversible addition-fragmentation chain-transfer polymerization (RAFT). The ABA sequence of these triblock copolymers was obtained in only two steps using a symmetrical trithiocarbonate as a transfer agent. The copolymers were combined with gold nanoparticles (AuNPs) to prepare nanocomposite materials with tunable optical properties. The results show that copolymers behave differently in solution due to the fact of variations in their composition. Therefore, they have a different impact on the nanoparticle formation process. Likewise, as expected, an increase in the length of the PNIPAM block promotes a better thermo-optical response.

Formation of n-Hexane-in-DMF Nonaqueous Pickering Emulsions: ABC Triblock Worms versus AB Diblock Worms

Nonaqueous Pickering emulsions exhibit promising applications in many industrial areas but have been relatively less studied in the past. In this study, n-hexane-in-DMF nonaqueous Pickering emulsions stabilized by core cross-linked copolymer worms with mixed shells are demonstrated for the first time. Core cross-linked copolymer worms with mixed shells were prepared by seeded reversible addition-fragmentation chain transfer (RAFT) quasi-solution polymerization. Specifically, polystyrene-poly(4-vinylpyridine) (PS-P4VP) diblock copolymer worms were first prepared via RAFT-mediated dispersion polymerization in toluene under the given conditions using PS as both the macro-CTA and the stabilizer block. After the chemical cross-linking of P4VP cores, PS-P4VP diblock copolymer worms were chain-extended with LMA in DMF/toluene (1:9, weight ratio) mixed solvents, producing core cross-linked PS-P4VP-PLMA worms with PS/PLMA mixed shells. The as-prepared core cross-linked PS-P4VP-PLMA worms with mixed PS/PLMA shells were further utilized as Pickering emulsifiers for the generation of nonaqueous n-hexane-in-DMF Pickering emulsions. The emulsifying performances of mixed-shell copolymer worms were compared with those of their spherical and linear analogues with entirely identical chemical compositions as well as PS-P4VP diblock copolymer worm precursors, respectively.

Exploration of the modification-induced self-assembly (MISA) technique and the preparation of nano-objects with a functional poly(acrylic acid) core

The hydrolysis-based post-polymerization modification method was introduced into the self-assembly process and a modification-induced self-assembly (MISA) technique was presented.