A hydrothermal synthesis of Ru-doped LiMn1.5Ni0.5O4 cathode materials for enhanced electrochemical performance

New Rare Earth-Doped Bilayered Perovskite Oxide Photocatalysts Sr2La0.5R0.5FeMnO7 (R = La, Nd, Sm, Gd, Dy) for the Degradation of Highly Toxic Methylene Blue Dye in Wastewater under Visible Light: Structural, Optical, and Magnetic Properties

This paper presents the rare earth doping effect on the structural, optical, and magnetic properties of bilayered Ruddlesden-Popper oxides Sr₂La_0.5R_0.5FeMnO₇ (R = La, Nd, Sm, Gd, Dy). Moreover, we are reporting for the first time a new rare earth-doped bilayered perovskite oxide series for the highly toxic methylene blue dye degradation in wastewater under visible light. Structural analysis of the PXRD data using the Rietveld refinements confirms the formation of the phases in tetragonal symmetry with the I4/mmm space group. The unit cell lattice parameters (a & c) and the cell volume (V) decrease monotonically from La- to Dy-doped samples owing to the decrease in the lanthanide ionic radii. The X-ray photoelectron spectroscopy analysis indicates the existence of the Mn ions in the mixed valence state. The DRS study shows that the energy band gap value decreases on moving from La to Gd substitution; however, it further increases for the Dy-doped sample. The magnetic measurements reveal that all the phases exhibit dominant anti-ferromagnetic interactions with Neel temperature (T _N) observed at 150, 147, 138, 113, and 117 K for La-, Nd-, Sm-, Gd-, and Dy-substituted phases, respectively. However, the presence of an unsaturated hysteresis loop observed in the isothermal magnetic field (H) vs magnetization (M) plot also indicates the existence of weak ferromagnetic interactions. The investigation of the photocatalytic activity of the synthesized samples was done by carrying out photo-oxidative degradation of methylene blue (MB) dye pollutants. The results show that the photodegradation enhances by doping with heavier rare earth ions with the exception of the Dy-doped sample. The Gd-doped catalyst shows the maximum degradation efficiency of 99.03% in 50 min under visible light irradiation. The scavenging experiments confirmed that the^·OH was the main/dominant oxidizing agent involved in the degradation of the MB dye.

The Effects of Ru4+ Doping on LiNi0.5Mn1.5O4 with Two Crystal Structures

Doping of Ru has been used to enhance the performance of LiNi_0.5Mn_1.5O₄ cathode materials. However, the effects of Ru doping on the two types of LiNi_0.5Mn_1.5O₄ are rarely studied. In this study, Ru⁴⁺ with a stoichiometric ratio of 0.05 is introduced into LiNi_0.5Mn_1.5O₄ with different space groups (Fd3¯m, P4₃32). The influence of Ru doping on the properties of LiNi_0.5Mn_1.5O₄ (Fd3¯m, P4₃32) is comprehensively studied using multiple techniques such as XRD, Raman, and SEM methods. Electrochemical tests show that Ru⁴⁺-doped LiNi_0.5Mn_1.5O₄ (P4₃32) delivers the optimal electrochemical performance. Its initial specific capacity reaches 132.8 mAh g^-1, and 97.7% of this is retained after 300 cycles at a 1 C rate at room temperature. Even at a rate of 10 C, the capacity of Ru⁴⁺-LiNi_0.5Mn_1.5O₄ (P4₃32) is still 100.7 mAh g^-1. Raman spectroscopy shows that the Ni/Mn arrangement of Ru⁴⁺-LiNi_0.5Mn_1.5O₄ (Fd3¯m) is not significantly affected by Ru⁴⁺ doping. However, LiNi_0.5Mn_1.5O₄ (P4₃32) is transformed to semi-ordered LiNi_0.5Mn_1.5O₄ after the incorporation of Ru⁴⁺. Ru⁴⁺ doping hinders the ordering process of Ni/Mn during the heat treatment process, to an extent.