Are the Wear and Osteolysis Outcomes Different between Annealed and Remelted First-Generation Highly Crosslinked Polyethylene after Long-Term Implantation?

The Measurement of the Oxidative Index of Polyethylene Obtained during Revision Hip Arthroplasty and Assessment of Its Variability Depending on the Degree of Osteolysis, Implantation Time, as Well as the Size and Material of the Utilized Head

Background/Objectives: Aseptic loosening is the leading cause of late revision in total hip arthroplasty, primarily due to degenerative oxidation of polyethylene components, leading to wear particle formation and periacetabular osteolysis. This study aimed to analyze the oxidation levels in polyethylene liners and cemented cups retrieved from revision surgeries using Fourier-transform infrared spectroscopy (FTIR) and to explore the correlation between oxidation levels and factors such as head size, head material, fixation method, and implant survival time. Methods: Polyethylene liners and cups were analyzed post-revision surgery to assess oxidation levels, which were then compared to periacetabular bone loss measured by the Paprosky classification. This study evaluated the impact of head size (28 mm vs. 32 mm), head material (ceramic vs. metal), and fixation methods on oxidation. The relationship between the mean oxidation index (OI) and implant survival time was also investigated. Results: There was a significant positive correlation between the mean oxidation index of the polyethylene components and the severity of periacetabular osteolysis according to the Paprosky scale. While the mean OI for samples articulating with ceramic heads was lower than for those with metal heads, and the mean OI for samples with a 32 mm head size was lower than for those with a 28 mm size, these differences were not statistically significant. Furthermore, the fixation method did not affect the oxidation index, and no correlation was found between OI and the survival time of the implants. Conclusions: This study confirms a direct correlation between polyethylene oxidation and periacetabular osteolysis in hip replacements, highlighting the importance of material choice and design in potentially reducing the risk of aseptic loosening. Despite the lack of significant differences in oxidation levels based on head material and size, these factors may still play a role in the long-term outcome of hip arthroplasty, warranting further investigation.

Synergy between vitamin E and D-sorbitol in enhancing oxidation stability of highly crosslinked ultrahigh molecular weight polyethylene

Oxidative stability of radiation crosslinked ultrahigh molecular weight polyethylene (UHMWPE) artificial joints is significantly improved by vitamin E (VE), but there is a dilemma that VE hinders crosslinking and thus jeopardizes the wear of UHMWPE. In this effort, we proposed an efficient strategy to stabilize UHMWPE under limited antioxidant contents, where VE and D-sorbitol (DS) were used as the primary antioxidant and the secondary antioxidant respectively. For non-irradiated blends with fixed antioxidant contents, oxidative stability accessed by oxidation induction time (OIT) of VE/DS/UHMWPE blends was superior to that of VE/UHMWPE blends, while DS/UHMWPE blends showed no increase in OIT. The cooperation between DS and VE exhibited a synergistic effect on enhancing the oxidative stability of UHMWPE. Interestingly, the irradiated VE/DS/UHMWPE blends showed comparable OIT but a significantly higher crosslink density than the irradiated VE/UHMWPE blends. The crystallinity, melting point, and in vitro biocompatibility of the blends were not affected by VE and DS. The quantitative relationships of mechanical properties, oxidation stability, crystallinity and crosslink density were established to unveil the correlation of these key factors. The overall properties of VE/UHMWPE and VE/DS/UHMWPE blends were compared to elucidate the superiority of the antioxidant compounding strategy. These findings provide a paradigm to break the trade-off between oxidative stability, crosslink density and mechanical properties, which is constructive to develop UHMWPE bearings with upgraded performance for total joint replacements. STATEMENT OF SIGNIFICANCE: VE-stabilized UHMWPE is the most commonly used material in total joint replacements at present. However, oxidation and wear resistance of VE/UHMWPE implants cannot be unified since VE reduces the efficiency of radiation crosslinking. It limits the use of VE. Herein, we proposed a compounding stabilization by the synergy between VE and DS. The antioxidation capability of VE was revived by DS, thus enhancing the oxidation stability of unirradiated UHMWPE. The irradiated VE/DS/UHMWPE exhibited similar oxidation stability but higher crosslink density than irradiated VE/UHMWPE, which is beneficial to combat wear of UHMWPE and to inhibit the occurrence of osteolysis. This synergistic antioxidation strategy endows the UHMWPE joint material with good overall performance, which is of clinical significance.