Amphiphilic Azo-Functionalized Polyhedral Oligomeric Silsesquioxane; Synthesis and Photo-Switched Efficient Phase Transfer via Host-Guest Encapsulation

A new amphiphilic azo-functionalized polyhedral oligomeric silsesquioxane (POSS) derivative was synthesized by functionalizing octa(3-aminopropyl)silsesquioxane (OAS-POSS) with 4-((4-(dodecyloxy)phenyl)diazenyl)benzoic acid, affording a hydrophilic amino POSS head and hydrophobic dodecyl tail with a diphenyl-azo connector. Prepared amphiphilic azo-functionalized POSS (azo-POSS) exhibited high ability for encapsulation and transferring cationic dyes into the organic phase by vigorously mixing with aqueous solutions of each dye. The photo-controlled encapsulating properties of the synthesized phase transfer reagent was studied using cationic dyes, such as methylene blue (MB), crystal violet (CV) and thymol blue in acidic conditions. Results showed more than 95 % encapsulation of MB. However, no considerable encapsulation was shown in the case of anionic dyes such as eriochrome black T (EBT) and thymol blue in alkaline solutions. By trans/cis isomerization of the azo moiety of the phase transfer reagent by UV irradiation (365 nm), the amount of dye encapsulation was decreased, which could be attributed to the formation of cis isomer that led to the folding of the dodecyl alkyl tail on the POSS moiety, and therefore prevent to lay the 3-aminopropyl moieties of POSS head to the water/DCM interface to adsorb and encapsulate MB molecules.

Fabricating a robust POSS-PCL nanofiber scaffold for nesting of mesenchymal stem cells: potential application in bone tissue regeneration

BACKGROUND

According to recent studies, electrospun Poly (Ɛ-caprolactone) (PCL) is an absorbing candidate for the formulation of biocompatible scaffolds used in tissue engineering. Tissue engineering is a set of techniques for producing or reconstructing tissue, whose primary purpose is to restore or improve the function of tissues in the human body. Tissue engineering combines the principles of materials and cell transplantation to develop alternative tissues or promote endogenous regeneration. However, this electrospun scaffold, consisting of PCL, has disadvantages such as low cell adhesion, inactivity of the surface, osteoinduction, and acidic destruction of the scaffold that causes inflammation at the implant site, often making it unsuitable implant. This study aimed to improve PCL base cellular scaffolds with the formulation of polyhedral oligomeric silsesquioxane - Polycaprolactone (POSS-PCL) nanofiber scaffolds. The present research focuses on the synthesis of nanofibers for their cell interaction features, and application in bone tissue engineering and regeneration.

RESULTS

POSS/ PCL Nanocomposites with 2, 5, and 10 wt.% of POSS were synthesized in the Trichloromethane, then POSS - PCL Nanofibers were prepared by the electrospinning technique. In this study, the structures of nanohybrids and nanofibers have been evaluated by FTIR, HNMR, XRD, SEM, EDX, and DSC. The biocompatibility of formulated POSS-PCL scaffolds was detected using mesenchymal stem cells (MSCs). Then several parameters were examined, involving DCFH ROS detection system, gene expression (cell viability/apoptosis, osteogenesis potentiality, and redox molecular homeostasis.

CONCLUSIONS

Based on our results, POSS-PCL nano-scaffolds in comparison with PCL have shown a robust potentiality in homing, growth, and differentiation of stem cells. Synthesis of POSS-PCL Nanofibers and their potential application in Bone Regeneration.

Corner-opening and corner-capping of mono-substituted T8 POSS: product distribution and isomerization

We applied chromatographic and spectroscopic techniques to revisit the product distribution of the corner-opening and corner-capping reactions of monosubstituted T₈ POSS. The monosubstituted Si is more likely to be removed than the remaining seven Si atoms during the corner-opening. After the corner-capping, the yield of monosubstituted T₈ POSS is much higher than the yields of the ortho- and meta-isomers of disubstituted T₈ POSS, and the para-isomer is negligible.