Boosting oxygen evolution reaction activity by tailoring MOF-derived hierarchical Co–Ni alloy nanoparticles encapsulated in nitrogen-doped carbon frameworks

Easy conversion perovskite fluorides KCo1-xFexF3 for efficient oxygen evolution reaction

Herein, we report an easily oxidized Co-Fe perovskite fluoride as an efficient catalyst for the oxygen evolution reaction (OER). In situ Raman spectroscopy showed that the presence of F promotes reconstruction to form highly active (Co3+Fe3+)OOH, and the current density of 10 mA cm-2 can be achieved at the overpotential of only 118 mV in 1 M KOH aqueous solution. This work helps to understand the role of fluoride during the OER.

Electrochemical Sensing of Favipiravir with an Innovative Water-Dispersible Molecularly Imprinted Polymer Based on the Bimetallic Metal-Organic Framework: Comparison of Morphological Effects

Molecularly imprinted polymers (MIPs) are widely used as modifiers in electrochemical sensors due to their high sensitivity and promise of inexpensive mass manufacturing. Here, we propose and demonstrate a novel MIP-sensor that can measure the electrochemical activity of favipiravir (FAV) as an antiviral drug, thereby enabling quantification of the concentration of FAV in biological and river water samples and in real-time. MOF nanoparticles’ application with various shapes to determine FAV at nanomolar concentrations was described. Two different MOF nanoparticle shapes (dodecahedron and sheets) were systematically compared to evaluate the electrochemical performance of FAV. After carefully examining two different morphologies of MIP-Co-Ni@MOF, the nanosheet form showed a higher performance and efficiency than the nanododecahedron. When MIP-Co/Ni@MOF-based and NIP-Co/Ni@MOF electrodes (nanosheets) were used instead, the minimum target concentrations detected were 7.5 × 10−11 (MIP-Co-Ni@MOF) and 8.17 × 10−9 M (NIP-Co-Ni@MOF), respectively. This is a significant improvement (>102), which is assigned to the large active surface area and high fraction of surface atoms, increasing the amount of greater analyte adsorption during binding. Therefore, water-dispersible MIP-Co-Ni@MOF nanosheets were successfully applied for trace-level determination of FAV in biological and water samples. Our findings seem to provide useful guidance in the molecularly imprinted polymer design of MOF-based materials to help establish quantitative rules in designing MOF-based sensors for point of care (POC) systems.

Design Principle of Monoclinic NiCo2Se4 and Co3Se4 Nanoparticles with Opposing Intrinsic and Geometric Electrocatalytic Activity toward the OER

Despite predictions of high electrocatalytic OER activity by selenide-rich phases, such as NiCo₂Se₄ and Co₃Se₄, their synthesis through a wet-chemical route remains a challenge because of the high sensitivity of the various oxidation states of selenium to the reaction conditions. In this work, we have determined the contribution of individual reactants behind the maintenance of conducive solvothermal reaction conditions to produce phase-pure NiCo₂Se₄ and Co₃Se₄ from elemental selenium. The maintenance of reductive conditions throughout the reaction was found to be crucial for their synthesis, as a decrease in the reductive conditions over time was found to produce nickel/cobalt selenites as the primary product. Further, the reluctance of Ni(II) to oxidize into Ni(III) in comparison to the proneness of Co(II) to Co(III) oxidation was found to have a profound effect on the final product composition, as a deficiency of ions in the III oxidation state under nickel-rich reaction conditions hindered the formation of a monoclinic "Co₃Se₄-type" phase. Despite its lower intrinsic OER activity, Co₃Se₄ was found to show geometric performance on a par with NiCo₂Se₄ by virtue of its higher textural and microstructural properties.