HKUST-1 MOF in reline deep eutectic solvent: synthesis and phase transformation

Remarkable N2-selectivity enhancement of NH3-SCR over HPMo modified MnCo-BTC@SiO2 catalyst

In this work, the phosphomolybdate (HPMo) modification strategy was applied to improve the N2 selectivity of MnCo-BTC@SiO2 catalyst for the selective catalytic reduction of NOx, and further, the mechanism of HPMo modification on enhanced catalytic performance was explored. Among MnCo-BTC@SiO2-x catalysts with different HPMo concentrations, MnCo-BTC@SiO2-0.75 catalyst exhibited not only the highest NH3-SCR performance (∼95% at 200-300°C) but also the best N2 selectivity (exceed 80% at 100-300°C) due to the appropriate redox capacity, greater surface acidity. X-ray photoelectron spectrometer (XPS) and temperature programmed reduction of H2 (H2-TPR) results showed that the modification with HPMo reduced the oxidation-reduction performance of the catalyst due to electron transfer from Mo5+ to Mn4+/Mn3+ and prevent the excessive oxidation of ammonia adsorption species. NH3 temperature-programmed desorption of (NH3-TPD) results showed that the modification with HPMo could significantly improve the surface acidity and NH3 adsorption, which enhance the catalytic activity and N2 selectivity. In-situ diffused reflectance infrared Fourier transform spectroscopy (in-situ DRIFTS) revealed that modification with HPMo increased significantly the amount of adsorbed NH3 species on the Bronsted acid site and CB/CL, it suppressed the production of N2O by inhibiting the production of NH species, the deep dehydrogenation of ammonia adsorption species. This study provided a simple design strategy for the catalyst to improve the low-temperature catalytic performance and N2 selectivity.

Metal-Organic Frameworks/Graphdiyne/Copper Foam Composite Membranes for Catalytic Applications

Graphdiyne (GDY) with a three-dimensional network structure was synthesized on a copper foam (CF) via an in situ Glaser-Hay coupling reaction. A metal-organic framework/GDY composite membrane was designed and synthesized for the first time. CF serves as a template and catalyst for the directed polymerization of GDY membranes. The catalytic activities of HKUST-1/GDY/CF membrane in wet peroxide oxidation of phenol, oxidation of benzyl alcohol, and ring opening of epoxide were studied. The composite membrane has the advantages of appropriateness for continuous operation, simple use process, easy recycling, high catalytic efficiency, etc. It was found that the incorporation of GDY can facilitate electron transfer and effectively improve the catalytic activity of HKUST-1 in membrane catalysis.

Constructing Randomly Lamellar HKUST-1@Clinoptilolite through Polyethylene Glycol-Assisted Hydrothermal Method and Coordinated Complexation for Enhanced Adsorptive Separation for CO2 and CH4

Clinoptilolite (CP) was successfully synthesized via a hydrothermal route in the presence of polyethylene glycol (PEG), and it was then delaminated by washing using Zn²⁺ containing acid. HKUST-1, as one kind of the Cu-based MOFs, showed a high CO₂ adsorption capacity owing to its large pore volume and specific surface area. In the present work, we selected one of the most efficient ways for preparing the HKUST-1@CP compounds via coordination between exchanged Cu²⁺ and ligand (trimesic acid). Their structural and textural properties were characterized by XRD, SAXS, N₂ sorption isotherms, SEM, and TG-DSC profiles. Particularly, the effect of the additive PEG (average molecular weight of 600) on the induction (nucleation) periods and growth behaviors were detailed and investigated in the hydrothermal crystallization procedures of synthetic CPs. The corresponding activation energies of induction (E_n) and growth (E_g) periods during crystallization intervals were calculated. Meanwhile, the pore size of the inter-particles of HKUST-1@CP was 14.16 nm, and the BET specific area and pore volume were 55.2 m²/g and 0.20 cm³/g, respectively. Their CO₂ and CH₄ adsorption capacities and selectivity were preliminarily explored, showing 0.93 mmol/g for HKUST-1@CP at 298 K with the highest selective factor of 5.87 for CO₂/CH₄, and the dynamic separation performance was evaluated in column breakthrough experiments. These results suggested an efficient way of preparing zeolites and MOFs composites that is conducive to being a promising adsorbent for applications in gas separation.

Ionothermal synthesis of calcium-based metal–organic frameworks in a deep eutectic solvent

The ionothermal synthesis of Ca-MOFs has been performed using the 1 : 2 choline chloride : e-urea deep eutectic solvent, allowing the preparation of water sensitive materials.

Synthesis of metal–organic frameworks (MOFs) and their application in the selective catalytic reduction of NOx with NH3

This review summarizes the synthesis, applications for the NH3-SCR and methods for strengthening the water resistance and thermal stability of MOF catalysts.

A facile morphology tunable strategy of Zn-MOF derived hierarchically carbon materials with enhanced supercapacitive performance through the solvent effect

Metal–organic framework (MOF) derived porous carbon materials have been widely applied as active materials for supercapacitors due to their large specific surface area and ordered pore structure.

A high-performance Co-MOF non-enzymatic electrochemical sensor for glucose detection

The non-enzymatic [Ch]2[Co3(BDC)3Cl2]/GCE electrocatalyst can rapidly detect glucose with high accuracy and reliability in both human serum and orange juice.

Deep eutectic solvents for the preparation and post-synthetic modification of metal- and covalent organic frameworks

The use of deep eutectic solvents (DES) as media for the preparation of metal- and covalent organic frameworks (MOFs and COFs) and their post-synthetic modification towards composites is reviewed.