Co-adsorption of water and oxygen on GaN: Effects of charge transfer and formation of electron depletion layer

Degradation Studies of Air-Exposed Black Phosphorous and Black Arsenic Phosphorous

This work investigates the effects of oxygen and humidity on black phosphorous (BP) and black arsenic phosphorous (AsxP1−x ) flakes using Raman spectroscopy and in situ electric transport measurements (four-probe resistance and thermoelectric power, TEP). The results show that the incorporation of arsenic into the lattice of BP renders it more stable, with the degradation times for BP, As0.2P0.8, and As0.4P0.6 being 4, 5, and 11 days, respectively. The P-P Raman peak intensities were determined to decrease with exposure to oxygen and moisture. The TEP measurements confirmed that both BP and AsxP1−x are p-type semiconductors with the TEP of As0.4P0.6 stabilizing more slowly than that of BP. In addition, the four-probe resistance of BP and AsxP1−x stabilized significantly faster when exposed to air after being degassed in a vacuum. This was attributed to the charge transfer between the oxygen redox potential of air and the Fermi energy (EF) of the semiconductors.

Environmental sensitivity of GaN nanofins grown by selective area molecular beam epitaxy

Nanostructures exhibit a large surface-to-volume ratio, which makes them sensitive to their ambient conditions. In particular, GaN nanowires and nanofins react to their environment as adsorbates influence their (opto-) electronic properties. Charge transfer between the semiconductor surface and adsorbed species changes the surface band bending of the nanostructures, and the adsorbates can alter the rate of non-radiative recombination in GaN. Despite the importance of these interactions with the ambient environment, the detailed adsorption mechanisms are still not fully understood. In this article, we present a systematic study concerning the environmental sensitivity of the electrical conductivity of GaN nanofins. We identify oxygen- and water-based adsorbates to be responsible for a quenching of the electrical current through GaN nanofins due to an increased surface band bending. Complementary contact potential difference measurements in controlled atmospheres on bulkm- andc-plane GaN reveal additional complexity with regard to water adsorption, for which surface dipoles might play an important role besides an increased surface depletion width. The sensitive reaction of the electrical parameters to the environment and surface condition underlines the necessity of a reproducible pre-treatment and/or surface passivation. The presented results help to further understand the complex adsorption mechanisms at GaN surfaces. Due to the sensitivity of the nanofin conductivity on the environment, such structures could perform well as sensing devices.

GaN Nanowire MOSFET with Near-Ideal Subthreshold Slope

Wrap-around gate GaN nanowire MOSFETs using Al₂O₃ as gate oxide have been experimentally demonstrated. The fabricated devices exhibit a minimum subthreshold slope of 60 mV/dec, an average subthreshold slope of 68 mV/dec over three decades of drain current, drain-induced barrier lowering of 27 mV/V, an on-current of 42 μA/μm (normalized by nanowire circumference), on/off ratio over 10⁸, an intrinsic transconductance of 27.8 μS/μm, for a switching efficiency figure of merit, Q=g_m/SS of 0.41 μS/μm-dec/mV. These performance metrics make GaN nanowire MOSFETs a promising candidate for emerging low-power applications such as sensors and RF for the internet of things.